OLED 소자의 특성에 미치는 밀봉 버퍼용 고분자박막의 영향
The Effect of Polymer Thin Film for Sealing Buffer on the Characteristics of OLED Device
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this paper, the LiF and polymer thin film as passivation layer have been evaporated on green OLED devices. HDPE, polyacenaphthylene, polytetrafluoroethylene, poly(2,6-dimethyl-1,4-pheneylene oxide), polysulfone and poly(dimer-acid-co-alkyl poly-amine) have been used as polymer materials. The optical transmittance of evaporated polymer thin film was very good as an above 90% in visible range. The morphology of polymer thin film was measured by AFM. As a result of the measurement average roughness(Ra) value of the polysulfone was very low as 2.2nm. The green OLED devices with a structure of ITO/HIL/HTL/ EML/Buffer/Al in series of various passivation films were fabricated and analyzed. It was observed that an OLED device with LiF as first passivation film has shown the good electrical and optical property, and all kind of polymer films did not influence on the I-V-L characteristics and the life time of OLED devices. Therefore, we found that polymer layer played a key role as a buffer layer between the inorganic passivation layers to relieve the stress of the inorganic layers.
Abstract
In this paper, the LiF and polymer thin film as passivation layer have been evaporated on green OLED devices. HDPE, polyacenaphthylene, polytetrafluoroethylene, poly(2,6-dimethyl-1,4-pheneylene oxide), polysulfone and poly(dimer-acid-co-alkyl poly-amine) have been used as polymer materials. The optical transmittance of evaporated polymer thin film was very good as an above 90% in visible range. The morphology of polymer thin film was measured by AFM. As a result of the measurement average roughness(Ra) value of the polysulfone was very low as 2.2nm. The green OLED devices with a structure of ITO/HIL/HTL/ EML/Buffer/Al in series of various passivation films were fabricated and analyzed. It was observed that an OLED device with LiF as first passivation film has shown the good electrical and optical property, and all kind of polymer films did not influence on the I-V-L characteristics and the life time of OLED devices. Therefore, we found that polymer layer played a key role as a buffer layer between the inorganic passivation layers to relieve the stress of the inorganic layers.
참고문헌 (18)
- C. W. Tang, , Appl. Phys. Lett, 51, pp.913~ (1987)
- 주성후, "SiNx 박막에 의한 OLED 소자의 보호막 특성", 전기전자재료학회논문지, 19(8), pp.758~763 (2006), 한국전기전자재료학회
- Z. Y. Xie, , Appl. Phys. Lett, 84(7), pp.1207~ (2004)
- C. N. Li, , Appl. Phys. A, 80, pp.301~ (2005)
- H. Aziz, , Appl. Phys. Lett, 72, pp.2642~ (1998)
- B. H. Cumpston, , J. Appl. Phys, 81, pp.3716~ (1997)
- V. N. Bliznyuk, , Macromolecules, 32, pp.361~ (1999)
- K. K. Lien, , J. Appl. Phys, 90, pp.976~ (2001)
- P. E. Burrows, , Appl. Phys. Lett, 65, pp.2922~ (1994)
- K. Yamashita, , J. Phys. D. Appl. Phys, 34, pp.740~ (2001)
- S. Kho, , Jpn. J. Appl. Phys, 41, pp.L1336~ (2002)
- S. H. Kwon, , Appl. Phys. Lett, 79, pp.4450~ (2001)
- M. S. Weaver, , Appl. Phys. Lett, 81, pp.2929~ (2002)
- J. D. Affinito, , Thin Solid Films, 308, pp.19~ (1997)
- P. E. Burrows, , Displays, 22, pp.65~ (2001)
- W. Graupner, , pp.11~ (2000), SPIE Proceedings
- R. C. Kwong, , Appl. Phys. Lett, 81, pp.162~ (2002)
- Shizuo Tokito, "유기 EL 디스플레이 기초와 응용", pp.125~ (2006), 성안당