연소합성 코팅된 NiAl 금속간화합물의 화학양론이 미끄럼 마모특성에 미치는 영향
Effects of Stoichiometry on Properties of NiAl Intermetallics coated on Carbon Steel through Combustion Synthesis
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effect of the stoichiometry on the sliding wear properties of NiAl coatings has been investigated. Three different powder mixtures with the compositions of Ni-50at%Al, Ni-54at%Al and Ni-42at%Al were diepressed respectively, and which were subsequently coated on mild steel through combustion synthesis in an induction heating system. Sliding wear behavior of the coatings was examined against an alloyed tool steel using a pin-on-disc type sliding wear test machine. As results, it could be seen that powder mixture(Ni-54at%Al) with displaying Al-rich deviations from the stoichiometry of NiAl(Ni-50at%Al) was promoted the most the synthetic reactivity. The microstructure of the coating layer with the compositions of Ni-54at%Al exhibits the porous NiAl single phase structure. However, the microstructure of the coating layer of the compositions of Ni-42at%Al exhibits the denser multi-phase structure containing several intermediate phases in addition to NiAl. Densification of the coating layer was enhanced by increasing the reacting temperature. On the other hand, the wear properties of the coating layers showed that the wear mode at speeds of around 1 m/s was severe wear, regardless of the stoichiometry and reacting temperature. However, wear properties of coating layer with the compositions of Ni-42at%Al were superior to those of coating layer with the compositions of Ni-54at%Al. This would be attributed by the fact that coating layer with the compositions of Ni-42at%Al develops little void and much intermediate phases with high strength.
Abstract
The effect of the stoichiometry on the sliding wear properties of NiAl coatings has been investigated. Three different powder mixtures with the compositions of Ni-50at%Al, Ni-54at%Al and Ni-42at%Al were diepressed respectively, and which were subsequently coated on mild steel through combustion synthesis in an induction heating system. Sliding wear behavior of the coatings was examined against an alloyed tool steel using a pin-on-disc type sliding wear test machine. As results, it could be seen that powder mixture(Ni-54at%Al) with displaying Al-rich deviations from the stoichiometry of NiAl(Ni-50at%Al) was promoted the most the synthetic reactivity. The microstructure of the coating layer with the compositions of Ni-54at%Al exhibits the porous NiAl single phase structure. However, the microstructure of the coating layer of the compositions of Ni-42at%Al exhibits the denser multi-phase structure containing several intermediate phases in addition to NiAl. Densification of the coating layer was enhanced by increasing the reacting temperature. On the other hand, the wear properties of the coating layers showed that the wear mode at speeds of around 1 m/s was severe wear, regardless of the stoichiometry and reacting temperature. However, wear properties of coating layer with the compositions of Ni-42at%Al were superior to those of coating layer with the compositions of Ni-54at%Al. This would be attributed by the fact that coating layer with the compositions of Ni-42at%Al develops little void and much intermediate phases with high strength.
참고문헌 (18)
- Materials Sci. Soc. of JPN, "Intermetallic compounds for materials", pp.88~ (1995), Shokabo
- Morsi, K., "Reaction synthesis processing of Ni-Al intermetallic materials", Mater. Sci. Eng, (A299), pp.1~15 (2001)
- Aoki, K., "Improvement in room temperature ductility of the LI2 type intermetallic compound Ni3Al by boron addition", J. Japan Inst. Metals, 43, pp.1190~1196 (1979)
- Liu, C. T., "Nickel aluminides for structural use : Metals, Reaction synthesis processing of Ni-Al intermetallic materials", J. of Metals, 38, pp.19~ (1986)
- 이한영, "Application of Ball-Milled Powder Mixture to Intermetallics Coating Through Reaction Synthesis", Metals and Materials International, 19(6), pp.1289~1293 (2013), 대한금속·재료학회[DOI]
- 이한영, "알루미늄 주물의 용탕열을 이용한 Ni-Al계 금속간화합물의 연소합성 코팅에 미치는 Ball-Milling의 영향", 대한금속·재료학회지, 52(2), pp.123~128 (2014), 대한금속·재료학회[DOI]
- 이한영, "Nickel Aluminides Coating on Aluminum Substrate Using a Reaction Synthesis Process", Metals and Materials International, 21(1), pp.147~152 (2015), 대한금속·재료학회[DOI]
- 이한영, "Ni-Al계 금속간화합물의 고주파 연소합성코팅에 미치는볼 밀링의 영향", 한국트라이볼로지학회지, 33(6), pp.296~302 (2017), 한국트라이볼로지학회[DOI]
- 이한영, "고주파 연소합성 코팅된 Ni-Al계 금속간화합물의 미끄럼마모 특성에 미치는 볼 밀링의 영향", 한국트라이볼로지학회지, 34(6), pp.284~291 (2018), 한국트라이볼로지학회[DOI]
- 이한영, "알루미늄 기판 위 반응합성 Coating 된 Ni-Al계금속간화합물의 미끄럼마모 특성 해석", 한국트라이볼로지학회지, 34(2), pp.67~73 (2018), 한국트라이볼로지학회[DOI]
- Lee, H. -Y., "Sliding wear properties for Ni-Al based intermetallic compound layer coated on ductile cast iron by combustion synthesis", Wear, 260, pp.83~89 (2006)
- Yamaguchi, M., "Introduction to intermetallic compounds", pp.61~ (2004), Uchida Rokakuho
- Westbrook, J. H., "Structural Applications of Intermetallic Compounds" (1995), John Wiley & Sons Ltd
- Westbrook, J. H., "Intermetallic Compounds" (1995), John Wiley & Sons Ltd
- Lee, H. -Y., "Analysis of sliding wear mode on annealed steel by X-ray diffraction technique", Wear, 256, pp.657~663 (2003)
- 조용재, "어닐링처리한 Ni-50at%Al 압분체의 연소합성 거동", 대한금속·재료학회지, 49(10), pp.790~796 (2011), 대한금속·재료학회
- Research Group for Combusion Synthesis, "Chemistry of Combusion synthesis", pp.45~ (1992), TIC bookCo
- Smith, W. F., "Foundations of Materials Science and Engineering", pp.640~ (2005), McGraw-Hill Korea Inc