Alloy 617계 산화물 분산강화(ODS) 합금의 제조와 인장특성
Fabrication and Tensile Properties of Alloy 617 base ODS Alloy
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Alloy 617, Ni-22Cr-12Co-9Mo base oxide dispersion strengthened alloy was fabricated by using mechanical alloying, hot isostatic pressing and hot rolling. Uniaxial tensile tests were performed at room temperature and at 700°C. Compared with the conventional Alloy 617, ODS alloy showed much higher yield strength and tensile strength, but lower elongation. Fracture surfaces of the tensile tested specimens were investigated in order to find out the mechanism of fracture mode at each test temperature. Grain adjustment during tensile deformation was analyzed by electron backscattered diffraction mapping, inverse pole figures and TEM observation.
Abstract
Alloy 617, Ni-22Cr-12Co-9Mo base oxide dispersion strengthened alloy was fabricated by using mechanical alloying, hot isostatic pressing and hot rolling. Uniaxial tensile tests were performed at room temperature and at 700°C. Compared with the conventional Alloy 617, ODS alloy showed much higher yield strength and tensile strength, but lower elongation. Fracture surfaces of the tensile tested specimens were investigated in order to find out the mechanism of fracture mode at each test temperature. Grain adjustment during tensile deformation was analyzed by electron backscattered diffraction mapping, inverse pole figures and TEM observation.
참고문헌 (14)
- 김우곤, "초고온가스로 중간 열교환기용 Alloy 617의 장시간 크리프 변형률-시간 곡선 모델링", 대한금속·재료학회지, 47(10), pp.613~620 (2009), 대한금속·재료학회
- T. Hirano, "R. Watanabe", Metall. Trans, 12A, pp.451~ (1981)
- Soo-Haeng Cho, "Corrosion Behavior of Ni-Base Alloys in a Hot Lithium Molten Salt under an Oxidizing Atmosphere", Metals and Materials International, 13(4), pp.303~309 (2007), 대한금속·재료학회
- T. H. Bassford, , Nucl. Technol, 66, pp.35~ (1984)
- "INCONEL alloy 617, SMC-029" (2005), Special Metals Corporation
- E. Orown, , Trans Inst. Eng. Shipbuild Scotl, 89, pp.165~ (1946)
- F. J. Humphreys, , Phil. Mag, 16, pp.927~ (1967)
- A. H. Clauer, , Met. Sci. J, 1, pp.86~ (1967)
- I. S. Kim, , Met. Mater. Int, 6, pp.513~ (2000)
- I. S. Kim, , J. of Nucl. Mater, 280, pp.264~ (2000)
- C. Suryanarayana, , Progress in Materials Science, 46, pp.6~ (2001)
- I. H. Kim, "Mechanical Property, Phase Transformation and High Temperature Oxidation Characteristics of ODS Ni-base Alloy with Nano Sized Grains Fabricated by Mechanical Alloying Method", 박사, pp.2006
- J. H. Kim, , J. of Nucl. Mater, 407, pp.143~ (2010)
- F. J. Humphreys, "Recrystallization and related annealing phenomena", pp.78~79 (2004), Elsevier