The ferroelectric properties of Ce-doped PZT/BFO multilayer thin films prepared using the sol-gel method
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
In this study, Ce-doped PZT/BFO multilayer thin films were prepared by the spin-coating method on Pt(200 nm)/Ti(10 nm)/SiO2(100 nm)/P-Si(100) substrates using Bi0.9Ce0.1FeO3 and Pb(Zr0.52Ti0.48)O3 metal alkoxide solutions. The coating and heatingprocedure was repeated several times to form multilayer thin films. All PZT/BCFO multilayer thin films display the typicalXRD pattern of a polycrystalline perovskite structure with a uniform, void-free grain microstructure. The thickness of the PZTand BCFO film after one cycle of drying/sintering was approximately 30 nm, and all films consist of fine grains with arelatively flat surface morphology. The relative dielectric constant and dielectric losses of the six-coated PZT/BCFO thin filmwere approximately 360 and 0.003%, respectively. As the number of coatings increased, the remanent polarization andcoercive field increased. The values for the six-coated PZT/BCFO thin film were 17.6 µC/cm2and 53 kV/cm, respectively
Abstract
In this study, Ce-doped PZT/BFO multilayer thin films were prepared by the spin-coating method on Pt(200 nm)/Ti(10 nm)/SiO2(100 nm)/P-Si(100) substrates using Bi0.9Ce0.1FeO3 and Pb(Zr0.52Ti0.48)O3 metal alkoxide solutions. The coating and heatingprocedure was repeated several times to form multilayer thin films. All PZT/BCFO multilayer thin films display the typicalXRD pattern of a polycrystalline perovskite structure with a uniform, void-free grain microstructure. The thickness of the PZTand BCFO film after one cycle of drying/sintering was approximately 30 nm, and all films consist of fine grains with arelatively flat surface morphology. The relative dielectric constant and dielectric losses of the six-coated PZT/BCFO thin filmwere approximately 360 and 0.003%, respectively. As the number of coatings increased, the remanent polarization andcoercive field increased. The values for the six-coated PZT/BCFO thin film were 17.6 µC/cm2and 53 kV/cm, respectively
참고문헌 (12)
- M. Fiebig, , Nature Reviews Materials, 1, pp.16046~ (2016)
- L.W. Martin, , Dalton Transactions, 39, pp.10813~10826 (2010)
- W. Eerenstein, , Nature, 442, pp.759~765 (2006)
- H. Liu, , J. phys. D : Appl. Phys, 41, pp.095302~ (2008)
- S. Yakovlev, , Thin Solid Films, 493, pp.24~29 (2005)
- L. Chen, , Thin Solid Films, 518, pp.1637~1640 (2010)
- J.H. Kim, , Jpn. J. Appl. Phys, 48, pp.09KB02~ (2009)
- Y. Hamazaki, , Jpn. J. Appl. Phys, 48, pp.09KA08~ (2009)
- T. Kawae, , Appl. Phys. Lett, 94, pp.112904~ (2009)
- T. Ozaki, , Jpn. J. Appl. Phys, 4, pp.09KC07~ (2009)
- S.K. Singh, , J. Appl. Phys, 102, pp.094109~ (2007)
- S.H. Jo, , Nanoscale Res. Lett, 7, pp.54~58 (2012)