방전플라즈마소결로 제조된 나노결정 FeNiCrMoMnSiC 합금의 오스테나이트 안정성과 기계적 특성
Austenite Stability and Mechanical Properties of Nanocrystalline FeNiCrMoMnSiC Alloy Fabricated by Spark Plasma Sintering
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, a nanocrystalline FeNiCrMoMnSiC alloy was fabricated, and its austenite stability, microstructure, and mechanical properties were investigated. A sintered FeNiCrMoMnSiC alloy sample with nanosized crystal was obtained by high-energy ball milling and spark plasma sintering. The sintering behavior was investigated by measuring the displacement according to the temperature of the sintered body. Through microstructural analysis, it was confirmed that a compact sintered body with few pores was produced, and cementite was formed. The stability of the austenite phase in the sintered samples was evaluated by X-ray diffraction analysis and electron backscatter diffraction. Results revealed a measured value of 51.6% and that the alloy had seven times more austenite stability than AISI 4340 wrought steel. The hardness of the sintered alloy was 60.4 HRC, which was up to 2.4 times higher than that of wrought steel.
Abstract
In this study, a nanocrystalline FeNiCrMoMnSiC alloy was fabricated, and its austenite stability, microstructure, and mechanical properties were investigated. A sintered FeNiCrMoMnSiC alloy sample with nanosized crystal was obtained by high-energy ball milling and spark plasma sintering. The sintering behavior was investigated by measuring the displacement according to the temperature of the sintered body. Through microstructural analysis, it was confirmed that a compact sintered body with few pores was produced, and cementite was formed. The stability of the austenite phase in the sintered samples was evaluated by X-ray diffraction analysis and electron backscatter diffraction. Results revealed a measured value of 51.6% and that the alloy had seven times more austenite stability than AISI 4340 wrought steel. The hardness of the sintered alloy was 60.4 HRC, which was up to 2.4 times higher than that of wrought steel.
참고문헌 (31)
- W. S. Lee, , J. Mater. Process. Technol, 87, pp.198~ (1999)
- Y. Tomita, , Metall. Trans. A, 22A, pp.1093~ (1991)
- R. L. McDaniels, , Metall. Trans. A, 485, pp.500~ (2008)
- G. Frommeyer, , ISIJ Int, 43, pp.438~ (2003)
- D. S. Park, , Arch. Metall. Mater, 63, pp.1479~ (2018)
- S. G. Choi, , Arch. Metall. Mater, 65, pp.1001~ (2020)
- C. N. Sastry, , Metall. Trans. A,, 13A, pp.676~ (1982)
- R. O. Ritchie, , Metall. Trans. A, 9A, pp.331~ (1978)
- S. J. Lee, , Int. J. Mater. Res, 104, pp.423~ (2013)
- J. Jeon, , Arch. Metall. Mater, 65, pp.1249~ (2020)
- 김영무, "탄탈륨 및 탄탈륨-텅스텐 합금 분말의 소결성 및 미세조직 연구", 한국분말재료학회지, 27(5), pp.373~380 (2020), 한국분말재료학회
- G. Kim, , Arch. Metall. Mater, 66, pp.759~ (2021)
- 오승진, "나노결정 FeMnNiC합금의 오스테나이트 안정성", 한국분말재료학회지, 26(5), pp.389~394 (2019), 한국분말재료학회[DOI]
- S. J. Oh, , Mater. Sci. Eng. A, 725, pp.382~ (2018)
- 김광훈, "소성유기마르텐사이트 변태에 의한 나노결정 FeCrC 소결합금의 기계적 강도 향상", 한국분말재료학회지, 28(3), pp.246~252 (2021), 한국분말재료학회
- G. Delaizir, , Mater. Res. Bull, 47, pp.1954~ (2012)
- V. Mihalache, , Powder Technol, 347, pp.103~ (2019)
- C. B. Wei, , Mater. Sci. Eng. A, 552, pp.427~ (2012)
- K. Chen, , J. Am. Ceram. Soc, 91, pp.2475~ (2008)
- B. L. Averbach, , Trans. AIME, 176, pp.401~ (1948)
- G. K. Williamson, , Acta Metall, 1, pp.22~ (1953)
- K. Oh-ishi, , Mater. Sci. Eng. A, 456, pp.20~ (2007)
- H. W. Zhang, , Scr. Mater, 53, pp.863~ (2005)
- C. Zheng, , Mater. Sci. Eng. A, 599, pp.16~ (2014)
- M. M. Bilal, , J. Mater. Res. Technol, 8, pp.5194~ (2019)
- S. Zhirafar, , J. Mater. Process. Technol, 186, pp.298~ (2007)
- P. Phetlam, , Mater. Des, 82, pp.189~ (2015)
- N. Niazi, , Int. J. Mater. Sci. Eng, 5, pp.6~ (2014)
- M. Houssny-Emam, , Mater. Sci. Eng, 61, pp.79~ (1983)
- I. Polyzois, , Mater. Sci. Eng. A, 631, pp.18~ (2015)
- S. J. Lee, , Mater. Des, 29, pp.1840~ (2008)