반복회전운동에서 코발트크롬합금과 미끄럼접촉하는 돼지무릎관절연골의 접촉압력이 마찰계수변화에 미치는 영향
Effect of Contact Pressure on the Variations in Coefficients of Friction Between Porcine Knee Joint Cartilage and Co-Cr Alloy in a Repeat Pass Sliding Motion
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, the influence of contact pressure on the variation in coefficients of friction between porcine knee joint cartilage and Co-Cr alloy in a repeat pass sliding motion was investigated. Flat-ended cartilage pin specimens(9 mm diameter, 8 mm long) were prepared from porcine(6 months old) knee joints by a drill-type punch. Friction tests were conducted by using a pin-on-disk type friction tester for an hour in PBS lubricated condition under the contact pressures of 0.5, 1 and 2 MPa with 50 mm distance per a cycle at ambient condition. As a result, coefficients of friction increased as the test duration increased for all contact pressures. The maximum coefficients of friction were 0.082, 0.06 and 0.098 for 0.5, 1, and 2 MPa, respectively. It showed that coefficients of friction of porcine knee joint cartilage against Co-Cr alloy depended on the level of contact pressure and related to squeeze film lubrication mechanism.
Abstract
In this study, the influence of contact pressure on the variation in coefficients of friction between porcine knee joint cartilage and Co-Cr alloy in a repeat pass sliding motion was investigated. Flat-ended cartilage pin specimens(9 mm diameter, 8 mm long) were prepared from porcine(6 months old) knee joints by a drill-type punch. Friction tests were conducted by using a pin-on-disk type friction tester for an hour in PBS lubricated condition under the contact pressures of 0.5, 1 and 2 MPa with 50 mm distance per a cycle at ambient condition. As a result, coefficients of friction increased as the test duration increased for all contact pressures. The maximum coefficients of friction were 0.082, 0.06 and 0.098 for 0.5, 1, and 2 MPa, respectively. It showed that coefficients of friction of porcine knee joint cartilage against Co-Cr alloy depended on the level of contact pressure and related to squeeze film lubrication mechanism.
참고문헌 (12)
- 고정식, "조직학, 제4판" (2000), 고문사
- 강종호, "고정이 관절연골에 미치는 영향에 대한 연구", 대한물리치료학회지, 16(2), pp.1~16 (2004), 대한물리치료학회
- Nordin, M, "Biomechanics of Articular Cartilage, Basic Biomechanics of the Musculoskeletal System, 3rd" (2001), Lippincott Williams & Wilkins
- 박성훈, "활액과 하이얼루러난이 소 연골의 마찰 특성에 작용하는 역할", 한국정밀공학회지, 25(10), pp.137~143 (2008), 한국정밀공학회
- Fukubayashi, T, "The Contact Area and Pressure Distribution Pattern of the Knee. A Study of Normal and Osteoarthrotic Knee Joint", Acta Orthop Scand, 51(6), pp.871~879 (1980)
- "1991", 205(2)
- "1996", 210
- Northwood, E, "Investigation of the Frection and Surface Degradation of Innovative Chondroplasty Materials Against Articular Cartilage", Proc ImechE Part H: J. Engineering in Medicine, 221, pp.263~279 (2007)
- Zhang, J. L, "Friction of Articular Cartilage UnderDifferent Pressures and Sliding Velocities", J. of Biomechanics, 41(S1) (2008)
- Russell, S, "Investigation of Friction Values of Cartilage Substitution Biomaterials", J. of Biomechanics, 41(S1) (2008)
- "1998", 212
- 이권용, "토끼 관절연골의 마찰 및 윤활 특성", J. of the KSTLE, 17(4), pp.307~311 (2001)