해수 환경에서 Al5083-H321 알루미늄 합금의 침식부식 손상에 미치는 유속의 영향과 손상 메카니즘
Effect of Flow Rate on Erosion Corrosion Damage and Damage Mechanism of Al5083-H321 Aluminum Alloy in Seawater Environment
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
In this study, erosion tests and erosion-corrosion tests of Al5083-H321 aluminum alloy were conductedat various flow rates in seawater. The erosion tests were conducted at a flow rate of 0 to 20 m/s, anderosion-corrosion tests were performed by potentiodynamic polarization method at the same flow rate. Characteristic evaluation after the erosion test was conducted by surface analysis. Characteristic evaluation after the erosion-corrosion test was performed by Tafel extrapolation and surface analysis. The results of the surface analysis after the erosion test showed that surface damage tended to increase as the flow rate increased. In particular, intermetallic particles were separated due to the breakdown of the oxide film at 10 m/s or more. In the erosion-corrosion test, the corrosion current density increased as the flow rate increased. Additionally, the surface analysis showed that surface damage occurred in a vortex shape and the width of the surface damage tended to increase as the flow rate increased. Moreover, damage at 0 m/s, proceeded in a depth direction due to the growth of pitting corrosion, and the damaged area tended to increase due to acceleration of the intermetallic particle loss by the fluid impact.
Abstract
In this study, erosion tests and erosion-corrosion tests of Al5083-H321 aluminum alloy were conductedat various flow rates in seawater. The erosion tests were conducted at a flow rate of 0 to 20 m/s, anderosion-corrosion tests were performed by potentiodynamic polarization method at the same flow rate. Characteristic evaluation after the erosion test was conducted by surface analysis. Characteristic evaluation after the erosion-corrosion test was performed by Tafel extrapolation and surface analysis. The results of the surface analysis after the erosion test showed that surface damage tended to increase as the flow rate increased. In particular, intermetallic particles were separated due to the breakdown of the oxide film at 10 m/s or more. In the erosion-corrosion test, the corrosion current density increased as the flow rate increased. Additionally, the surface analysis showed that surface damage occurred in a vortex shape and the width of the surface damage tended to increase as the flow rate increased. Moreover, damage at 0 m/s, proceeded in a depth direction due to the growth of pitting corrosion, and the damaged area tended to increase due to acceleration of the intermetallic particle loss by the fluid impact.
참고문헌 (13)
- S. J. Kim, , J. Korean Soc. Mar. Eng, 30, pp.540~ (2006)
- 박일초, "대형요트의 내구성 향상을 위한 도장작업의 최적화 및 캐비테이션 침식 특성", 대한용접접합학회지, 37(3), pp.254~261 (2019), 대한용접접합학회[DOI]
- 김성종, "선박의 해양 부식과 부식방지 장치", 한국표면공학회지, 44(3), pp.105~116 (2011), 한국표면공학회
- S. R. Dehghani, , Cold Reg. Sci. Technol, 127, pp.1~ (2016)[DOI]
- A. George, , Corrosion, 37, pp.232~ (1981)[DOI]
- O. Erfan, , Int. J.Mech. Eng., 3, pp.15~ (2014)
- 박일초, "양극산화 처리된 5083 알루미늄 합금의 해수 내 유속변화에 따른 전기화학적 손상 특성", 한국표면공학회지, 49(4), pp.349~356 (2016), 한국표면공학회[DOI]
- 김성종, "해수 유속 변화에 따른 Al5052-O와 Al6061-T6 알루미늄 합금의 침식부식 특성", CORROSION SCIENCE AND TECHNOLOGY, 18(6), pp.292~299 (2019), 한국부식방식학회[DOI]
- C. Vargel, "Corrosion of Aluminium", pp.113~117 (2004), Elevier Ltd.
- Hosni Ezuber, "A study on the corrosion behavior of aluminum alloys in seawater", Materials & Design, 29(4), pp.801~805 (2008), Elsevier BV[DOI]
- F. D. Bogar, "The Influence of Chloride Ion on the Pitting of Aluminum", Journal of The Electrochemical Society, 119(4), pp.462~ (1972), The Electrochemical Society[DOI]
- 김용상, "온도 및 유속이 선박의 음극방식 및 수중 전자기장 신호 특성에 미치는 영향", 대한금속·재료학회지, 55(5), pp.348~356 (2017), 대한금속·재료학회[DOI]
- 이승준, "해양 금속재료의 부식속도와 방식전류에 미치는 유속의 영향", CORROSION SCIENCE AND TECHNOLOGY, 14(5), pp.226~231 (2015), 한국부식방식학회[DOI]