초록
This study investigates the directional recrystallization behavior of Ni based oxide dispersion strengthened (ODS) alloy according to the zone annealing velocity. The zone annealing temperature is set as 1390oC, while the zone velocities are set as 2.5, 4, 6, and 10 cm/h, respectively. The initial microstructure observation of the as-extruded sample shows equiaxed grains of random orientation, with an average grain size of 530 nm. On the other hand, the zone annealed samples show a large deviation in grain size depending on the zone velocities. In particular, grains with a size of several millimeters are observed at 2.5-cm/h zone velocity. It is also found that the preferred orientation varies with the zone annealing velocity. On the basis of these results, this study discusses the role of zone velocities in the directional recrystallization of Ni base ODS alloy.
Abstract
This study investigates the directional recrystallization behavior of Ni based oxide dispersion strengthened (ODS) alloy according to the zone annealing velocity. The zone annealing temperature is set as 1390oC, while the zone velocities are set as 2.5, 4, 6, and 10 cm/h, respectively. The initial microstructure observation of the as-extruded sample shows equiaxed grains of random orientation, with an average grain size of 530 nm. On the other hand, the zone annealed samples show a large deviation in grain size depending on the zone velocities. In particular, grains with a size of several millimeters are observed at 2.5-cm/h zone velocity. It is also found that the preferred orientation varies with the zone annealing velocity. On the basis of these results, this study discusses the role of zone velocities in the directional recrystallization of Ni base ODS alloy.
참고문헌 (13)
- E.F. Bradley, "Superalloys-A Technical Guide" (1988)
- R.L. Klueh, , J. Nucl. Mater., 341, pp.103~ (2005)[DOI]
- T.M. Pollock, , J. Propul. Power, 22, pp.361~ (2006)[DOI]
- C. Suryanarayana, , Prog. Mater. Sci., 46, pp.1~ (2001)[DOI]
- L. Ma, , KONA Powder Part. J., 31, pp.146~ (2014)[DOI]
- Z.W. Zhang, , Mater. Sci. Eng. A, 435-436, pp.573~ (2006)[DOI]
- A.Y. Badmos, , Acta Mater., 50, pp.3347~ (2002)[DOI]
- Z.W. Zhang, , Mater. Sci. Eng. A, 434, pp.58~ (2006)[DOI]
- M. Heilmaier, , JOM, 51, pp.23~ (1999)
- P. Podany, , Mater. Technol., 50, pp.199~ (2016)
- A.S. Taha, , Phys. Status Solidi A, 119, pp.455~ (1990)[DOI]
- S. Ukai, , J. Alloy. Compd., 744, pp.204~ (2018)[DOI]
- J. Li, , Mater. Sci. Eng. A, 392, pp.8~ (2005)[DOI]