선박용 AA5083-H321의 유속에 의한 침식손상 방지를 위한 최적 음극방식전위 규명
Investigation of Optimum Cathodic Protection Potential to Prevent Erosion with a Flow Rate of AA5083-H321 for Marine Vessels
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study investigated the erosion-corrosion characteristics of 5038-H321 aluminum alloy in a natural seawater solution through various electrochemical experiments and flow rate parameters. Cathodic polarization experiments were conducted at flow rates ranging from 4 to 12 knots. Considering the concentration polarization section representing a relatively low current density, the range of the potentiostatic experiment was determined to be -1.6 to -1.0 V. The potentiostatic experiment was conducted at various potentials for 180 minutes in seawater. After the experiment, the corrosion characteristics were evaluated by observing surface morphology and measuring surface roughness. As a result, as the applied potential was lower, the amount of calcareous deposits increased and the roughness tended to increase. On the other hand, it was confirmed that the roughness was larger in the static condition than the flow rate condition due to the influence of the flow velocity. Variations in the chemical composition with flow rate variations were analyzed by energy-dispersive spectroscopy (EDS). In conclusion, the cathodic potential of AA5083-H321 in seawater was determined to be -1.0 V.
Abstract
This study investigated the erosion-corrosion characteristics of 5038-H321 aluminum alloy in a natural seawater solution through various electrochemical experiments and flow rate parameters. Cathodic polarization experiments were conducted at flow rates ranging from 4 to 12 knots. Considering the concentration polarization section representing a relatively low current density, the range of the potentiostatic experiment was determined to be -1.6 to -1.0 V. The potentiostatic experiment was conducted at various potentials for 180 minutes in seawater. After the experiment, the corrosion characteristics were evaluated by observing surface morphology and measuring surface roughness. As a result, as the applied potential was lower, the amount of calcareous deposits increased and the roughness tended to increase. On the other hand, it was confirmed that the roughness was larger in the static condition than the flow rate condition due to the influence of the flow velocity. Variations in the chemical composition with flow rate variations were analyzed by energy-dispersive spectroscopy (EDS). In conclusion, the cathodic potential of AA5083-H321 in seawater was determined to be -1.0 V.
참고문헌 (16)
- 조수연, "3 wt% NaCl 수용액에서 알루미늄과 스테인리스강의 부식에 따른 광 반사 거동", CORROSION SCIENCE AND TECHNOLOGY, 19(3), pp.109~114 (2020), 한국부식방식학회[DOI]
- Hosni Ezuber, "A study on the corrosion behavior of aluminum alloys in seawater", Materials & Design, 29(4), pp.801~805 (2008), Elsevier BV[DOI]
- S.R. Dehghani, "Droplet trajectories of wave-impact sea spray on a marine vessel", Cold Regions Science and Technology, 127(1), pp.1~9 (2016), Elsevier BV[DOI]
- George A. Gehring, "Corrosion of 5456-H117 Aluminum in High Velocity Sea Water", CORROSION, 37(4), pp.232~242 (1981), NACE International[DOI]
- "Stray current corrosion of ship" (2018)[URL]
- 박일초, "양극산화 처리된 5083 알루미늄 합금의 해수 내 유속변화에 따른 전기화학적 손상 특성", 한국표면공학회지, 49(4), pp.349~356 (2016), 한국표면공학회[DOI]
- 김성종, "해수 유속 변화에 따른 Al5052-O와 Al6061-T6 알루미늄 합금의 침식부식 특성", CORROSION SCIENCE AND TECHNOLOGY, 18(6), pp.292~299 (2019), 한국부식방식학회[DOI]
- Seong-Jong KIM, "Mechanical and electrochemical characteristics in sea water of 5052-O aluminum alloy for ship", Transactions of Nonferrous Metals Society of China, 23(3), pp.636~641 (2013), Elsevier BV[DOI]
- J. S. Jeon, , J. Corros. Sci. Soc. of Kor., 15, pp.3~ (1986)
- E. McCafferty, "Introduction to Corrosion Science" (2010), Springer Science & Business Media
- S. L. Wolfson, "An Initial Investigation of Calcareous Deposits upon Cathodic Steel Surfaces in Sea Water", Corrosion, 37(2), pp.70~76 (1981), NACE International[DOI]
- 이승준, "해양 금속재료의 부식속도와 방식전류에 미치는 유속의 영향", CORROSION SCIENCE AND TECHNOLOGY, 14(5), pp.226~231 (2015), 한국부식방식학회[DOI]
- H. J. Ryu, , J. Corros. Sci. Soc. of Kor., 29, pp.240~ (2000)
- William H. Hartt, "Calcareous Deposits on Metal Surfaces in Seawater—A Critical Review", CORROSION, 40(11), pp.609~618 (1984), NACE International[DOI]
- K. E. Mantel, "Substrate, Surface Finish, and Flow Rate Influences on Calcareous Deposit Structure", CORROSION, 48(6), pp.489~500 (1992), NACE International[DOI]
- C. J. Li, "The growth mechanism of calcareous deposits under various hydrostatic pressures during the cathodic protection of carbon steel in seawater", RSC Advances, 7(46), pp.28819~28825 (2017), Royal Society of Chemistry (RSC)[DOI]