PURPOSE. To investigate the effect of reducing tooth preparation and ceramic thickness on fracture resistance of lithium disilicate crowns. MATERIALS AND METHODS. Specimen preparation included a standard complete crown preparation of a typodont mandibular left first molar with an occlusal reduction of 2 mm, proximal/axial wall reduction of 1.5 mm, and 1.0 mm deep chamfer (Group A). Another typodont mandibular first molar was prepared with less tooth reduction: 1 mm occlusal and proximal/axial wall reduction and 0.8 mm chamfer (Group B). Twenty crowns were milled from each preparation corresponding to control group (n=5) and conditioned group of simultaneous thermal and mechanical loading in aqueous environment (n=15). All crowns were then loaded until fracture to determine the fracture load. RESULTS. The mean (SD) fracture load values (in Newton) for Group A were 2340 (83) and 2149 (649), and for Group B, 1752 (134) and 1054 (249) without and with fatigue, respectively. Reducing tooth preparation thickness significantly decreased fracture load of the crowns at baseline and after fatigue application. After fatigue, the mean fracture load statistically significantly decreased (P<.001) in Group B; however, it was not affected (P>.05) in Group A. CONCLUSION. Reducing the amount of tooth preparation by 0.5 mm on the occlusal and proximal/axial wall with a 0.8 mm chamfer significantly reduced fracture load of the restoration. Tooth reduction required for lithium disilicate crowns is a crucial factor for a long-term successful application of this all-ceramic system.
Abstract
PURPOSE. To investigate the effect of reducing tooth preparation and ceramic thickness on fracture resistance of lithium disilicate crowns. MATERIALS AND METHODS. Specimen preparation included a standard complete crown preparation of a typodont mandibular left first molar with an occlusal reduction of 2 mm, proximal/axial wall reduction of 1.5 mm, and 1.0 mm deep chamfer (Group A). Another typodont mandibular first molar was prepared with less tooth reduction: 1 mm occlusal and proximal/axial wall reduction and 0.8 mm chamfer (Group B). Twenty crowns were milled from each preparation corresponding to control group (n=5) and conditioned group of simultaneous thermal and mechanical loading in aqueous environment (n=15). All crowns were then loaded until fracture to determine the fracture load. RESULTS. The mean (SD) fracture load values (in Newton) for Group A were 2340 (83) and 2149 (649), and for Group B, 1752 (134) and 1054 (249) without and with fatigue, respectively. Reducing tooth preparation thickness significantly decreased fracture load of the crowns at baseline and after fatigue application. After fatigue, the mean fracture load statistically significantly decreased (P<.001) in Group B; however, it was not affected (P>.05) in Group A. CONCLUSION. Reducing the amount of tooth preparation by 0.5 mm on the occlusal and proximal/axial wall with a 0.8 mm chamfer significantly reduced fracture load of the restoration. Tooth reduction required for lithium disilicate crowns is a crucial factor for a long-term successful application of this all-ceramic system.
참고문헌 (48)
- Edelhoff D, "Tooth structure removal associated with various preparation designs for posterior teeth", Int J Periodontics Restorative Dent, 22, pp.241~249 (2002)
- Seydler B, "In vitro fracture load of monolithic lithium disilicate ceramic molar crowns with different wall thicknesses", Clin Oral Investig, 18, pp.1165~1171 (2014)
- Shahrbaf S, "Fracture strength of machined ceramic crowns as a function of tooth preparation design and the elastic modulus of the cement", Dent Mater, 30, pp.234~241 (2014)
- Rekow ED, "Performance of dental ceramics: challenges for improvements", J Dent Res, 90, pp.937~952 (2011)
- Soares CJ, "Influence of cavity preparation design on fracture resistance of posterior Leucite-reinforced ceramic restorations", J Prosthet Dent, 95, pp.421~429 (2006)
- Steiner M, "In vitro evaluation of a mechanical testing chewing simulator", Dent Mater, 25, pp.494~499 (2009)
- Sibbald B, "Understanding controlled trials. Why are randomised controlled trials important?", BMJ, 316, pp.201~ (1998)
- Wiskott HW, "Stress fatigue: basic principles and prosthodontic implications", Int J Prosthodont, 8, pp.105~116 (1995)
- Naumann M, "Influence of test parameters on in vitro fracture resistance of post-endodontic restorations: a structured review", J Oral Rehabil, 36, pp.299~312 (2009)
- Kelly JR, "Clinically relevant approach to failure testing of allceramic restorations", J Prosthet Dent, 81, pp.652~661 (1999)
- Attia A, "Influence of cyclic loading and luting agents on the fracture load of two all-ceramic crown systems", J Prosthet Dent, 92, pp.551~556 (2004)
- Clausen JO, "Dynamic fatigue and fracture resistance of non-retentive all-ceramic full-coverage molar restorations. Influence of ceramic material and preparation design", Dent Mater, 26, pp.533~538 (2010)
- Albrecht T, "Fracture load of different crown systems on zirconia implant abutments", Dent Mater, 27, pp.298~303 (2011)
- Mitsias M, "Influence of zirconia abutment preparation on the fracture strength of single implant lithium disilicate crowns after chewing simulation", Clin Oral Implants Res, 25, pp.675~682 (2014)
- Zhao K, "Influence of veneer and cyclic loading on failure behavior of lithium disilicate glass-ceramic molar crowns", Dent Mater, 30, pp.164~171 (2014)
- Chitmongkolsuk S, "Fracture strength of all-ceramic lithium disilicate and porcelain-fused-to-metal bridges for molar replacement after dynamic loading", Eur J Prosthodont Restor Dent, 10, pp.15~22 (2002)
- Schultheis S, "Monolithic and bi-layer CAD", CAM lithium-disilicate versus metal-ceramic fixed dental prostheses: comparison of fracture loads and failure modes after fatigue, 2013, pp.17, 1407~1413
- Kheradmandan S, "Fracture strength of four different types of anterior 3-unit bridges after thermo-mechanical fatigue in the dual-axis chewing simulator", J Oral Rehabil, 28, pp.361~369 (2001)
- Rosentritt M, "Approach for valuating the significance of laboratory simulation", J Dent, 36, pp.1048~1053 (2008)
- Pieger S, "Clinical outcomes of lithium disilicate single crowns and partial fixed dental prostheses: a systematic review", J Prosthet Dent, 112, pp.22~30 (2014)
- Rekow ED, "Factorial analysis of variables influencing stress in all-ceramic crowns", Dent Mater, 22, pp.125~132 (2006)
- Guess PC, "Monolithic CAD", CAM lithium disilicate versus veneered Y-TZP crowns: comparison of failure modes and reliability after fatigue, 2010, pp.23, 434~442
- Reich S, "Chair-side generated posterior lithium disilicate crowns after 4 years", Clin Oral Investig, 17, pp.1765~1772 (2013)
- Kern M, "Ten-year outcome of three-unit fixed dental prostheses made from monolithic lithium disilicate ceramic", J Am Dent Assoc, 143, pp.234~240 (2012)
- Fasbinder DJ, "A clinical evaluation of chairside lithium disilicate CAD", CAM crowns: a two-year report, 2010, pp.141, 10S~14S
- Valenti M, "Retrospective survival analysis of 261lithium disilicate crowns in a private general practice", Quintessence Int, 40, pp.573~579 (2009)
- Suputtamongkol K, "Clinical performance and wear characteristics of veneered lithia-disilicate-based ceramic crowns", Dent Mater, 24, pp.667~673 (2008)
- Altamimi AM, "Comparison of fracture resistance and fracture characterization of bilayered zirconia", fluorapatite and monolithic lithium disilicate all ceramic crowns, 2014, pp.9, 98~110
- Carvalho AO, "Fatigue resistance of CAD", CAM complete crowns with a simplified cementation process, 2014, pp.111, 310~317
- Ferrario VF, "Single tooth bite forces in healthy young adults", J Oral Rehabil, 31, pp.18~22 (2004)
- Tortopidis D, "The variability of bite force measurement between sessions, in different positions within the dental arch", J Oral Rehabil, 25, pp.681~686 (1998)
- Kohyama K, "Chewing patterns of various texture foods studied by electromyography in young and elderly populations", J Texture Stud, 33, pp.269~283 (2007)
- Kohyama K, "Chewing behavior observed at different stages of mastication for six foods, studied by electromyography and jaw kinematics in young and elderly subjects", J Texture Stud, 35, pp.395~414 (2004)
- Bates JF, "Masticatory function - a review of the literature. III. Masticatory performance and efficiency", J Oral Rehabil, 3, pp.57~67 (1976)
- Kohyama K, "Effects of sample hardness on human chewing force: a model study using silicone rubber", Arch Oral Biol, 49, pp.805~816 (2004)
- Schindler HJ, "Feedback control during mastication of solid food textures-a clinical-experimental study", J Prosthet Dent, 80, pp.330~336 (1998)
- De Boever JA, "Functional occlusal forces: an investigation by telemetry", J Prosthet Dent, 40, pp.326~333 (1978)
- Kim B, "Fracture of porcelain-veneered structures in fatigue", J Dent Res, 86, pp.142~146 (2007)
- Kim JW, "Sliding contact fatigue damage in layered ceramic structures", J Dent Res, 86, pp.1046~1050 (2007)
- Heintze SD, "Fracture frequency of all-ceramic crowns during dynamic loading in a chewing simulator using different loading and luting protocols", Dent Mater, 24, pp.1352~1361 (2008)
- Dhima M, "Evaluation of fracture resistance in aqueous environment under dynamic loading of lithium disilicate restorative systems for posterior applications. Part 2", J Prosthodont, 23, pp.353~357 (2014)
- Johansson C, "Fracture strength of monolithic all-ceramic crowns made of high translucent yttrium oxide-stabilized zirconium dioxide compared to porcelain-veneered crowns and lithium disilicate crowns", Acta Odontol Scand, 72, pp.145~153 (2014)
- Rosentritt M, "Influence of stress simulation parameters on the fracture strength of allceramic fixed-partial dentures", Dent Mater, 22, pp.176~182 (2006)
- Wakabayashi N, "Crack initiation modes in bilayered alumina", porcelain disks as a function of core, J Dent Res, pp.2000, 79[DOI]
- Campbell SD., "A comparative strength study of metal ceramic and all-ceramic esthetic materials: modulus of rupture", J Prosthet Dent, 62, pp.476~479 (1989)
- Mahmood DJ, "The influence of support properties and complexity on fracture strength and fracture mode of all-ceramic fixed dental prostheses", Acta Odontol Scand, 69, pp.229~237 (2011)
- Scherrer SS, "The fracture resistance of all-ceramic crowns on supporting structures with different elastic moduli", Int J Prosthodont, 6, pp.462~467 (1993)
- Yucel MT, "Influence of the supporting die structures on the fracture strength of all-ceramic materials", Clin Oral Investig, 16, pp.1105~1110 (2012)