Crystal growth and optical properties with preheating temperature of solgel derived ZnO thin films
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
We try to use isopropanol which has low boiling point to prepare ZnO thin films at low temperature. ZnO thin films were prepared by sol-gel spin-coating method using zinc acetate dehydrate-isopropanol-monoethanolamine (MEA) solution. The c-axis preferred orientation and optical properties of ZnO films with preheating temperature have been investigated. ZnO thin films were preheated at 200 to 300oC with an interval of 25oC and post-heated at 650oC. The ZnO film preheated at 275oC and post-heated at 650oC was highly oriented along c-axis (002) plane, and the surface with homogeneous and dense microstructures was formed having nano-sized grains. The optical transmittance was above 90 % in the visible range and exhibited absorption edges at 368 nm wavelength.
Abstract
We try to use isopropanol which has low boiling point to prepare ZnO thin films at low temperature. ZnO thin films were prepared by sol-gel spin-coating method using zinc acetate dehydrate-isopropanol-monoethanolamine (MEA) solution. The c-axis preferred orientation and optical properties of ZnO films with preheating temperature have been investigated. ZnO thin films were preheated at 200 to 300oC with an interval of 25oC and post-heated at 650oC. The ZnO film preheated at 275oC and post-heated at 650oC was highly oriented along c-axis (002) plane, and the surface with homogeneous and dense microstructures was formed having nano-sized grains. The optical transmittance was above 90 % in the visible range and exhibited absorption edges at 368 nm wavelength.
참고문헌 (17)
- "Transpar-ent and highly conductive films of ZnO prepared by rfreactive magnetron sputtering", pp.640~ (1981)
- "High rate planar magnetron deposition of trans-parent and heat reflecting films on glasand plastic", pp.352~ (1983)
- "Aluminium content dependence of milkytransparent conducting ZnO Al films with textured sur-face prepared by d.c. magnetron sputering", pp.86~ (1994)
- J.A. Aranovich,
- "Electrical and opticalproperties of ZnO transparent conducting films by thesol-gel method,", 247, pp.119~ (2003)
- "Preparation and character-ization of Al-doped ZnO transparent conducting thinfilm by sol-gel processing", 33, pp.149~ (1996)
- "Crystallizationbehavior and origin of c-axis orientation in sol-gel-derived ZnO Li thin films on glass substrate", 180, pp.341~ (2001)
- "JCPDS-International Centre for Difraction Data", pp.05~0664
- "Characterizationof ZnO thin films deposited onto Al", Si substrates by r.f.magnetron sputtering, 1997, pp.302, 116~
- "Epitaxial growth of Al-doped ZnO thin films grown bypulsed laser deposition", pp.107~ (2002)
- "?Sol-gel prepara-tion of ZnO films with extremely preferred orientationalong (002)plane from zinc acetate solution", 78, pp.78~ (1997)
- "Textured aluminum-dopedZnO thin films from atmospheric pressure chemical-vapor deposition", pp.880~ (1992)
- "Zinc oxide films preparedby sol-gel spin-coating,", 372, pp.30~ (2000)
- "X-ray photoelectron spectroscopy andauger electron spectroscopy studies of Al-doped ZnOfilms,", 158, pp.134~ (2000)
- "Depositionof highly oriented ZnO films by spray pyrolysis andtheir structrual, optical and electrical characterization", 57, pp.573~ (2002)
- "Suherties of zinc oxide films post-annealed in H2 after fabri-cation by sol-gel process", 78, pp.170~ (2002)
- "Electronic processes in non-crystalline materials"