A comparative study on the bond strength of porcelain to the millingable Pd-Ag alloy
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. The porcelain fused to gold has been widely used as a restoration both with the natural esthetics of the porcelain and durability and marginal fit of metal casting. However, recently, due to the continuous rise in the price of gold, an interest towards materials to replace gold alloy is getting higher. This study compared the bond strength of porcelain to millingable palladium-silver (Pd-Ag) alloy, with that of 3 conventionally used metal-ceramic alloys. MATERIALS AND METHODS. Four types of metal-ceramic alloys, castable nonprecious nickel-chrome alloy, castable precious metal alloys containing 83% and 32% of gold, and millingable Pd-Ag alloy were used to make metal specimens (n=40). And porcelain was applied on the center area of metal specimen. Three-point bending test was performed with universal testing machine. The bond strength data were analyzed with a one-way ANOVA and post hoc Scheffe’s tests (α=.05). RESULTS. The 3-point bending test showed the strongest (40.42 ± 5.72 MPa) metal-ceramic bond in the nonprecious Ni-Cr alloy, followed by millingable Pd-Ag alloy (37.71 ± 2.46 MPa), precious metal alloy containing 83% of gold (35.89 ± 1.93 MPa), and precious metal alloy containing 32% of gold (34.59 ± 2.63 MPa). Nonprecious Ni-Cr alloy and precious metal alloy containing 32% of gold showed significant difference (P<.05). CONCLUSION. The type of metalceramic alloys affects the bond strength of porcelain. Every metal-ceramic alloy used in this study showed clinically applicable bond strength with porcelain (25 MPa).
Abstract
PURPOSE. The porcelain fused to gold has been widely used as a restoration both with the natural esthetics of the porcelain and durability and marginal fit of metal casting. However, recently, due to the continuous rise in the price of gold, an interest towards materials to replace gold alloy is getting higher. This study compared the bond strength of porcelain to millingable palladium-silver (Pd-Ag) alloy, with that of 3 conventionally used metal-ceramic alloys. MATERIALS AND METHODS. Four types of metal-ceramic alloys, castable nonprecious nickel-chrome alloy, castable precious metal alloys containing 83% and 32% of gold, and millingable Pd-Ag alloy were used to make metal specimens (n=40). And porcelain was applied on the center area of metal specimen. Three-point bending test was performed with universal testing machine. The bond strength data were analyzed with a one-way ANOVA and post hoc Scheffe’s tests (α=.05). RESULTS. The 3-point bending test showed the strongest (40.42 ± 5.72 MPa) metal-ceramic bond in the nonprecious Ni-Cr alloy, followed by millingable Pd-Ag alloy (37.71 ± 2.46 MPa), precious metal alloy containing 83% of gold (35.89 ± 1.93 MPa), and precious metal alloy containing 32% of gold (34.59 ± 2.63 MPa). Nonprecious Ni-Cr alloy and precious metal alloy containing 32% of gold showed significant difference (P<.05). CONCLUSION. The type of metalceramic alloys affects the bond strength of porcelain. Every metal-ceramic alloy used in this study showed clinically applicable bond strength with porcelain (25 MPa).
참고문헌 (46)
- Brecker SC., "Porcelain baked to gold-A new medium in prosthodontics", J Prosthet Dent, 6, pp.801~810 (1956)
- Bagby M., "Metal ceramic compatibility : a review of the literature", J Prosthet Dent, 63, pp.21~25 (1990)
- 김철만, "도재 전장 금관용 비귀금속 합금의 결합강도에 관한 연구", 구강회복응용과학지, 22(3), pp.203~210 (2006), 대한턱관절교합학회
- Kim I., "A study on the bond strength between reused dental alloys and porcelain", J Korean Acad Prosthodont, 31, pp.181~190 (1993)
- do Prado RA., "Shear bond strength of dental porcelains to nickel-chromium alloys", Braz Dent J, 16, pp.202~206 (2005)
- Moffa JP., "An evaluation of nonprecious alloys for use with porcelain veneers. Part I. Physical properties", J Prosthet Dent, 30, pp.424~431 (1973)
- Kelly JR., "Nonprecious alloys for use in fixed prosthodontics : a literature review", J Prosthet Dent, 49, pp.363~370 (1983)
- Morris HF., "Veterans Administration Cooperative Studies Project No. 147. Part IV : Biocompatibility of base metal alloys", J Prosthet Dent, 58, pp.1~5 (1987)
- Spear F., "Which all-ceramic system is optimal for anterior esthetics?", J Am Dent Assoc, 139, pp.19S~24S (2008)
- Magne P., "The esthetic width in fixed prosthodontics", J Prosthodont, 8, pp.106~118 (1999)
- O’Boyle KH., "An investigation of new metal framework design for metal ceramic restorations", J Prosthet Dent, 78, pp.295~301 (1997)
- Stappert CF., "Marginal adaptation of three-unit fixed partial dentures constructed from pressed ceramic systems", Br Dent J, 196, pp.766~770 (2004)
- Campbell SD., "Evaluation of the fit and strength of an all-ceramic fixed partial denture", J Prosthet Dent, 59, pp.301~306 (1988)
- Kelly JR., "Failure of all-ceramic fixed partial dentures in vitro and in vivo : analysis and modeling", J Dent Res, 74, pp.1253~1258 (1995)
- Zervas PJ., "Distortion of three-unit implant frameworks during casting, soldering, and simulated porcelain firings", J Prosthodont, 8, pp.171~179 (1999)
- Katsoulis J., "Precision of fit of implant-supported screw-re tained 10-unit computer-aided-designed and computer-aidedmanufactured frameworks made from zirconium dioxide and titanium : an in vitro study", Clin Oral Implants Res, 25, pp.165~174 (2014)
- Gilbert JL., "Bond characteristics of porcelain fused to milled titanium", Dent Mater, 10, pp.134~140 (1994)
- Reich S., "Clinical fit of all-ceramic three-unit fixed partial dentures, generated with three different CAD", CAM systems, 2005, pp.113, 174~179
- Bachhav VC., "Zirconia-based fixed partial dentures : a clinical review", Quintessence Int, 42, pp.173~182 (2011)
- Huget EF., "Status report on palladium-silver-based crown and bridge alloys", J Am Dent Assoc, 89, pp.383~385 (1974)
- Goodacre CJ., "Palladium-silver alloys : a review of the literature", J Prosthet Dent, 62, pp.34~37 (1989)
- Kansu G., "Evaluation of the biocompatibility of various dental alloys : Part I-Toxic potentials", Eur J Prosthodont Restor Dent, 4, pp.129~136 (1996)
- International Organization for Standardization, "ISO 9693: metal-ceramic dental restorative systems", ~ (2012)
- Knap FJ., "Study of bond strength of dental porcelain fused to metal", J Dent Res, 45, pp.1047~1051 (1966)
- Silver M., "An evaluation and comparison of porcelain-fused-to-cast metals", J Prosthet Dent, 10, pp.1055~1064 (1960)
- Ozcan M., "Fracture reasons in ceramic-fused-to-metal restorations", J Oral Rehabil, 30, pp.265~269 (2003)
- Fairhurst CW., "Porcelain-metal thermal compatibility", J Dent Res, 60, pp.815~819 (1981)
- Shell JS., "Study of the bond between gold alloys and porcelain", J Dent Res, 41, pp.1424~1437 (1962)
- de Melo RM., "Shear bond strengths of a ceramic system to alternative metal alloys", J Prosthet Dent, 93, pp.64~69 (2005)
- Mackert JR Jr., "The relationship between oxide adherence and porcelain-metal bonding", J Dent Res, 67, pp.474~478 (1988)
- McLean JW., "The metal-ceramic restoration", Dent Clin North Am, 27, pp.747~761 (1983)
- Barghi N., "Comparison of fracture strength of porcelain-veneered-to-high noble and base metal alloys", J Prosthet Dent, 57, pp.23~26 (1987)
- Lee EH., "Effect of degassing condition on ceramic bond strength of Ni-Cr alloys", J Korean Acad Prosthodont, 38, pp.461~471 (2000)
- Jochen DG., "Effect of metal surface treatment on ceramic bond strength", J Prosthet Dent, 55, pp.186~188 (1986)
- Külünk T., "Effect of different air-abrasion particles on metal-ceramic bond strength", J Dent Sci, 6, pp.140~146 (2011)
- Anusavice KJ., "Comparative evaluation of ceramic-metal bond tests using finite element stress analysis", J Dent Res, 59, pp.608~613 (1980)
- Lenz J., "Bond strength of metal-ceramic systems in three-point flexure bond test", J Appl Biomater, 6, pp.55~64 (1995)
- Papazoglou E., "Porcelain adherence vs force to failure for palladium-gallium alloys : a critique of metal-ceramic bond testing", Dent Mater, 14, pp.112~119 (1998)
- Hammad IA., "Designs of bond strength tests for metal-ceramic complexes : review of the literature", J Prosthet Dent, 75, pp.602~608 (1996)
- Barghi N., "Optimum thickness of opaque and body porcelain", J Prosthet Dent, 48, pp.429~431 (1982)
- Warpeha WS Jr., "Design and technique variables affecting fracture resistance of metal-ceramic restorations", J Prosthet Dent, 35, pp.291~298 (1976)
- Lahori M., "The effect of surface treatments on the bond strength of a nonprecious alloyceramic interface : an invitro study", J Indian Prosthodont Soc, 14, pp.151~155 (2014)
- Li BH., "Effect of pretreatments on the metal-ceramic bonding strength of a Pd-Ag alloy", J Dent, 42, pp.319~328 (2014)
- Gilbert JL., "Bond characteristics of porcelain fused to milled titanium", Dent Mater, 10, pp.134~140 (1994)
- Anusavice KJ., "Delayed crack development in porcelain due to incompatibility stress", J Dent Res, 67, pp.1086~1091 (1988)
- Rosenstiel SF, "Contemporary fixed prosthodontics", pp.743~750 (2006), Mosby Elsevier