알루미늄 기판 위 반응합성 Coating 된 Ni-Al계금속간화합물의 미끄럼마모 특성 해석
Sliding Wear Properties of Ni-Al based Intermetallics Layer coated on Aluminum through Reaction Synthesis Process
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Ni–Al intermetallic coating technology is an available method for the strengthening of aluminum substrate. In this study, Ni–Al intermetallics were coated on an aluminum substrate through a reaction synthesis process at a temperature lower than melting point of aluminum. And the sliding wear properties of the coatings have been investigated to verify their usability and compared the wear properties with those of a cast Al-12.5%Si alloy and an anodizing layer on aluminum. Results show that the wear rate of the coating layer greatly increased at 1 m/s and 1.5 m/s when compared with that of the cast Al-12.5%Si alloy. Much pitting damages were observed on the worn surfaces at these sliding speeds, unlike at other sliding speeds. The wear of the intermetallic coating layer at these sliding speeds seems to be increased by pitting as a consequence of adhesion. In contrast, wear of the coating layer at other speeds hardly occurs, regardless of wear periods. Nevertheless, the wear properties of the intermetallic coating layer on the aluminum substrate through the reaction synthesis process are more stable than those of anodized aluminum and are superior to those of the cast Al-12.5%Si alloy in a steady-state wear period.
Abstract
Ni–Al intermetallic coating technology is an available method for the strengthening of aluminum substrate. In this study, Ni–Al intermetallics were coated on an aluminum substrate through a reaction synthesis process at a temperature lower than melting point of aluminum. And the sliding wear properties of the coatings have been investigated to verify their usability and compared the wear properties with those of a cast Al-12.5%Si alloy and an anodizing layer on aluminum. Results show that the wear rate of the coating layer greatly increased at 1 m/s and 1.5 m/s when compared with that of the cast Al-12.5%Si alloy. Much pitting damages were observed on the worn surfaces at these sliding speeds, unlike at other sliding speeds. The wear of the intermetallic coating layer at these sliding speeds seems to be increased by pitting as a consequence of adhesion. In contrast, wear of the coating layer at other speeds hardly occurs, regardless of wear periods. Nevertheless, the wear properties of the intermetallic coating layer on the aluminum substrate through the reaction synthesis process are more stable than those of anodized aluminum and are superior to those of the cast Al-12.5%Si alloy in a steady-state wear period.
참고문헌 (13)
- Akhlaghi, F., "Influence of graphite content on the dry sliding and oil impregnated sliding wear behavior of Al 2024-Grapgite composites produced by in situ powder metallurgy method", Wear, 266, pp.37~45 (2009)[DOI]
- Prasada Rao, A. K., "Microstructure and wear mechanism of grainrefined aluminum during dry sliding against steel disc", Wear, 264, pp.638~647 (2008)[DOI]
- Md. Aminul Islam, A. S. M. A. Haseeb, "A comparative wear steady on heat-treated aluminum-lithium alloy and pour aluminum", Mater. Sci. Eng., A268, pp.101~108 (1999)
- Korkut, M. H., "Microstucture and wear behavior of Al2024", SiFe and Al2024, <TEX>$Al_2O_3$<, pp.TEX> Composites, Tribology International[DOI]
- Liu, L., "Fiction and wear properties of short carbon fiber reinforced aluminum matrix composites", Wear, 266, pp.733~738 (2009)[DOI]
- Mandal, A., "Sliding wear behavior of T6 treated A356-TiB2 in-situ composites", Wear, 266, pp.865~872 (2009)[DOI]
- Kent R. Van Horn, "Aluminum Vol. I", pp.252~253 (1967), American Society for Metals
- Lee, H.-Y., "Sliding wear properties for Ni-Al based intermetallic compound layer coated on ductile cast iron by combustion synthesis", Wear, 260, pp.83~89 (2006)[DOI]
- Salehi, M., "Formation of TiNi Intermetallic coatings on carbon tool steel by a duplex process", Sur & Coat. Tech., 148, pp.55~60 (2001)[DOI]
- 이한영, "Ni-Al계 금속간화합물 코팅에 미치는 고주파유도 가열 조건의 영향", 대한금속·재료학회지, 48(2), pp.141~147 (2010), 대한금속·재료학회
- Izumi, T., "Formation and oxidation behavior of <TEX>$Ni_2Al_3$<", TEX> Coating on Heat-resistant Ti-Alloy, 2005, pp.12, 615~619
- 이한영, "Nickel Aluminides Coating on Aluminum Substrate Using a Reaction Synthesis Process", Metals and Materials International, 21(1), pp.147~152 (2015), 대한금속·재료학회[DOI]
- Lee, H.-Y., "Analysis of sliding wear mode on annealed steel by X-ray diffraction technique", Wear, 256, pp.657~663 (2004)[DOI]