Color alterations of a PMMA resin for fixed interim prostheses reinforced with silica nanoparticles
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of the present study was to evaluate the color changes of an autopolymerizing PMMA resin used for interim fixed restorations, reinforced with SiO2 nanoparticles. MATERIALS AND METHODS. Silica nanoparticles were blended with the PMMA resin powder through high-energy ball milling. Four shades of PMMA resin were used (A3, B3, C3, D3) and total color differences were calculated through the equations ΔEab=[(ΔL*)² + (Δa*)² + (Δb*)²]½ and ΔE00= . Statistically significant differences between ΔEab and the clinically acceptable values of 3.3 and 2.7 and those between ΔE00 and the clinically acceptable value of 1.8 were evaluated with one sample t-test (P<.05). Differences among the different shades were assessed through One-Way ANOVA and Bonferroni multiple comparison tests. RESULTS. Significantly lower values were detected for all groups concerning ΔEab compared to the intraorally clinicalacceptable values of 3.3 and 2.7. Significantly lower mean values were detected for groups B3, C3, and D3, concerning ΔE00 compared to the intraorally clinical acceptant value of 1.8. Color pigments in red-brown (A3) and red-grey (D3) shades affect the total color change to a greater extent after the reinforcement with SiO2 nanoparticles compared to the red-yellow (B3) shade. CONCLUSION. Within the limitations of this in vitro study, it can be suggested that reinforcing PMMA with SiO2 nanoparticles at 0.25 wt% slightly affects the optical properties of the PMMA resin without being clinically perceivable.
Abstract
PURPOSE. The aim of the present study was to evaluate the color changes of an autopolymerizing PMMA resin used for interim fixed restorations, reinforced with SiO2 nanoparticles. MATERIALS AND METHODS. Silica nanoparticles were blended with the PMMA resin powder through high-energy ball milling. Four shades of PMMA resin were used (A3, B3, C3, D3) and total color differences were calculated through the equations ΔEab=[(ΔL*)² + (Δa*)² + (Δb*)²]½ and ΔE00= . Statistically significant differences between ΔEab and the clinically acceptable values of 3.3 and 2.7 and those between ΔE00 and the clinically acceptable value of 1.8 were evaluated with one sample t-test (P<.05). Differences among the different shades were assessed through One-Way ANOVA and Bonferroni multiple comparison tests. RESULTS. Significantly lower values were detected for all groups concerning ΔEab compared to the intraorally clinicalacceptable values of 3.3 and 2.7. Significantly lower mean values were detected for groups B3, C3, and D3, concerning ΔE00 compared to the intraorally clinical acceptant value of 1.8. Color pigments in red-brown (A3) and red-grey (D3) shades affect the total color change to a greater extent after the reinforcement with SiO2 nanoparticles compared to the red-yellow (B3) shade. CONCLUSION. Within the limitations of this in vitro study, it can be suggested that reinforcing PMMA with SiO2 nanoparticles at 0.25 wt% slightly affects the optical properties of the PMMA resin without being clinically perceivable.
참고문헌 (51)
- Gratton DG, "Interim restorations", Dent Clin North Am, 48, pp.vii~ (2004)
- Kaiser DA, "Temporization techniques in fixed prosthodontics", Dent Clin North Am, 29, pp.403~412 (1985)
- Young HM, "Comparative in vitro evaluation of two provisional restorative materials", J Prosthet Dent, 85, pp.129~132 (2001)
- Tjong S. C, "Structural and mechanical properties of polymer nanocomposites", Mater Sci Eng R Reports, 53, pp.73~197 (2006)
- Alhavaz A, "Effect of untreated zirconium oxide nanofiller on the flexural strength and surface hardness of autopolymerized interim fixed restoration resins", J Esthet Restor Dent, 29, pp.264~269 (2017)
- Protopapa P, "Reinforcement of a PMMA resin for fixed interim prostheses with nanodiamonds", Dent Mater J, 30, pp.222~231 (2011)
- Larson WR, "The effect of carbon graphite fiber reinforcement on the strength of provisional crown and fixed partial denture resins", J Prosthet Dent, 66, pp.816~820 (1991)
- Gutteridge DL, "Reinforcement of poly(methyl methacrylate)with ultra-high-modulus polyethylene fibre", J Dent, 20, pp.50~54 (1992)
- Zuccari AG, "Reinforcement of acrylic resins for provisional fixed restorations. Part I: Mechanical properties", Biomed Mater Eng, 7, pp.327~343 (1997)
- Panyayong W, "Part III : effects of addition of titania and zirconia mixtures on some mechanical and physical properties", Biomed Mater Eng, 12, pp.353~366 (2002)
- Vallittu PK, "Flexural properties of acrylic resin polymers reinforced with unidirectional and woven glass fibers", J Prosthet Dent, 81, pp.318~326 (1999)
- Kim SH, "Effect of glass-fiber reinforcement and water storage on fracture toughness(KIC)of polymer-based provisional crown and FPD materials", Int J Prosthodont, 17, pp.318~322 (2004)
- Vallittu PK, "A review of methods used to reinforce polymethyl methacrylate resin", J Prosthodont, 4, pp.183~187 (1995)
- Geerts GA, "The effect of different reinforcements on the fracture toughness of materials for interim restorations", J Prosthet Dent, 99, pp.461~467 (2008)
- Hamza TA, "The effect of fiber reinforcement on the fracture toughness and flexural strength of provisional restorative resins", J Prosthet Dent, 91, pp.258~264 (2004)
- Nohrström TJ, "The effect of placement and quantity of glass fibers on the fracture resistance of interim fixed partial dentures", Int J Prosthodont, 13, pp.72~78 (2000)
- Topouzi M, "Reinforcement of a PMMA resin for interim fixed prostheses with silica nanoparticles", J Mech Behav Biomed Mater, 69, pp.213~222 (2017)
- Priyadarsini S, "Nanoparticles used in dentistry : A review", J Oral Biol Craniofac Res, 8, pp.58~67 (2018)
- O’ Brien W-J, "Dental materials and their selection", pp.24~36 (2002), Quintessence Publishing Co, Inc
- Douglas RD, "Intraoral determination of the tolerance of dentists for perceptibility and acceptability of shade mismatch", J Prosthet Dent, 97, pp.200~208 (2007)
- Ruyter IE, "Color stability of dental composite resin materials for crown and bridge veneers", Dent Mater, 3, pp.246~251 (1987)
- Luo MR, "The development of the CIE 2000colour-difference formula : CIEDE2000", Color Res Appl, 26, pp.340~350 (2001)
- Wee AG, "Use of a porcelain color discrimination test to evaluate color difference formulas", J Prosthet Dent, 98, pp.101~109 (2007)
- Gómez-Polo C, "Comparison of the CIELab and CIEDE2000 color difference formulas", J Prosthet Dent, 115, pp.65~70 (2016)
- Paravina RD, "Color difference thresholds in dentistry", J Esthet Restor Dent, 27, pp.S1~9 (2015)
- Bikiaris DN, "Compatibilisation effect of PP-g-MA copolymer on iPP", SiO2 nanocomposites prepared by melt mixing, 2005, pp.41, 1965~1978
- Castrillo PD, "Real dispersion of isolated fumed silica nanoparticles in highly filled PMMA prepared by high energy ball milling", J Colloid Interface Sci, 308, pp.318~324 (2007)
- Bohin F, "Determination of the infiltration kinetics of polymer into filler agglomerates using transient buoyancy measurements", Powder Technol, 83, pp.159~162 (1995)
- Gegauff AG, "Fracture toughness of provisional resins for fixed prosthodontics", J Prosthet Dent, 58, pp.23~29 (1987)
- Ireland MF, "In vitro mechanical property comparison of four resins used for fabrication of provisional fixed restorations", J Prosthet Dent, 80, pp.158~162 (1998)
- Rosenstiel SF, "Contemporary fixed prosthodontics", pp.272~335 (2006), Mosby
- Zeighami S, "Effect of ceramic thickness and cement color on final shade of all ceramic restoration : a systematic review", Sch Acad J Biosci, 5, pp.459~464 (2017)
- Balkenhol M, "Mechanical properties of provisional crown and bridge materials : chemical-curing versus dual-curing systems", J Dent, 36, pp.15~20 (2008)
- Anni Berger-Schunn, "Practical color measurement: A primer for the beginner, a reminder for the expert", pp.73~97 (1994), John Willey
- Perez Mdel M, "Dental ceramics : A CIEDE2000acceptability thresholds for lightness, chroma and hue differences", J Dent, 39, pp.e37~e44 (2011)
- Ghinea R, "Color difference thresholds in dental ceramics", J Dent, 38, pp.e57~64 (2010)
- Green SB, "Using SPSS for windows: Analyzing and understanding data", pp.146~150 (1999), Pearson Education, Inc
- Johnston WM, "Assessment of appearance match by visual observation and clinical colorimetry", J Dent Res, 68, pp.819~822 (1989)
- Seghi RR, "Performance assessment of colorimetric devices on dental porcelains", J Dent Res, 68, pp.1755~1759 (1989)
- Noie F, "Color stability of resin cements after accelerated aging", Int J Prosthodont, 8, pp.51~55 (1995)
- Doray PG, "Color stability of provisional restorative materials after accelerated aging", J Prosthodont, 10, pp.212~216 (2001)
- Stober T, "Color stability of highly filled composite resin materials for facings", Dent Mater, 17, pp.87~94 (2001)
- Da Silva JD, "Clinical performance of a newly developed spectrophotometric system on tooth color reproduction", J Prosthet Dent, 99, pp.361~368 (2008)
- Hunter RS, "The measurement of appearance", pp.162~191 (1987), John Wiley & Sons
- Yoshida Y, "Effect of presilanization filler decontamination on aesthetics and degradation resistance of resin composites", Dent Mater J, 21, pp.383~395 (2002)
- Arikawa H, "Effect of filler properties in composite resins on light transmittance characteristics and color", Dent Mater J, 26, pp.38~44 (2007)
- Emami N, "How filler properties, filler fraction, sample thickness and light source affect light attenuation in particulate filled resin composites", Dent Mater, 21, pp.721~730 (2005)
- Mitra SB, "An application of nanotechnology in advanced dental materials", J Am Dent Assoc, 134, pp.1382~1390 (2003)
- Masotti AS, "UV-vis spectrophotometric direct transmittance analysis of composite resins", Dent Mater, 23, pp.724~730 (2007)
- Lim YK, "Influence of filler distribution on the color parameters of experimental resin composites", Dent Mater, 24, pp.67~73 (2008)
- Goodkind RJ, "Use of a fiber-optic colorimeter for in vivo color measurements of 2830 anterior teeth", J Prosthet Dent, 58, pp.535~542 (1987)