고주파 유도가열을 통한 알루미늄 기판재위 Ni-Al계 금속간화합물의 연소합성코팅에 관한 연구
A Study for Ni-Al based Intermetallics Coating onto Aluminum Substrate by Induction Heating
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In order to investigate the possibility of Ni-Al based intermetallics coating onto aluminum substrate, the coating process for induction heating has been evaluated by microscopically analyzing the intermetallic layers coated at temperatures lower than the melting temperature of aluminum. The coating layers were divided into two parts with different microstructure along the depth. Hard NiAl3 layer was found at lower parts of the coatings near the interface with aluminum substrate. This layer was formed by the diffusion of aluminum atoms from the substrate into the coating layer across the interface during the induction heating. Meanwhile, at the upper parts of the coating near the surface, a large amount of un-reacted Ni was still remained and surrounded by several Ni-Al based intermetallic compounds, such as Ni3Al, NiAl and Ni2Al3 formed by the lattice diffusion.
Abstract
In order to investigate the possibility of Ni-Al based intermetallics coating onto aluminum substrate, the coating process for induction heating has been evaluated by microscopically analyzing the intermetallic layers coated at temperatures lower than the melting temperature of aluminum. The coating layers were divided into two parts with different microstructure along the depth. Hard NiAl3 layer was found at lower parts of the coatings near the interface with aluminum substrate. This layer was formed by the diffusion of aluminum atoms from the substrate into the coating layer across the interface during the induction heating. Meanwhile, at the upper parts of the coating near the surface, a large amount of un-reacted Ni was still remained and surrounded by several Ni-Al based intermetallic compounds, such as Ni3Al, NiAl and Ni2Al3 formed by the lattice diffusion.
참고문헌 (12)
- 日本材料科學會, "金屬間化合物と材料", pp.88~132 (1995), 裳華房
- T. Kimata, "Enhanced Densification of Combustion Synthesized Ni-Al Intermetallic Compound by Si Addition", Intermetallics, 11, pp.947~952 (2003)
- H.Y. Lee, "Sliding Wear Properties for Ni-Al Based Intermetallic Compound Layer Coated On Ductile Cast Iron by Combustion Synthesis", Wear, 260, pp.83~89 (2006)
- H.Y. Lee, "The effects of induction heating rate on properties of Ni-Al based intermetallic compound layer coated on ductile cast iron by combustion synthesis", INTERMETALLICS, 15, pp.1050~1056, ELSEVIER SCI LTD
- 이한영, "Ni-Al계 금속간화합물 코팅에 미치는 고주파유도 가열 조건의 영향", 대한금속·재료학회지, 48(2), pp.141~147 (2010), 대한금속·재료학회
- 이한영, "알루미늄 주물 위 용탕열을 이용한 Ni-Al계 금속간화합물의 연소합성 코팅", 한국주조공학회지, 31(2), pp.83~86 (2011), 한국주조공학회
- 이한영, "Cu-Al-Ni계 금속간화합물의 연소합성 Coating에 미치는 Ball Mill처리의 영향", 한국윤활학회지, 27(1), pp.1~6 (2011), 한국윤활학회
- T. Izumi, "Formation and Oxidation behavior of Ni2Al3 Coating on Heatresistant Ti-alloy", Intermetallics, 13, pp.615~619 (2005)
- 燃燒合成硏究會, "燃燒合成の化學", pp.45~ (1992), TIC
- 조용재, "어닐링처리한 Ni-50at%Al 압분체의 연소합성 거동", 대한금속·재료학회지, 49(10), pp.790~796 (2011), 대한금속·재료학회
- K.Morsi, "Reaction Synthesis Processing of Ni-Al Intermetallic Materials", Mat. Sci & Eng., A299, pp.1~15 (2001)
- 和泉 修, "金屬間化合物", pp.56~ (1990), 産業圖書