접착 필름과 평판 유리를 이용하여 봉지된 유기 발광 소자의 발광 특성
Emission Characteristics of Encapsulated Organic Light Emitting Devices Using Attaching Film and Flat Glass
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
To study the encapsulation method for large-area organic light emitting devices (OLEDs), OLED of ITO /2-TNATA / NPB / Alq3:Rubrene / Alq3 / LiF / Al structure was fabricated, which on Alq3/LiF/Al as protective layer of OLED was deposited to protect the damage of OLED, and subsequently it was encapsulated using attaching film and flat glass. The current density and luminance of encapsulated OLED using attaching film and flat glass has similar characteristics compared with non-encapsulated OLED when thickness of Al as a protective layer was 1200 nm, otherwise power efficiency of encapsulated OLED was better than nonencapsulated OLED. Encapsulation process using attaching film and flat glass did not have any effects on the emission spectrum and the Commission International de L’Eclairage (CIE) coordinate. The lifetime of encapsulated OLED using attaching film and flat glass was 287 hours in 1200 nm Al thickness, which was increased according to thickness of Al protective layer, and was improved 54% compared with 186 hours in same Al thickness, lifetime of encapsulated OLED using epoxy and flat glass. As a result, it showed the improved efficiency and the long lifetime, because the encapsulation method using attaching film and flat glass could minimize the impact on OLED caused through UV hardening process in case of glass encapsulation using epoxy.
Abstract
To study the encapsulation method for large-area organic light emitting devices (OLEDs), OLED of ITO /2-TNATA / NPB / Alq3:Rubrene / Alq3 / LiF / Al structure was fabricated, which on Alq3/LiF/Al as protective layer of OLED was deposited to protect the damage of OLED, and subsequently it was encapsulated using attaching film and flat glass. The current density and luminance of encapsulated OLED using attaching film and flat glass has similar characteristics compared with non-encapsulated OLED when thickness of Al as a protective layer was 1200 nm, otherwise power efficiency of encapsulated OLED was better than nonencapsulated OLED. Encapsulation process using attaching film and flat glass did not have any effects on the emission spectrum and the Commission International de L’Eclairage (CIE) coordinate. The lifetime of encapsulated OLED using attaching film and flat glass was 287 hours in 1200 nm Al thickness, which was increased according to thickness of Al protective layer, and was improved 54% compared with 186 hours in same Al thickness, lifetime of encapsulated OLED using epoxy and flat glass. As a result, it showed the improved efficiency and the long lifetime, because the encapsulation method using attaching film and flat glass could minimize the impact on OLED caused through UV hardening process in case of glass encapsulation using epoxy.
참고문헌 (9)
- G. Parthasarathy, , Appl. Phys. Lett, 76, pp.2128~ (2000)
- J. Kido, , Science, 267, pp.1332~ (1995)
- 장지근, "Alq3:Rubrene-GDI4234 형광 시스템을 이용한적색 OLED의 제작과 특성 평가", 전기전자재료학회논문지, 19(5), pp.437~441 (2006), 한국전기전자재료학회
- 주성후, "SiNx 박막에 의한 OLED 소자의 보호막 특성", 전기전자재료학회논문지, 19(8), pp.758~763 (2006), 한국전기전자재료학회
- Y. Sato, , IEEE J. Selected Topics in Quantum Electron, 4, pp.40~ (1998)
- Z. D. Popovic, , IEEE J. Selected Topics in Quantum Electron, 8, pp.362~ (2002)
- H. Kubota, , J. of Luminescence, 87·88, pp.56~ (2000)
- 박민경, "평판 유리로 봉인된 다층 무기 박막을 갖는 OLED 봉지 방법", 전기전자재료학회논문지, 24(11), pp.905~910 (2011), 한국전기전자재료학회
- 주성후, "OLED소자의 수명에 미치는 다층 보호막의 영향", 한국표면공학회지, 45(1), pp.20~24 (2012), 한국표면공학회