합금도금강판 내식성 향상을 위한 UV 경화형 유무기 하이브리드 코팅
Improvement of anti-corrosive property for alloy plated steel sheet by UV curable organic-inorganic hybrid coatings
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
According to its merits about high curing speed and low emission of volatile organic compounds, UV curable inorganic-organic coating technology has been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. Based on the tetra-ethylorthosilicate(TEOS) and methacryloxypropyl trimethoxysilane(MPTMS), inorganic sol was synthesized and formed hybrid networks with UV curable acrylic monomer, 6-hexanediol diacrylate(HDDA), trimethylolpropane triacrylate(TMPTA), pentaerylthritol triacrylate(PETA). Several methods were used to test their properties such as salt spray test, potentiodynamic measurement, tape peel test, etc. It was shown that anti-corrosive property and stability of storage were affected by the molecular ratios of inorganic and organic compounds. It was not only the stability of storage, but had a excellent anti-corrosive, paint adhesive, and anti-solvent properties in a final molar ratios of 0.6/0.04/0.86/0.005 (TEOS/MPTMS/Acetone/HNO3) and 0.08/0.106/0.081/0.02 (TMPTA/HDDA/PETA/photo initiator).
Abstract
According to its merits about high curing speed and low emission of volatile organic compounds, UV curable inorganic-organic coating technology has been developed as an alternative for toxic and carcinogenic chromate-based treatments for years. It is consistently observed that ultra-thin films offer excellent corrosion protection as well as paint adhesion to metals. Based on the tetra-ethylorthosilicate(TEOS) and methacryloxypropyl trimethoxysilane(MPTMS), inorganic sol was synthesized and formed hybrid networks with UV curable acrylic monomer, 6-hexanediol diacrylate(HDDA), trimethylolpropane triacrylate(TMPTA), pentaerylthritol triacrylate(PETA). Several methods were used to test their properties such as salt spray test, potentiodynamic measurement, tape peel test, etc. It was shown that anti-corrosive property and stability of storage were affected by the molecular ratios of inorganic and organic compounds. It was not only the stability of storage, but had a excellent anti-corrosive, paint adhesive, and anti-solvent properties in a final molar ratios of 0.6/0.04/0.86/0.005 (TEOS/MPTMS/Acetone/HNO3) and 0.08/0.106/0.081/0.02 (TMPTA/HDDA/PETA/photo initiator).
참고문헌 (24)
- M. S. Lee, , J. Korean Ind. Eng. Chem., 12(6), pp.643~ (2001)
- S. Kwak, , Polymer Sci. Tech., 14(2), pp.181~ (2003)
- J. D. Mackenzie, , J. Sol-Gel Sci. Tech., 19(23), pp.23~ (2000)
- G. Schottner, , J. Sol-Gel Sci. Tech., 27, pp.71~ (2003)
- J. K. Park, , Hwahak Konghak, 40(6), pp.735~ (2002)
- S. K. Oh, "Preparation of UV-curable organic-inorganic hybrid hard coating solutions by sol-gel method", 박사, pp.2009
- O. H. Park, , J. Sol-Gel Sci. Tech., 16, pp.235~ (1999)
- Y. J. Eo, , Sol-Gel Sci. Tech., 13, pp.409~ (1998)
- C. J. Brinker, "Sol-Gel Science: The physics and chemistry of sol-gel processing" (1990), Academic Press
- B. Wessling, "Handbook of Nanostructured materials and nanotechnology" (1999), Academic Press
- K. Rose, "Organosilicon chemistry IV" (1999), VCH Weinheim
- C. Sanchez, , J. Mater. Chem., 15, pp.3559~ (2005)
- D. Wang, , Prog. Org. Coat., 64, pp.327~ (2009)
- H. Wang, , Corros. Sci., 49, pp.4491~ (2007)
- H. E. Bergna, , Surf. Sci., 131, pp.139~ (2006)
- P. Ocon, , Corros. Sci., 47, pp.649~ (2005)
- Z. W. Wicks, "Inorganic coatings: Science and Technology" (1994), Wiley-Vch
- S. Tasic, , Prog. Org. Coat., 51, pp.321~ (2004)
- P. Favia, , Surf. Coat. Technol., 169, pp.609~ (2003)
- W. Que, , Thin Solid Films, 358, pp.16~ (2000)
- Y. J. Ji, , J. Adhesion Interface, 7, pp.234~ (2006)
- "Standard practice for conventions applicable to electrochemical measurement in corrosion testing", ASTM G3-89, ~
- "Standar test methods for measuring adhesion tape test", ASTM G3359, ~
- P. Kiruthika, , Surf. Coating Tech., 204, pp.1270~ (2010)