ZnO/Ti/ZnO 박막의 결정성 및 전기광학적 완성도 개선 연구
Enhancements of Crystallization and Opto-Electrical performance of ZnO/Ti/ZnO Thin Films
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Transparent ZnO (100 nm thick) and ZnO/Ti/ZnO (ZTZ) films were prepared with radio frequency (RF) and direct current (DC) magnetron sputtering on the glass substrate at room temperature. During the ZTZ film deposition, the thickness of the Ti interlayer was varied, such as 6, 9, 12, and 15 nm, while the thickness of ZnO films was kept at 50 nm to investigate the effect of the Ti interlayer on the crystallization and opto-electrical performance of the films. From the XRD pattern, it is concluded that the 9 nm thick Ti interlayer showed some characteristic peaks of Ti (200) and (220), and the grain size of the ZnO (002) enlarged from 13.32 to 15.28 nm as Ti interlayer thickness increased. In an opto-electrical performance observation, ZnO single-layer films show a figure of merit of 1.4×10-11 Ω-1, while ZTZ films with a 9 nm-thick Ti interlayer show a higher figure of merit of 2.0×10-5 Ω-1.
Abstract
Transparent ZnO (100 nm thick) and ZnO/Ti/ZnO (ZTZ) films were prepared with radio frequency (RF) and direct current (DC) magnetron sputtering on the glass substrate at room temperature. During the ZTZ film deposition, the thickness of the Ti interlayer was varied, such as 6, 9, 12, and 15 nm, while the thickness of ZnO films was kept at 50 nm to investigate the effect of the Ti interlayer on the crystallization and opto-electrical performance of the films. From the XRD pattern, it is concluded that the 9 nm thick Ti interlayer showed some characteristic peaks of Ti (200) and (220), and the grain size of the ZnO (002) enlarged from 13.32 to 15.28 nm as Ti interlayer thickness increased. In an opto-electrical performance observation, ZnO single-layer films show a figure of merit of 1.4×10-11 Ω-1, while ZTZ films with a 9 nm-thick Ti interlayer show a higher figure of merit of 2.0×10-5 Ω-1.
참고문헌 (11)
- M. Yahya, "The effects of argon plasma treatment on ITO properties and the performance of OLED devices", Optical Mater, 120, pp.111400~ (2021)
- D. Kim, "Improved electrical and optical properties of GZO films with a thin TiO2buffer layer deposited by RF magnetron sputtering", Ceram. Inter, 40, pp.1457~1460 (2014)
- 최수현, "전자빔 조사 에너지에 따른 TIO", Ag, 한국생산제조학회지, pp.2021, 30(5)[DOI]
- 최수현, "Ag 중간층 두께에 따른 Ti-doped In2O3", Ag, 대한금속·재료학회지, pp.2021, 59(8)[DOI]
- W. Zhao, "A study on Ti-doped ZnO transparent conducting thin films fabricatedby pulsed laser deposition", Appl. Surf. Sci, 305, pp.481~486 (2014)
- 박윤제, "Au 층간박막 두께에 따른 ZnO 박막의 전기광학적 특성 변화", 한국표면공학회지, 53(3), pp.104~108 (2020), 한국표면공학회
- B. D. Cullity, "Elements of X-ray diffraction" (1978), Addison-Wesley Pub. Co.
- Y. S. Kim, "ITO", Au, Appl. Surf. Sci, pp.2007, 254[DOI]
- S. Peng, "Influences of the RF power ratio on the optical and electrical properties of GZO thin films by DC coupled RF magnetron sputtering at room temperature", Physica B, 503, pp.111~116 (2016)
- J. Tauc, "Amorphous and liquid semiconductor" (1974), Plenum
- 송영환, "급속열처리에 따른 ZTO", Ag, 열처리공학회지, pp.2017, 30(4)[DOI]