분말야금법으로 제조한 새로운 Co10Fe10Mn35Ni35Zn10 고엔트로피 합금
New Co10Fe10Mn35Ni35Zn10 high-entropy alloy Fabricated by Powder Metallurgy
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this paper, a new Co10Fe10Mn35Ni35Zn10 high entropy alloy (HEA) is identified as a strong candidate for the single face-centered cubic (FCC) structure screened using the upgraded TCFE2000 thermodynamic CALPHAD database. The Co10Fe10Mn35Ni35Zn10 HEA is fabricated using the mechanical (MA) procedure and pressure-less sintering method. The Co10Fe10Mn35Ni35Zn10 HEA, which consists of elements with a large difference in melting point and atomic size, is successfully fabricated using powder metallurgy techniques. The MA behavior, microstructure, and mechanical properties of the Co10Fe10Mn35Ni35Zn10 HEA are systematically studied to understand the MA behavior and develop advanced techniques for fabricating HEA products. After MA, a single FCC phase is found. After sintering at 900oC, the microstructure has an FCC single phase with an average grain size of 18 μm. Finally, the Co10Fe10Mn35Ni35Zn10 HEA has a compressive yield strength of 302 MPa.
Abstract
In this paper, a new Co10Fe10Mn35Ni35Zn10 high entropy alloy (HEA) is identified as a strong candidate for the single face-centered cubic (FCC) structure screened using the upgraded TCFE2000 thermodynamic CALPHAD database. The Co10Fe10Mn35Ni35Zn10 HEA is fabricated using the mechanical (MA) procedure and pressure-less sintering method. The Co10Fe10Mn35Ni35Zn10 HEA, which consists of elements with a large difference in melting point and atomic size, is successfully fabricated using powder metallurgy techniques. The MA behavior, microstructure, and mechanical properties of the Co10Fe10Mn35Ni35Zn10 HEA are systematically studied to understand the MA behavior and develop advanced techniques for fabricating HEA products. After MA, a single FCC phase is found. After sintering at 900oC, the microstructure has an FCC single phase with an average grain size of 18 μm. Finally, the Co10Fe10Mn35Ni35Zn10 HEA has a compressive yield strength of 302 MPa.
참고문헌 (21)
- J. W. Yeh, , Adv. Eng. Mater., 6, pp.299~ (2004)[DOI]
- J. W. Yeh, , Metall. Mater. Trans. A, 35, pp.2533~ (2004)[DOI]
- B. Cantor, , Mater. Sci. Eng. A, 375-377, pp.213~ (2004)[DOI]
- J. M. Wu, , Wear, 261, pp.513~ (2006)[DOI]
- Y. H. Jo, , Nat. Commun., 15719, pp.1~ (2017)
- O. N. Senkov, , Intermetallics, 19, pp.698~ (2011)[DOI]
- P. P. Bhattacharjee, , J. Alloys Compd., 587, pp.544~ (2014)[DOI]
- S. Singh, , Acta Mater., 59, pp.182~ (2011)[DOI]
- T. T. Shun, , J. Alloys Compd., 478, pp.269~ (2009)[DOI]
- S. H. Joo, , J. Alloys Compd., 698, pp.591~ (2017)[DOI]
- D. Yim, , Mater. Sci. Eng. A, 708, pp.291~ (2017)[DOI]
- S. Praveen, , J. Alloys Compd., 662, pp.361~ (2016)[DOI]
- 최원미, "Design of New Face-Centered Cubic High Entropy Alloys by Thermodynamic Calculation", Metals and Materials International, 23(5), pp.839~847 (2017), 대한금속·재료학회[DOI]
- C. Suryanarayana, , Prog. Mater. Sci., 46, pp.1~ (2001)[DOI]
- Y. L. Chen, , J. Alloys Compd., 481, pp.768~ (2009)[DOI]
- D. A. Porter, , Annu. Rev. Mater. Sci., 3, pp.327~ (1973)[DOI]
- D. A. Porter, , Annu. Rev. Mater. Sci., 3, pp.327~ (1973)[DOI]
- X. Yang, , Mater. Che. Phys., 132, pp.233~ (2012)[DOI]
- S. Guo, , Prog. Nat. Sci. Mater. Int., 21, pp.433~ (2011)[DOI]
- S. Guo, , J. Appl. Phys., 109, pp.1~ (2011)
- O. N. Senkov, , JOM, 66, pp.2030~ (2014)[DOI]