양극산화 후 실링처리된 알루미늄 합금의 해수 내 내식성과 캐비테이션 침식 저항성 평가
Evaluation of Corrosion and Cavitation Erosion Resistance of Sealed Aluminum Alloy after Anodizing Treatment in Seawater
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Various sealing techniques were applied to the anodized 5083 aluminum alloy for marine environment to reduce corrosion and cavitation erosion damage. Electrochemical experiments and cavitation erosion tests were conducted to evaluate the corrosion resistance and cavitation resistance of the anodic oxide film treated with sealing in natural seawater solution. Then, damaged surface morphology was analyzed by scanning electron microscope(SEM) and 3D microscope. As the results of the electrochemical experiments, it was observed that the surface damage of all the experimental conditions in the anodic polarization experiment was locally grown by the combination of crack and corrosion damage. In the Tafel analysis, the corrosion resistance of all sealing treatment conditions was improved compared to the anodizing. On the other hand, cavitation erosion tests showed that the anodizing and all the sealing treatment conditions generated local pit damage by cavitation erosion attack and grew to crater damage in the observation of damaged surface by SEM. Also, the weight loss and the surface damage depth measured with the experiment time presented that most of the sealing treatment conditions showed better cavitation erosion resistance than the anodizing, and they had an incubation period at the beginning of the experiment.
Abstract
Various sealing techniques were applied to the anodized 5083 aluminum alloy for marine environment to reduce corrosion and cavitation erosion damage. Electrochemical experiments and cavitation erosion tests were conducted to evaluate the corrosion resistance and cavitation resistance of the anodic oxide film treated with sealing in natural seawater solution. Then, damaged surface morphology was analyzed by scanning electron microscope(SEM) and 3D microscope. As the results of the electrochemical experiments, it was observed that the surface damage of all the experimental conditions in the anodic polarization experiment was locally grown by the combination of crack and corrosion damage. In the Tafel analysis, the corrosion resistance of all sealing treatment conditions was improved compared to the anodizing. On the other hand, cavitation erosion tests showed that the anodizing and all the sealing treatment conditions generated local pit damage by cavitation erosion attack and grew to crater damage in the observation of damaged surface by SEM. Also, the weight loss and the surface damage depth measured with the experiment time presented that most of the sealing treatment conditions showed better cavitation erosion resistance than the anodizing, and they had an incubation period at the beginning of the experiment.
참고문헌 (17)
- B.K. Sreedhar, "Cavitation damage: Theory and measurements-A review", Wear, 372, pp.177~196 (2017)
- F. Caupin, "Cavitation in water: a review", CR Phys, 7, pp.1000~1017 (2006)[DOI]
- L. van Wijngaarden, "Mechanics of collapsing cavitation bubbles", Ultrason. Sonochem, 29, pp.524~527 (2016)[DOI]
- D. Liu, "The effect of sealing and trivalent chromium passivating on anodized aluminum", Int. J. Electrochem. Sci, 11, pp.2097~2105 (2016)
- Y. Zuo, "The influences of sealing methods on corrosion behavior of anodized aluminum alloys in NaCl solutions", Surf. Coat. Technol, 166, pp.237~242 (2003)[DOI]
- Y. Guo, "Characterization of trivalent chromium process coating on AA2024-T3", Surf. Coat. Technol, 206, pp.3895~3902 (2012)[DOI]
- 강수영, "알루미늄의 아노다이징과 나노 다이아몬드 분말 봉공처리에 의한 내식성과 내마모성 향상에 관한 연구", 한국표면공학회지, 47(3), pp.121~127 (2014), 한국표면공학회[DOI]
- Corrosion resistance improvement technology of anodic oxide films on aluminum alloy that uses a lithium hydroxide solution, "M. Fujita", SAE, ~, pp.No. 2013-32-9049 (2013)
- 문성모, "황산용액에서 Al7075 합금 표면의 양극산화피막 형성거동", 한국표면공학회지, 47(4), pp.155~161 (2014), 한국표면공학회[DOI]
- 박일초, "양극산화 처리된 5083 알루미늄 합금의 해수 내 유속변화에 따른 전기화학적 손상 특성", 한국표면공학회지, 49(4), pp.349~356 (2016), 한국표면공학회[DOI]
- D.A. Jones, "Principles and Prevention of Corrosion", pp.75~ (2011), Prentice Hall
- I.C. Park, "Electrochemical characteristics in seawater for cold thermal spray-coated Al-Mg alloy layer", Acta Metall. Sin. (Engl. Lett.), 29, pp.727~734 (2016)[DOI]
- J.A. Gonzalez, "Postsealing changes in porous aluminum oxide films obtained in sulfuric acid solutions", J. Electrochem. Soc, 147, pp.984~990 (2000)[DOI]
- H. Soyama, "Comparison between cavitation peening and shot peening for extending the fatigue life of a duralumin plate with a hole", J. Mater. Process. Technol, 227, pp.80~87 (2016)[DOI]
- P. Diodati, "Cavitation damage on metallic plate surfaces oscillating at 20 kHz", Ultrason. Sonochem, 8, pp.49~53 (2001)[DOI]
- H. Guoliang, "Cavitation erosion of several oxy-fuel sprayed coatings tested in deionized water and artificial seawater", Wear, 311, pp.81~92 (2014)[DOI]
- Y. Zhang, "Electrochemical behavior of anodized Mg alloy AZ91D in chloride containing aqueous solution", Corros. Sci, 47, pp.2816~2831 (2005)[DOI]