원전 2차계통수 모사 환경에서 용접배관 감육 특성에 미치는 재료 및 유속의 영향
Effects of alloys and flow velocity on welded pipeline wall thinning in simulated secondary environment for nuclear power plants
2
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
The pipelines and equipments are degraded by flow-accelerated corrosion (FAC), and a large-scale test facility was constructed for simulating the FAC phenomena in secondary coolant environment for PWR type nuclear power plants. Using this facility, the FAC test was performed on a weld pipe (carbon steel and low alloy steel) under the high velocity flow conditions (> 10 m/s). Wall thickness was measured by high temperature ultrasonic monitoring systems (four-channel buffer rod type and waveguide type) during the test period and the room temperature manual ultrasonic method before and after the test period. This work deals with the complex effects of flow velocity on wall thinning of a weld pipe, and the test results showed that higher flow velocity induced different increments in the wall thinning rate for the carbon steel and low alloy steel pipe.
Abstract
The pipelines and equipments are degraded by flow-accelerated corrosion (FAC), and a large-scale test facility was constructed for simulating the FAC phenomena in secondary coolant environment for PWR type nuclear power plants. Using this facility, the FAC test was performed on a weld pipe (carbon steel and low alloy steel) under the high velocity flow conditions (> 10 m/s). Wall thickness was measured by high temperature ultrasonic monitoring systems (four-channel buffer rod type and waveguide type) during the test period and the room temperature manual ultrasonic method before and after the test period. This work deals with the complex effects of flow velocity on wall thinning of a weld pipe, and the test results showed that higher flow velocity induced different increments in the wall thinning rate for the carbon steel and low alloy steel pipe.
참고문헌 (11)
- D. H. Lister, , ICPWS XV (2008)
- R. B. Dooley, , Pressure Vessel and Piping, 77, pp.85~ (2000)
- S. Uchida, , J. Nuclear Science and Technology, 46, pp.31~ (2009)
- T. Satoh, , Corrosion, 63, pp.770~ (2007)
- H. Schmidt, , Framatome ANP GmbH (2001)
- E. M. Pavageau, , Int. Conf. on FAC (2008)
- 이요섭, "Cause Analysis of Flow Accelerated Corrosion and Erosion-Corrosion Cases in Korea Nuclear Power Plants", CORROSION SCIENCE AND TECHNOLOGY, 15(4), pp.182~188 (2016), 한국부식방식학회[DOI]
- 이은희, "유동가속부식에 영향을 미치는 수화학 인자 : pH, 용존산소, 하이드라진", CORROSION SCIENCE AND TECHNOLOGY, 12(6), pp.280~287 (2013), 한국부식방식학회[DOI]
- Y. M. Cheong, , Trans. of the Korean Nuclear Society Spring Meeting (2014)
- Y. M. Cheong, , Trans. KSNT Spring Conf (2013)
- L. Dejoux, , Int. Conf. on FAC (2010)