Metal-ceramic bond strength between a feldspathic porcelain and a Co-Cr alloy fabricated with Direct Metal Laser Sintering technique
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. MATERIALS AND METHODS. Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity (E) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. RESULTS. Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was 222 ± 5.13 GPa and 227 ± 3 GPa, respectively. The bond strength was 51.87 ± 7.50 MPa for test group and 54.60 ± 6.20 MPa for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. CONCLUSION. Specimens produced by the DMLS technique cover the lowest acceptable metalceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use.
Abstract
PURPOSE. The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. MATERIALS AND METHODS. Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity (E) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. RESULTS. Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was 222 ± 5.13 GPa and 227 ± 3 GPa, respectively. The bond strength was 51.87 ± 7.50 MPa for test group and 54.60 ± 6.20 MPa for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. CONCLUSION. Specimens produced by the DMLS technique cover the lowest acceptable metalceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use.
참고문헌 (27)
- Bezzon OL, "Effect of beryllium on the castability and resistance of ceramometal bonds in nickel-chromium alloys", J Prosthet Dent, 80, pp.570~574 (1998)[DOI]
- Willis HH, "Potential exposures and risks from beryllium-containing products", Risk Anal, 22, pp.1019~1033 (2002)[DOI]
- Youssef S. Al Jabbari, "Physico-mechanical properties and prosthodontic applications of Co-Cr dental alloys: a review of the literature", The Journal of Advanced of Prosthodontics, 6(2), pp.138~145 (2014), 대한치과보철학회[DOI]
- Alkmina LB, "Microstructural evidence of beryllium in commercial dental Ni-Cr alloys", Mat Res, 17, pp.627~631 (2014)[DOI]
- Chen WC, "Characterization of Ni-Cr alloys using different casting techniques and molds", Mater Sci Eng C Mater Biol Appl, 35, pp.231~238 (2014)[DOI]
- Henriques B, "Influence of preoxidation cycle on the bond strength of CoCrMoSi-porcelain dental composites", Mater Sci Engin: C, 32, pp.2374~2380 (2012)[DOI]
- Molina A, "Metallographic characterization of overdentures bars manufactured by over-castting abutments for dental implants", Rev Fac Odontol Univ Antioq, 25, pp.26~43 (2013)
- Atluri KR, "Comparative evaluation of metal-ceramic bond strengths of nickel chromium and cobalt chromium alloys on repeated castings: An in vitro study", J Int Oral Health, 6, pp.99~103 (2014)
- Akova T, "Comparison of the bond strength of laser-sintered and cast base metal dental alloys to porcelain", Dent Mater, 24, pp.1400~1404 (2008)[DOI]
- van Noort R, "The future of dental devices is digital", Dent Mater, 28, pp.3~12 (2012)[DOI]
- Koutsoukis T, "Selective laser melting technique of Co-Cr dental alloys: A review of structure and properties and comparative analysis with other available techniques", J Prosthodont, 24, pp.303~312 (2015)[DOI]
- Henriques B, "Microstructure, hardness, corrosion resistance and porcelain shear bond strength comparison between cast and hot pressed CoCrMo alloy for metal-ceramic dental restorations", J Mech Behav Biomed Mater, 12, pp.83~92 (2012)[DOI]
- Takaichi A, "Microstructures and mechanical properties of Co-29Cr-6Mo alloy fabricated by selective laser melting process for dental applications", J Mech Behav Biomed Mater, 21, pp.67~76 (2013)[DOI]
- Al Jabbari YS, "Metallurgical and interfacial characterization of PFM Co-Cr dental alloys fabricated via casting, milling or selective laser melting", Dent Mater, 30, pp.e79~e88 (2014)
- Khaing MW, "Direct metal laser sintering for rapid tooling: processing and characterisation of EOS parts", J Mater Proces Technol, 113, pp.269~272 (2001)[DOI]
- Simchi A, "Direct laser sintering of metal powders: Mechanism, kinetics and microstructural features", Mater Sci Engin: A, 428, pp.148~158 (2006)[DOI]
- Akagi K, "Properties of test metal ceramic titanium alloys", J Prosthet Dent, 68, pp.462~467 (1992)[DOI]
- Ban S, "Influence of test method on failure stress of brittle dental materials", J Dent Res, 69, pp.1791~1799 (1990)[DOI]
- "ISO 9693. Metal-ceramic dental restorative systems, Second edition", International Organization for Standardization, ~ (1999)
- Ritter JE, "Critique of test methods for lifetime predictions", Dent Mater, 11, pp.147~151 (1995)[DOI]
- Probster L, "Three-point bending strength of ceramics fused to cast titanium", Eur J Oral Sci, 104, pp.313~319 (1996)[DOI]
- Liu J, "Effect of preparation methods on the metal-porcelain bond strength of Co-Cr alloys", Hua Xi Kou Qiang Yi Xue Za Zhi, 32, pp.115~118 (2014)
- 배은정, "Bond and fracture strength of metalceramic restorations formed by selective laser sintering", The Journal of Advanced of Prosthodontics, 6(4), pp.266~271 (2014), 대한치과보철학회[DOI]
- 배은정, "In vitro evaluation of the bond strength between various ceramics and cobalt-chromium alloy fabricated by selective laser sintering", The Journal of Advanced of Prosthodontics, 7(4), pp.312~316 (2015), 대한치과보철학회[DOI]
- Liu J, "Metal-ceramic bond strength of Co-Cr alloy processed by selective laser melting", Zhonghua Kou Qiang Yi Xue Za Zhi, 48, pp.170~172 (2013)
- Xiang N, "Metal-ceramic bond strength of Co-Cr alloy fabricated by selective laser melting", J Dent, 40, pp.453~457 (2012)[DOI]
- Wu L, "Evaluation of the mechanical properties and porcelain bond strength of cobalt-chromium dental alloy fabricated by selective laser melting", J Prosthet Dent, 111, pp.51~55 (2014)[DOI]