고주파 연소합성 코팅된 Ni-Al계 금속간화합물의 미끄럼마모 특성에 미치는 볼 밀링의 영향
Effects of Ball Milling on Sliding Wear Behavior of Ni-Al Intermetallics Coated on Mild Steel through Induction Heating Process
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Ball-milling for reactant powders in advance and using an induction heating system for Ni-Al intermetallic coating process are known to enhance the reactivity of combustion synthesis. In this work, the effects of the charging weight ratio of ball to powder in ball-milling for reactant Ni-Al powders and the synthesizing temperature in induction heating on sliding wear behavior of the coating layers are investigated. Sliding wear behavior of the coating layers is examined against a tool steel using a pin-on-disc type sliding wear machine. As results, wear of the coating layer ball-milled without ball was severely worn out at the sliding speed of 2m/ s, regardless of the synthesizing temperature in induction heating. However, the wear rate of the coating layers at the sliding speed was remarkably decreased with increasing the charging weight ratio of ball in ball-milling for reactant powders. This can be explained by the fact that the void in the coating layer is disappeared and the coating layer is densified by the ball-milling. The evidence showed that pitting damages were disappeared on the worn surface of ball-milled coating layer. Consequentially, the Ni-Al intermetallic coating layer could have better wear resistance at all sliding speed ranges with the ball-milling for reactant powders in advance.
Abstract
Ball-milling for reactant powders in advance and using an induction heating system for Ni-Al intermetallic coating process are known to enhance the reactivity of combustion synthesis. In this work, the effects of the charging weight ratio of ball to powder in ball-milling for reactant Ni-Al powders and the synthesizing temperature in induction heating on sliding wear behavior of the coating layers are investigated. Sliding wear behavior of the coating layers is examined against a tool steel using a pin-on-disc type sliding wear machine. As results, wear of the coating layer ball-milled without ball was severely worn out at the sliding speed of 2m/ s, regardless of the synthesizing temperature in induction heating. However, the wear rate of the coating layers at the sliding speed was remarkably decreased with increasing the charging weight ratio of ball in ball-milling for reactant powders. This can be explained by the fact that the void in the coating layer is disappeared and the coating layer is densified by the ball-milling. The evidence showed that pitting damages were disappeared on the worn surface of ball-milled coating layer. Consequentially, the Ni-Al intermetallic coating layer could have better wear resistance at all sliding speed ranges with the ball-milling for reactant powders in advance.
참고문헌 (16)
- Materials Sci. Soc. of JPN, "Intermetallic compounds for materials", pp.88~ (1995), Shokabo
- Morsi, K., "Reaction synthesis processing of Ni-Al intermetallic materials", Mater. Sci. Eng., (A299), pp.1~15 (2001)
- Salehi, M., "Formation of TiNi intermetallic coatings on carbon tool steel by a duplex process", Surf. Coat. Tech, 148, pp.55~60 (2000)
- 이한영, "저온 연소합성 후 확산 열처리한 Ni3Al 금속간화합물 코팅층의 미끄럼 마모거동", 한국트라이볼로지학회지, 25(1), pp.7~12 (2009), 한국트라이볼로지학회
- Lee, H. -Y., "Sliding wear properties for Ni-Al based intermetallic compound layer coated on ductile cast iron by combustion synthesis", Wear, 260, pp.83~89 (2006)
- Okamoto, A., "Effects of silicon addition on NickelAluminide surface coatings through combustion synthesis", J. Jpn. Found. Soc, 77, pp.744~751 (2005)
- Kimata, T., "Enhanced densification of combustion synthesized Ni-Al intermetallic compound by Si addition", Intermetallics, 11, pp.947~952 (2003)
- 이한영, "고주파 유도가열을 통한 알루미늄 기판재위 Ni-Al계 금속간화합물의 연소합성코팅에 관한 연구", 한국트라이볼로지학회지, 28(2), pp.56~61 (2012), 한국트라이볼로지학회[DOI]
- Zhan, Z., "Low-temperature processing of Fe-Al intermetallic coatings assisted by ball milling", Intermetallics, 14, pp.7581~ (2006)
- 이한영, "Application of Ball-Milled Powder Mixture to Intermetallics Coating Through Reaction Synthesis", Metals and Materials International, 19(6), pp.1289~1293 (2013), 대한금속·재료학회[DOI]
- 이한영, "주철의 용탕열을 이용한 Ni-Al계 금속간화합물의 연소합성 코팅에 미치는 Ball Milling의 영향", 대한금속·재료학회지, 50(1), pp.28~33 (2012), 대한금속·재료학회
- Van Dyck, S., "Reactive powder metallurgy of Ni3Si-based alloys", Intermetallics, 3, pp.309~314 (1995)
- Lee, H. -Y., "The effects of induction heating rate on properties of Ni-Al based intermetallic compound layer coated on ductile cast iron by combustion synthesis", Intermetallics, 15, pp.1050~1055 (2007)
- 이한영, "Ni-Al계 금속간화합물 코팅에 미치는 고주파유도 가열 조건의 영향", 대한금속·재료학회지, 48(2), pp.141~147 (2010), 대한금속·재료학회
- Sanchez Bautista, C., "NiAl intermetallic coatings elaborated by solar assisted SHS process", Intermetallics, 14, pp.1270~1275 (2006)
- 이한영, "Ni-Al계 금속간화합물의 고주파 연소합성코팅에 미치는볼 밀링의 영향", 한국트라이볼로지학회지, 33(6), pp.296~302 (2017), 한국트라이볼로지학회[DOI]