Bi-Te 및 Bi-Sb-Te 나노와이어로 구성된 열전소자의 형성공정
Fabrication Process of the Thermoelectric Module Composed of the Bi-Te and the Bi-Sb-Te Nanowires
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
n형 Bi-Te 박막과 p형 Bi-Sb-Te 박막을 전기도금법으로 형성하여 열전특성을 측정하였으며, Bi-Te 나노와이어와 Bi-Sb-Te 나노와이어의 전기도금 성장거동을 분석하였다. 알루미나 템프레이트의 200nm 직경의 나노기공 내에 전기도금으로 Bi-Te 나노와이어와 Bi-Sb-Te 나노와이어를 형성시 각기 81%와 77%의 filling 비를 나타내었다. 알루미나 템프레이트에 Bi-Te 나노와이어와 Bi-Sb-Te 나노와이어 를 순차적으로 전기도금하여 열전소자를 구성하였으며, Bi-Te 나노와이어 부위의 Ni 전극과 Bi-Sb-Te 나 노와이어 부위의 Ni 전극 사이에서 15 Ω의 저항이 측정되었다.
Abstract
Thermoelectric properties of the n-type Bi-Te and the p-type Bi-Sb-Te films were measured and the growth behaviors of the electrodeposited Bi-Te and Bi-Sb-Te nanowires were characterized. Filling ratios of 81% and 77% were obtained for electrodeposition of the Bi-Te and the Bi-Sb-Te nanowires, respectively, into the nano pores of 200 nm-diameter of an alumina template. A thermoelectric module, composed of the Bi-Te nanowires and the Bi-Sb-Te nanowires was processed by electrodeposition, and a resistance value of 15 Ω was measured between the Ni electrodes formed on the Bi-Te nanowires and the Bi-Sb-Te nanowires of the module.
참고문헌 (18)
- D. M. Rowe, "CRC Handbook of Thermoelectrics" (1995), CRC Press
- M. A. Ryan, , Electochem. Soc. Interface, 11, pp.30~ (2002)
- B. Poudel, , Science, 320, pp.634~ (2008)
- B. W. Kim, , Phys. Rev. Lett, 96, pp.45901~ (2006)
- R. Venkatasubramanian, , Phys. Rev. B, 61, pp.3091~ (2000)
- X. Sun, , Appl. Phys. Lett, 74, pp.4005~ (1999)
- M. S. Dresselhaus, , Adv. Mater, 19, pp.1~ (2007)
- B. Yoo, , Adv. Mater, 19, pp.296~ (2007)
- R. Venkatasubramanian, , Nature, 413, pp.597~ (2001)
- T. C. Harman, , Science, 297, pp.2229~ (2002)
- T. Koga, , Appl. Phys. Lett, 77, pp.1490~ (2000)
- O. Yamashita, , J. Mater. Sci, 42, pp.5867~ (2007)
- A. L. Prieto, , J. Am. Chem. Soc, 123, pp.7160~ (2001)
- W. Wang, , J. Appl. Phys, 96, pp.615~ (2004)
- J. R. Lim, , Adv. Mater, 17, pp.1488~ (2005)
- W. M. Yim, , J. Solid-State Electronics, 15, pp.1121~ (1972)
- K. Y. Lee, , J. Korean Metall. Mater, 40, pp.333~ (2002)
- T. S. Oh, , Scripta Mater, 42, pp.849~ (2000)