Initial bacterial adhesion on resin, titanium and zirconia in vitro
2
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of this in vitro study was to investigate the adhesion of initial colonizer, Streptococcus sanguis, on resin, titanium and zirconia under the same surface polishing condition. MATERIALS AND METHODS. Specimens were prepared from Z-250, cp-Ti and 3Y-TZP and polished with 1 μm diamond paste. After coating with saliva, each specimen was incubated with Streptococcus sanguis. Scanning electron microscope, crystal violet staining and measurement of fluorescence intensity resulting from resazurin reduction were performed for quantifying the bacterial adhesion. RESULTS. Surface of resin composite was significantly rougher than that of titanium and zirconia, although all tested specimens are classified as smooth. The resin specimens showed lower value of contact angle compared with titanium and zirconia specimens, and had hydrophilic surfaces. The result of scanning electron microscopy demonstrated that bound bacteria were more abundant on resin in comparison with titanium and zirconia. When total biofilm mass determined by crystal violet, absorbance value of resin was significantly higher than that of titanium or zirconia. The result of relative fluorescence intensities also demonstrated that the highest fluorescence intensity was found on the surface of resin. Absorbance value and fluorescence intensity on titanium was not significantly different from those on zirconia. CONCLUSION. Resin specimens showed the roughest surface and have a significantly higher susceptibility to adhere Streptococcus sanguis than titanium and zirconia when surfaces of each specimen were polished under same condition. There was no significant difference in bacteria adhesion between titanium and zirconia in vitro.
Abstract
PURPOSE. The aim of this in vitro study was to investigate the adhesion of initial colonizer, Streptococcus sanguis, on resin, titanium and zirconia under the same surface polishing condition. MATERIALS AND METHODS. Specimens were prepared from Z-250, cp-Ti and 3Y-TZP and polished with 1 μm diamond paste. After coating with saliva, each specimen was incubated with Streptococcus sanguis. Scanning electron microscope, crystal violet staining and measurement of fluorescence intensity resulting from resazurin reduction were performed for quantifying the bacterial adhesion. RESULTS. Surface of resin composite was significantly rougher than that of titanium and zirconia, although all tested specimens are classified as smooth. The resin specimens showed lower value of contact angle compared with titanium and zirconia specimens, and had hydrophilic surfaces. The result of scanning electron microscopy demonstrated that bound bacteria were more abundant on resin in comparison with titanium and zirconia. When total biofilm mass determined by crystal violet, absorbance value of resin was significantly higher than that of titanium or zirconia. The result of relative fluorescence intensities also demonstrated that the highest fluorescence intensity was found on the surface of resin. Absorbance value and fluorescence intensity on titanium was not significantly different from those on zirconia. CONCLUSION. Resin specimens showed the roughest surface and have a significantly higher susceptibility to adhere Streptococcus sanguis than titanium and zirconia when surfaces of each specimen were polished under same condition. There was no significant difference in bacteria adhesion between titanium and zirconia in vitro.
참고문헌 (18)
- Filoche S, "Oral biofilms: emerging concepts in microbial ecology", J Dent Res, 89, pp.8~18 (2010)
- Scheie AA, "The biofilm concept: consequences for future prophylaxis of oral diseases", Crit Rev Oral Biol Med, 15, pp.4~12 (2004)
- Ono M, "Surface properties of resin composite materials relative to biofilm formation", Dent Mater J, 26, pp.613~622 (2007)
- Hojo K, "Bacterial interactions in dental biofilm development", J Dent Res, 88, pp.982~990 (2009)
- Li J, "Identification of early microbial colonizers in human dental biofilm", J Appl Microbiol, 97, pp.1311~1318 (2004)
- Teughels W, "Effect of material characteristics and", or surface topography on biofilm development, 2006, pp.17, 68~81
- Subramani K, "Biofilm on dental implants: a review of the literature", Int J Oral Maxillofac Implants, 24, pp.616~626 (2009)
- Busscher HJ, "Biofilm formation on dental restorative and implant materials", J Dent Res, 89, pp.657~665 (2010)
- Scarano A, "Bacterial adhesion on commercially pure titanium and zirconium oxide disks: an in vivo human study", J Periodontol, 75, pp.292~296 (2004)
- Auschill TM, "The effect of dental restorative materials on dental biofilm", Eur J Oral Sci, 110, pp.48~53 (2002)
- Hahnel S, "Surface characterization of dental ceramics and initial streptococcal adhesion in vitro", Dent Mater, 25, pp.969~975 (2009)
- Manicone PF, "An overview of zirconia ceramics: basic properties and clinical applications", J Dent, 35, pp.819~826 (2007)
- Ikeda M, "Effect of surface characteristics on adherence of S. mutans biofilms to indirect resin composites", Dent Mater J, 26, pp.915~923 (2007)
- Pihlstrom BL, "Periodontal diseases", Lancet, 366, pp.1809~1820 (2005)
- Quirynen M, "The influence of surface roughness and surface-free energy on supra- and subgingival plaque formation in man. A review of the literature", J Clin Periodontol, 22, pp.1~14 (1995)
- Bollen CM, "Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: a review of the literature", Dent Mater, 13, pp.258~269 (1997)
- Al-Ahmad A, "Biofilm formation and composition on different implant materials in vivo", J Biomed Mater Res B Appl Biomater, 95, pp.101~109 (2010)
- Puckett SD, "The relationship between the nanostructure of titanium surfaces and bacterial attachment", Biomaterials, 31, pp.706~713 (2010)