양극산화 시간 및 전류밀도 변화에 따른 다공질 실리콘의 특성 변화
Effects of Current Density and Anodization Time on the Properties of Porous Si
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The PS(porous Si) were fabricated with different anodization time and current density. The structural and optical properties of PS were investigated by SEM(scanning electron microscopy), AFM(atomic force microscopy), and PL(photoluminescence). It is found that the pore size and surface roughness of PS are proportional to the current density. The PL spectra show that the PL peak position is red-shifted with increasing anodization time. This behavior corresponds to the change of pore size which is consistent with the quantum confinement model. The FWHM(full width at half maximum) of PL peak is decreased from 97 to 51 nm and the PL peak position is blue-shifted with increasing current density up to 10 mA/cm2. The PL peak intensity of the PS fabricated under 1 mA/cm2 is the highest among samples.
Abstract
The PS(porous Si) were fabricated with different anodization time and current density. The structural and optical properties of PS were investigated by SEM(scanning electron microscopy), AFM(atomic force microscopy), and PL(photoluminescence). It is found that the pore size and surface roughness of PS are proportional to the current density. The PL spectra show that the PL peak position is red-shifted with increasing anodization time. This behavior corresponds to the change of pore size which is consistent with the quantum confinement model. The FWHM(full width at half maximum) of PL peak is decreased from 97 to 51 nm and the PL peak position is blue-shifted with increasing current density up to 10 mA/cm2. The PL peak intensity of the PS fabricated under 1 mA/cm2 is the highest among samples.
참고문헌 (16)
- A. Uhlir, , The Bell System Technical Journal, 35, pp.333~ (1956)
- D. R. Turner, , J. Electrochem. Soc., 105, pp.402~ (1958)
- L. T. Canham, , Appl. Phys. Lett., 57, pp.1046~ (1990)
- S. H. Jang, , Mater. Lett., 62, pp.552~ (2008)
- G. Lammel, , Sens. Actuator A-Phys., 92, pp.52~ (2001)
- B. Ünal, , J. Porous Mat., 7, pp.295~ (2000)
- W. T. Hsieh, , Electron. Lett., 36, pp.1869~ (2000)
- D.C. Chang, , J. Porous Mat., 7, pp.349~ (2000)
- S. H. D. Milani, , J. Optoelectron. Adv. M., 8, pp.1216~ (2006)
- T. Nakagawa, , Jpn. J. Appl. Phys., 37, pp.7186~ (1998)
- N. Happo, , Jpn. J. Appl. Phys., 37, pp.3951~ (1998)
- G. Ledoux, , Phys. Rev. B, 62, pp.15942~ (2000)
- T. I. Gorbanyuk, , Thin Solid Films, 495, pp.134~ (2006)
- C. Tsai, , Appl. Phys. Lett., 60, pp.1700~ (1992)
- 박현아, "n-type과 p-type 다공성 실리콘의 구조와 광학적 특성에 관한 연구", 한국진공학회지, 12(4), pp.257~262 (2003), 한국진공학회
- M. Ohmukai, , Jpn. J. Appl. Phys., 36, pp.L292~ (1997)