Ta20Nb20V20W20Ti20 하이엔트로피 합금의 미세조직 및 기계적 특성에 미치는 밀링 시간의 영향
Effect of Milling Time on the Microstructure and Mechanical Properties of Ta20Nb20V20W20Ti20 High Entropy Alloy
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, we report the microstructure and characterization of Ta20Nb20V20W20Ti20 high-entropy alloy powders and sintered samples. The effects of milling time on the microstructure and mechanical properties were investigated in detail. Microstructure and structural characterization were performed by scanning electron microscopy and X-ray diffraction. The mechanical properties of the sintered samples were analyzed through a compressive test at room temperature with a strain rate of 1 × 10−4 s−1. The microstructure of sintered Ta20Nb20V20W20Ti20 high-entropy alloy is composed of a BCC phase and a TiO phase. A better combination of compressive strength and strain was achieved by using prealloyed Ta20Nb20V20W20Ti20 powder with low oxygen content. The results suggest that the oxide formed during the sintering process affects the mechanical properties of Ta20Nb20V20W20Ti20 high-entropy alloys, which are related to the interfacial stability between the BCC matrix and TiO phase.
Abstract
In this study, we report the microstructure and characterization of Ta20Nb20V20W20Ti20 high-entropy alloy powders and sintered samples. The effects of milling time on the microstructure and mechanical properties were investigated in detail. Microstructure and structural characterization were performed by scanning electron microscopy and X-ray diffraction. The mechanical properties of the sintered samples were analyzed through a compressive test at room temperature with a strain rate of 1 × 10−4 s−1. The microstructure of sintered Ta20Nb20V20W20Ti20 high-entropy alloy is composed of a BCC phase and a TiO phase. A better combination of compressive strength and strain was achieved by using prealloyed Ta20Nb20V20W20Ti20 powder with low oxygen content. The results suggest that the oxide formed during the sintering process affects the mechanical properties of Ta20Nb20V20W20Ti20 high-entropy alloys, which are related to the interfacial stability between the BCC matrix and TiO phase.
참고문헌 (17)
- J. -W. Yeh, , Adv. Eng. Mater, 6, pp.299~ (2004)
- Y. Zhang, , Prog. Mater. Sci, 61, pp.1~ (2014)
- M. -H. Tsai, , Mater. Res. Lett, 2, pp.107~ (2014)
- M. G. Poletti, , Mater. Des, 115, pp.247~ (2017)
- 이제인, "혼합엔트로피 제어에 따른 단일 FCC 고용체 합금의 물성변화 분석", 대한금속·재료학회지, 55(1), pp.1~9 (2017), 대한금속·재료학회
- S. I. Hong, , Mater. Sci. Eng. A, 682, pp.569~ (2017)
- B. Gludovatz, , Science, 345, pp.1153~ (2014)
- Y. S. Na, , Trends Met. Mater. Eng, 30, pp.50~ (2017)
- O. N. Senkov, , Intermetallics, 19, pp.698~ (2011)
- O. N. Senkov, , Acta Mater, 68, pp.214~ (2014)
- O. N. Senkov, , J. Mater. Res, 33, pp.3092~ (2018)
- S. Praveen, , Adv. Eng. Mater, 20, pp.1~ (2018)
- W. Guo, , J. Alloys Compd, 776, pp.428~ (2019)
- K. S. Kormout, , Adv. Eng. Mater, 19, pp.1~ (2017)
- D. Raabe, , Acta Mater, 57, pp.5254~ (2009)
- Y. -L. Chen, , J. Alloys Compd, 481, pp.768~ (2009)
- H. Hadraba, , Mater. Sci. Eng. A, 689, pp.252~ (2017)