DC 스퍼터법과 유도결합 플라즈마 마그네트론 스퍼터법으로 증착된 CrN 코팅막의 물성 비교연구
A Comparative Study of CrN Coatings Deposited by DC and Inductively Coupled Plasma Magnetron Sputtering
0
조회
0
다운로드
9
인용
0
참고문헌
키워드
초록
Nanocrystalline CrN coatings were fabricated by DC and ICP (inductively coupled plasma) assisted magnetron sputtering techniques. The effect of ICP power, ranging from 0 to 500 W, on coating microstructure,preferred orientation mechanical properties were systematically investigated with HR-XRD, SEM, AFM and nanoindentation. The results show that ICP power has an significant influence on coating microstructure and mechanical properties of CrN coatings. With the increasing of ICP power, coating microstructure evolves from the columnar structure of DC process to a highly dense one. Grain size of CrN coatings were decreased from 11.7 nm to 6.6 nm with increase of ICP power. The maximum nanohardness of 23.0 GPa was obtained for the coatings deposited at ICP power of 500 W. Preferred orientation in CrN coatings also vary with ICP power, exerting an effective influence on film nanohardness.
Abstract
Nanocrystalline CrN coatings were fabricated by DC and ICP (inductively coupled plasma) assisted magnetron sputtering techniques. The effect of ICP power, ranging from 0 to 500 W, on coating microstructure,preferred orientation mechanical properties were systematically investigated with HR-XRD, SEM, AFM and nanoindentation. The results show that ICP power has an significant influence on coating microstructure and mechanical properties of CrN coatings. With the increasing of ICP power, coating microstructure evolves from the columnar structure of DC process to a highly dense one. Grain size of CrN coatings were decreased from 11.7 nm to 6.6 nm with increase of ICP power. The maximum nanohardness of 23.0 GPa was obtained for the coatings deposited at ICP power of 500 W. Preferred orientation in CrN coatings also vary with ICP power, exerting an effective influence on film nanohardness.
참고문헌 (16)
- T. Polcar, , Surf. Coat. Technol., 201, pp.5228~ (2007)
- P. H. Mayrhofer, , Surf. Coat. Technol., 146, pp.222~ (2001)
- L. Cunha, , Thin Solid Films, 355, pp.465~ (1999)
- Q. Kong, , Mater. Sci. Eng., B, 176, pp.850~ (2011)
- 백정호, "CrN 코팅구조에 따른 Polymer Electrode Membrane Fuel Cell 금속분리판의 부식특성 비교", 한국재료학회지, 20(4), pp.187~193 (2010), 한국재료학회
- 구범모, "유도결합 플라즈마(ICP) Sputtering에 의한 평판디스플레이(FPD)용 ITO 박막의 저온 증착", 한국표면공학회지, 37(3), pp.146~151 (2004), 한국표면공학회
- S. J. Jung, , Surf. Coat. Technol., 169, pp.363~ (2003)
- D. K. Lee, , Suf. Coat. Technol., 173, pp.1234~ (2003)
- I. Petrov, , J. Vac. Sci. Tech, A 21, pp.774~ (2003)
- 전성용, "DC 스퍼터법과 비대칭 바이폴라 펄스 DC 스퍼터법으로 증착된 TiN 코팅막의 물성 비교연구", 한국표면공학회지, 44(5), pp.179~184 (2011), 한국표면공학회
- N. Maazi, , J. Cryst. Growth, 243, pp.361~ (2002)
- C. Barret, "Structure of Metals", pp.204~ (1980), Pergamon
- S. Tan, , Thin Solid Films, 519, pp.2116~ (2011)
- C. W. Zou, , Vacuum, 83, pp.1086~ (2009)
- I. Petrov, , Thin Solid Films, 169, pp.299~ (1989)
- G. R. Lee, , Surf. Coat. Tech., 201, pp.5207~ (2007)