RF 마그네트론 스퍼터링법으로 상온 증착된 비정질 ITZO 산화물의 전기적 및 광학적 특성
Electrical and Optical Properties of Amorphous ITZO Deposited at Room Temperature by RF Magnetron Sputtering
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The electrical and optical properties of amorphous In-Tin-Zinc-Oxide(ITZO) deposited at room temperatureusing rf-magnetron sputtering were investigated. The amorphous ITZO thin films were obtained at the composition of In:Sn:Zn = 6:2:2, 4:3:3, and 2:4:4, but the ITZO (8:1:1) showed a crystalline phase of bixbyite structure of In2O3. The resistivity of ITZO could be controlled by oxygen pressure in the sputtering ambient. The resistivity of post-annealed ITZO thin films exhibited the dependence on the amount of Indium. Optical energy band gap and transmittance increased as the amount of indium in ITZO increased. For the device application with ITZO, the bottom-gated thin-film transistor using ITZO as a active channel layer was fabricated. It showed a threshold voltage of 1.42V and an on/off ratio of 5.63×107 operated with saturation field-effect mobility of 14.2 cm2/V·s.
Abstract
The electrical and optical properties of amorphous In-Tin-Zinc-Oxide(ITZO) deposited at room temperatureusing rf-magnetron sputtering were investigated. The amorphous ITZO thin films were obtained at the composition of In:Sn:Zn = 6:2:2, 4:3:3, and 2:4:4, but the ITZO (8:1:1) showed a crystalline phase of bixbyite structure of In2O3. The resistivity of ITZO could be controlled by oxygen pressure in the sputtering ambient. The resistivity of post-annealed ITZO thin films exhibited the dependence on the amount of Indium. Optical energy band gap and transmittance increased as the amount of indium in ITZO increased. For the device application with ITZO, the bottom-gated thin-film transistor using ITZO as a active channel layer was fabricated. It showed a threshold voltage of 1.42V and an on/off ratio of 5.63×107 operated with saturation field-effect mobility of 14.2 cm2/V·s.
참고문헌 (14)
- K. Nomura, , Nature, 432, pp.488~ (2004)
- T. Kamiya, , Sci. Technol. Adv. Mater, 11, pp.044305~ (2010)
- K. Ebata, , Appl. Phys Express, 5, pp.011102~ (2012)
- J. S. Seo, , ACS Appl. Mater. Interfaces, 6(17), pp.15335~ (2014)
- D. P. Heineck, , IEEE Electron Device Lett, 30, pp.514~ (2009)
- K. C. Lee, , J. Vac. Sci. Technol., B, 29, pp.021008~ (2011)
- S. Y. Sung, , Appl. Phys. Lett, 96, pp.102107~ (2010)
- Y. H. Kim, , Nature, 489, pp.128~ (2012)
- 정태동, "High Temperature Durability Amorphous ITO:Yb Films Deposited by Magnetron Co-Sputtering", 한국표면공학회지, 45(6), pp.242~247 (2012), 한국표면공학회
- L. Raniero, , Thin Solid Films, 511-512, pp.295~ (2006)
- C. A. Hoel, , Chem. Mater, 22, pp.3569~ (2010)
- T. Kamiya, , J. Disp. Technol, 5, pp.237~ (2009)
- H. Q. Chiang, , J. Vac. Sci. Techol. B, 24, pp.2702~ (2006)
- K. Nomura, , Jpn. J. Appl. Phys, 45, pp.4303~ (2006)