Effect of light-curing, pressure, oxygen inhibition, and heat on shear bond strength between bis-acryl provisional restoration and bis-acryl repair materials
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. This study aimed to discover a way to increase the bond strength between bis-acryl resins, using a comparison of the shear bond strengths attained from bis-acryl resins treated with light curing, pressure, oxygen inhibition, and heat. MATERIALS AND METHODS. Self-cured bis-acryl resin was used as both a base material and as a repair material. Seventy specimens were distributed into seven groups according to treatment methods: pressure - stored in a pressure cooker at 0.2 Mpa; oxygen inhibition- applied an oxygen inhibitor around the repaired material,; heat treatment - performed heat treatment in a dry oven at 60C, 100C, or 140C. The shear bond strength was measured with a universal testing machine, and the shear bond strength (MPa) was calculated from the peak load of failure. A comparison of the bond strength between the repaired specimens was conducted using one-way ANOVA and Tukey multiple comparison tests (α=.05). RESULTS. There were no statistically significant differences in the shear bond strength between the control group and the light curing, pressure, and oxygen inhibition groups. However, the heat treatment groups showed statistically higher bond strengths than the groups treated without heat, and the groups treated at a higher temperature resulted in higher bond strengths. Statistically significant differences were seen between groups after different degrees of heat treatment, except in groups heated at 100C and 140C. CONCLUSION. Strong bonding can be achieved between a bis-acryl base and bis-acryl repair material after heat treatment.
Abstract
PURPOSE. This study aimed to discover a way to increase the bond strength between bis-acryl resins, using a comparison of the shear bond strengths attained from bis-acryl resins treated with light curing, pressure, oxygen inhibition, and heat. MATERIALS AND METHODS. Self-cured bis-acryl resin was used as both a base material and as a repair material. Seventy specimens were distributed into seven groups according to treatment methods: pressure - stored in a pressure cooker at 0.2 Mpa; oxygen inhibition- applied an oxygen inhibitor around the repaired material,; heat treatment - performed heat treatment in a dry oven at 60C, 100C, or 140C. The shear bond strength was measured with a universal testing machine, and the shear bond strength (MPa) was calculated from the peak load of failure. A comparison of the bond strength between the repaired specimens was conducted using one-way ANOVA and Tukey multiple comparison tests (α=.05). RESULTS. There were no statistically significant differences in the shear bond strength between the control group and the light curing, pressure, and oxygen inhibition groups. However, the heat treatment groups showed statistically higher bond strengths than the groups treated without heat, and the groups treated at a higher temperature resulted in higher bond strengths. Statistically significant differences were seen between groups after different degrees of heat treatment, except in groups heated at 100C and 140C. CONCLUSION. Strong bonding can be achieved between a bis-acryl base and bis-acryl repair material after heat treatment.
참고문헌 (16)
- Davies JE, "Mechanisms of endosseous integration", Int J Prosthodont, 11, pp.391~401 (1998)
- Romanos GE, "Bone quality and the immediate loading of implants-critical aspects based on literature, research, and clinical experience", Implant Dent, 18, pp.203~209 (2009)
- Bahat O, "Parameters for successful implant integration revisited part I: immediate loading considered in light of the original prerequisites for osseointegration", Clin Implant Dent Relat Res, 12, pp.e2~e12 (2010)
- Turkyilmaz I, "Determination of bone quality of 372 implant recipient sites using Hounsfield unit from computerized tomography: a clinical study", Clin Implant Dent Relat Res, 10, pp.238~244 (2008)
- Shapurian T, "Quantitative evaluation of bone density using the Hounsfield index", Int J Oral Maxillofac Implants, 21, pp.290~297 (2006)
- Turkyilmaz I, "Bone density assessments of oral implant sites using computerized tomography", J Oral Rehabil, 34, pp.267~272 (2007)
- Valiyaparambil JV, "Bone quality evaluation: comparison of cone beam computed tomography and subjective surgical assessment", nt J Oral Maxillofac Implants, 27, pp.1271~1277 (2012)
- Mah P, "Deriving Hounsfield units using grey levels in cone beam computed tomography", Dentomaxillofac Radiol, 39, pp.323~335 (2010)
- Nomura Y, "Reliability of voxel values from cone-beam computed tomography for dental use in evaluating bone mineral density", Clin Oral Implants Res, 21, pp.558~562 (2010)
- Lekholm U, "Tissueintegrated prostheses: osseointegration in clinical dentistry", pp.199~209 (1985), Quintessence
- Misch CE, "Contemporary Implant Dentistry", pp.645~667 (2008), CV Mosby
- Trisi P, "Bone classification: clinical-histomorphometric comparison", Clin Oral Implants Res, 10, pp.1~7 (1999)
- Iezzi G, "Correlation between the bone density recorded by a computerized implant motor and by a histomorphometric analysis: a preliminary in vitro study on bovine ribs", Clin Implant Dent Relat Res, 17, pp.e35~e44 (2015)
- Di Stefano DA, "A possible novel objective intraoperative measurement of maxillary bone density", Minerva Stomatol, 62, pp.259~265 (2013)
- Ekfeldt A, "A retrospective analysis of factors associated with multiple implant failures in maxillae", Clin Oral Implants Res, 12, pp.462~467 (2001)
- Javed F, "The role of primary stability for successful immediate loading of dental implants. A literature review", J Dent, 38, pp.612~620 (2010)