ZrN 및 TiN 코팅된 치과교정 용 미니나사의 표면특성과 전기화학적 거동
Surface Characteristics and Electrochemical Behaviors ofTiN and ZrN Coated Orthodontic Mini-screw
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The dental orthodontic mini-screw requires good mechanical properties and high corrosion resistance for implantation in the bone. The purpose of this study was to investigate the electrochemical characteristics of TiN and ZrN coated orthodontic mini-screws, mini-screws were used for experiment. Ion plating was carried out for mini-screw using Ti and Zr coating materials with nitrogen gas. Ion plated surface of each specimen was observed with field emission scanning electron microscopy (FE-SEM), energy dispersive x-ray spectroscopy (EDX), and electrochemical tester. The surface of TiN and ZrN coated mini-screw were more smooth than that of other kinds of non-coated mini-screw due to dercrease of machined defects. The corrosion current density of the TiN and ZrN coated mini-screw decreased compared to non-coated sample. The corrosion potential of TiN and ZrN coated mini-screw were higher than that of non-coated mini-screw in 0.9% NaCl solution. The pitting corrosion resistance increased in the order of ZrN coated, TiN coated and non-coated wire. Pitting potential of ZrN coated mini-screw was the highest in the other specimens.
Abstract
The dental orthodontic mini-screw requires good mechanical properties and high corrosion resistance for implantation in the bone. The purpose of this study was to investigate the electrochemical characteristics of TiN and ZrN coated orthodontic mini-screws, mini-screws were used for experiment. Ion plating was carried out for mini-screw using Ti and Zr coating materials with nitrogen gas. Ion plated surface of each specimen was observed with field emission scanning electron microscopy (FE-SEM), energy dispersive x-ray spectroscopy (EDX), and electrochemical tester. The surface of TiN and ZrN coated mini-screw were more smooth than that of other kinds of non-coated mini-screw due to dercrease of machined defects. The corrosion current density of the TiN and ZrN coated mini-screw decreased compared to non-coated sample. The corrosion potential of TiN and ZrN coated mini-screw were higher than that of non-coated mini-screw in 0.9% NaCl solution. The pitting corrosion resistance increased in the order of ZrN coated, TiN coated and non-coated wire. Pitting potential of ZrN coated mini-screw was the highest in the other specimens.
참고문헌 (15)
- D.E. Peebles, , Thin Solid Films, 173, pp.19~ (1989)
- K.H. Habig, , Surf. Coat. Technol, 42, pp.133~ (1990)
- R.I. Damaschek, , Surf. Eng, 13, pp.128~ (1997)
- J.C. Knight, , Thin Solid Films, 193, pp.431~ (1990)
- E. Erturk, , Thin Solid Films, 153, pp.135~ (1987)
- A.T. Santhanam, "US Patent 5", 257~, pp.Patent (1993)
- E. Harju, , Surf. Coat. Technol, 85, pp.189~ (1996)
- A. Ramalho, "Proceedings of 6th international congress on tribology (EUROTRIB93)", Budapest(Hungary), 통권 : 3, pp.309~ (1993), Edited by Mihaly Kosma
- H.C. Choe, , Surf. Coat. Technol, 112, pp.299~ (1999)
- B. Berghaus, "German Patent DRP", 639~, pp.Patent (1932)
- J.A. Thornton, "Thin Film Processes", pp.75~ (1978), Academic Press
- H.C. Choe, , Materials Science Forum, 475, pp.2287~ (2005)
- D.A. Jones, "Principles and prevention of corrosion", pp.21~ (1992), Maxwell MacMillan International Ed
- D.M. Brunette, "Titanium in medicine", pp.320~ (2001), Springer
- M. Pourbaix, "Atlas of electrochemical equilibria in aqueous solutions", pp.193~ (1966), Pergamon Press