경질양극산화된 5083-H321 알루미늄 합금의 해수 내 액적충격침식부식 손상 연구
Investigation of Liquid Droplet Impingement Erosion Corrosion based on the Flow Rate of Anodized 5083-H321 Al Alloy in Seawater
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
This study investigated the damage to the specimen due to liquid droplet impingement erosion corrosion, which improved the corrosion resistance and durability via hard anodization of 5083-H321 aluminum alloy, which is widely used for small ships and marine structures. The experiment combined liquid droplet impingement erosion and electrochemical equipment with the flow rates in natural seawater solution. Subsequently, Tafel extrapolation of polarization curves was performed to evaluate damage due to the liquid droplet impingement erosion corrosion. The damaged surface was observed using a 3D microscope and a scanning electron microscope. The degree of pitting damage was measured using the Image J program, and the surface hardness was measured using the micro-Vickers hardness tester. The corrosion current density, area, depth, and ratio of the damaged areas increased with the increase in flow rate. The grain size of the damaged area at a flow rate of 20 m s-1 showed fewer and minor differences in height, and a smooth curved shape. The hardness of the damaged surface tended to decrease with increase in flow rate.
Abstract
This study investigated the damage to the specimen due to liquid droplet impingement erosion corrosion, which improved the corrosion resistance and durability via hard anodization of 5083-H321 aluminum alloy, which is widely used for small ships and marine structures. The experiment combined liquid droplet impingement erosion and electrochemical equipment with the flow rates in natural seawater solution. Subsequently, Tafel extrapolation of polarization curves was performed to evaluate damage due to the liquid droplet impingement erosion corrosion. The damaged surface was observed using a 3D microscope and a scanning electron microscope. The degree of pitting damage was measured using the Image J program, and the surface hardness was measured using the micro-Vickers hardness tester. The corrosion current density, area, depth, and ratio of the damaged areas increased with the increase in flow rate. The grain size of the damaged area at a flow rate of 20 m s-1 showed fewer and minor differences in height, and a smooth curved shape. The hardness of the damaged surface tended to decrease with increase in flow rate.
참고문헌 (16)
- C. Vargel, "Corrosion of Aluminum", pp.88~109 (2004), Elsevier
- 황현규, "양극산화된 5083-H321 합금의 천연해수 내 전기화학적 부식 및 응력부식균열 특성에 관한 연구", CORROSION SCIENCE AND TECHNOLOGY, 19(5), pp.259~264 (2020), 한국부식방식학회[DOI]
- 신동호, "알루미늄 6061-T6 합금에 대한 양극산화층이 해수 내 부식 및 응력부식균열에 미치는 영향", 한국표면공학회지, 53(5), pp.219~226 (2020), 한국표면공학회
- Y. Zuo, , Surf. Coat. Tech, 166, pp.237~ (2003)[DOI]
- M. G. Kim, , Corros. Sci. Tech., 29, pp.11~ (2000)
- I. J. Son, , Corros. Sci. Tech., 6, pp.275~ (2007)
- 이승준, "경금속 표면개질 시 황산 수용액 조건에 따른 내식성 개선 효과", 한국마린엔지니어링학회지, 39(3), pp.223~229 (2015), 한국마린엔지니어링학회[DOI]
- D. A. Jones, "Principles and prevention of corrosion", pp.77~85 (1992), Macmillan
- Her-Hsiung Huang, "Erosion- and wear-corrosion behavior of Fe–Mn–Al alloys in NaCl solution", Materials Science and Engineering: A, 292(1), pp.90~95 (2000), Elsevier BV[DOI]
- 이승준, "해양 금속재료의 부식속도와 방식전류에 미치는 유속의 영향", CORROSION SCIENCE AND TECHNOLOGY, 14(5), pp.226~231 (2015), 한국부식방식학회[DOI]
- 김영복, "해수 환경에서 Al5083-H321 알루미늄 합금의 침식부식 손상에 미치는 유속의 영향과 손상 메카니즘", CORROSION SCIENCE AND TECHNOLOGY, 19(3), pp.115~121 (2020), 한국부식방식학회[DOI]
- George A. Gehring, "Corrosion of 5456-H117 Aluminum in High Velocity Sea Water", CORROSION, 37(4), pp.232~242 (1981), NACE International[DOI]
- S Giddey, "Stability of oxide films formed on mild steel in turbulent flow conditions of alkaline solutions at elevated temperatures", Corrosion Science, 43(8), pp.1497~1517 (2001), Elsevier BV[DOI]
- Iain Finnie, "Some reflections on the past and future of erosion", Wear, 186-187, pp.1~10 (1995), Elsevier BV[DOI]
- N. Kamkar, "Water droplet erosion mechanisms in rolled Ti–6Al–4V", Wear, 301(1-2), pp.442~448 (2013), Elsevier BV[DOI]
- N. Fujisawa, "Experiments on liquid droplet impingement erosion on a rough surface", Wear, 398-399, pp.158~164 (2018), Elsevier BV[DOI]