치과 임플란트 고정체의 여러 가지 제조공정과정에 따른 표면특성
Surface Characteristics of Dental Implant Fixture with Various Manufacturing Process
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, surface characteristics of dental implant fixture with various manufacturing process have been researched using electrochemical methods. The dental implant fixture was selected with 5 steps by cleaning, surface treatment and sterilization with same size and screw structure; the 1st step-machined surface, 2nd step-cleaned by thinner and prosol solution, 3th step-surface treated by RBM (resorbable blasting media) method, 4th step-cleaned and dried, 5th step-sterilized by gamma-ray. The electrochemical behavior of dental implant fixture has been evaluated by using potentiostat (EG&G Co, 2273A) in 0.9 % NaCl solution at 36.5±1℃. The corrosion surface was observed using field-emission scanning electron microscopy (FE-SEM) and energy dispersive x-ray spectroscopy (EDS). The step 5 sample showed the cleaner and rougher surface than step 3 sample. The step 5 sample of implant fixture treated by RBM and gamma sterilization showed the low corrosion current density compared to others. Especially, the step 3 sample of implant fixture treated by RBM was presented the lowest value of corrosion resistance and the highest value of corrosion current density. The step 3 sample showed the low value of polarization resistance compared to other samples. In conclusion, the implant fixture treated with RBM and gamma sterilization has the higher corrosion resistance, and corrosion resistance depends on the step of manufacturing process.
Abstract
In this study, surface characteristics of dental implant fixture with various manufacturing process have been researched using electrochemical methods. The dental implant fixture was selected with 5 steps by cleaning, surface treatment and sterilization with same size and screw structure; the 1st step-machined surface, 2nd step-cleaned by thinner and prosol solution, 3th step-surface treated by RBM (resorbable blasting media) method, 4th step-cleaned and dried, 5th step-sterilized by gamma-ray. The electrochemical behavior of dental implant fixture has been evaluated by using potentiostat (EG&G Co, 2273A) in 0.9 % NaCl solution at 36.5±1℃. The corrosion surface was observed using field-emission scanning electron microscopy (FE-SEM) and energy dispersive x-ray spectroscopy (EDS). The step 5 sample showed the cleaner and rougher surface than step 3 sample. The step 5 sample of implant fixture treated by RBM and gamma sterilization showed the low corrosion current density compared to others. Especially, the step 3 sample of implant fixture treated by RBM was presented the lowest value of corrosion resistance and the highest value of corrosion current density. The step 3 sample showed the low value of polarization resistance compared to other samples. In conclusion, the implant fixture treated with RBM and gamma sterilization has the higher corrosion resistance, and corrosion resistance depends on the step of manufacturing process.
참고문헌 (18)
- D. M. Brunette, "Titanium in Medicine" (2001), Springer
- A. Balfour, , J. Prosthet. Dent., 73, pp.36~ (1995)
- P. Binon, , Implant Dentistry, 5, pp.235~ (1996)
- 김원기, "치과용 Ti-6Al-4V 합금 골 고정판 표면에 형성된 나노튜브의 부식거동", 한국표면공학회지, 43(1), pp.25~30 (2010), 한국표면공학회
- S. Hobo, "Osseointegration and Occlusal Rehabilitation" (1989), Quintessence
- H. Hamanaka, "Titanium and Titanium Alloys: Dental Materials of Preference in the 21th Century", Proceedings of the Fifth International Symposium on Titanium in Dentistry, Society for Titanium Alloys in Dentistry (2001)
- L. R. Rubin, "Biomaterials in Reconstructive Surgery" (1983), C. V. Mosby
- D. D Deligianni, , Biometer. Res., 32, pp.166~ (2001)
- Z. Schwarts, , J. Periodontal Res., 32, pp.166~ (1997)
- B. Feng, , J. Mater. Sci. Mater. Med., 13, pp.457~ (2002)
- B. Kasemo, "Metal Selection and Surface Characteristics", pp.99~ (1985), Quintessence
- A. F. Recum, , Biomaterials, 9, pp.297~ (1990)
- A. K. Shukla, , J .Alloys Comp., 24, pp.144~ (2005)
- 이 강, "양극산화처리된 치과용 임플란트 합금의 전기화학적 특성", 대한치과기재학회지, 35(3), pp.285~296 (2008), 대한치과기재학회
- N. Ibris, , J. Electro. Chem., 526, pp.53~ (2002)
- E. Obayashi, , Mater Sci.:Mater. Med., 9, pp.567~ (1998)
- D. M. Brunette, "Titanium in Medicine. Engineering Materials" (2001), Springer
- R. R. Winston, , Corros. Sci., 9, pp.755~ (1969)