Lithium Disilicate (IPS e.max CAD) 코어와 전장 도재 사이의 전단결합강도에 관한 연구
A Study on the Shear Bond Strength of Veneering Ceramics to the Lithium Disilicate (IPS e.max CAD) Core
2
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
The purpose of this study was to investigate the shear bond strength between various commercial all-ceramic system core and veneering ceramics,and evaluate the clinical stability by comparing the conventional metal ceramic system. The test samples were divided into three groups: Ni-Cr alloy (metal bond), yttria-stabilized, tetragonal zirconia polycrystal (Y-TZP) (zirconia bond), lithium disilicate (lithium disilicate bond). The veneering porcelain recommended by the manufacturer for each type of material was fired to the core. After firing, the specimens were subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.50 mm/min until failure. Average shear strengths (mega pascal)were analyzed with a one-way analysis of variance and the Tukey test (α=0.05). The mean shear bond strength±SD in MPa was 44.79±2.31 in the Ni-Cr alloy group, 28.32±4.41 in the Y-TZP group, 15.91±1.39 in the Lithium disilicate group. The ANOVA showed a significant difference among groups (p＜0.05). None of the all-ceramic system core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.
Abstract
The purpose of this study was to investigate the shear bond strength between various commercial all-ceramic system core and veneering ceramics,and evaluate the clinical stability by comparing the conventional metal ceramic system. The test samples were divided into three groups: Ni-Cr alloy (metal bond), yttria-stabilized, tetragonal zirconia polycrystal (Y-TZP) (zirconia bond), lithium disilicate (lithium disilicate bond). The veneering porcelain recommended by the manufacturer for each type of material was fired to the core. After firing, the specimens were subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.50 mm/min until failure. Average shear strengths (mega pascal)were analyzed with a one-way analysis of variance and the Tukey test (α=0.05). The mean shear bond strength±SD in MPa was 44.79±2.31 in the Ni-Cr alloy group, 28.32±4.41 in the Y-TZP group, 15.91±1.39 in the Lithium disilicate group. The ANOVA showed a significant difference among groups (p＜0.05). None of the all-ceramic system core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.
참고문헌 (21)
- Braga RR, "Influence of time and adhesive system on the extrusion shear strength between feldspathic porcelain and bovine dentin", Dent Mater, 16, pp.303~310 (2000)
- Kelly JR, "Ceramics in dentistry: historical roots and current perspectives", J Prosthet Dent, 75, pp.18~32 (1996)
- Fasbinder DJ, "A clinical evaluation of chairside lithium disilicate CAD", CAM crowns: a two-year report, 2010, pp.141, 10S~14S
- Tysowsky G, "The science behind lithium disilicate: today’s surprisingly versatile, esthetic & durable metal-free alternative", Oral Health J, 10, pp.93~97 (2009)
- 김재홍, "전치부 전부도재관을 이용한 테트라싸이클린 착색의 심미보철 회복 증례 (IPS e.max CAD 블록의 이용)", 치위생과학회지, 11(4), pp.299~303 (2011), 한국치위생과학회
- Sundh A, "A comparison of yttrium-oxide-partially- stabilized zirconia ceramic crowns with varying core thickness, shapes and veneer ceramic", J Oral Rehabilitation, 31, pp.682~688 (2004)
- Aboushelib MN, "Effect of zirconia type on its bond strength with different veneer ceramics", J Prosthodont, 17, pp.401~408 (2008)
- Albakry M, "Fracture toughness and hardness evaluation of three pressable all-ceramic dental materials", J Dent, 31, pp.181~188 (2003)
- Al-Dohan HM, "Shear strength of core-veneer interface in bi-layered ceramics", J Prosthet Dent, 91, pp.349~355 (2004)
- Isgro G, "The influence of the veneering porcelain and different surface treatments on the biaxial flexural strength of a heat-pressed ceramic", J Prosthet Dent, 90, pp.465~473 (2003)
- Schmitz K, "Determination of the adhesion of dental metal-porcelain bonding systems", Dental Labor, 23, pp.1416~1420 (1975)
- 김재홍, "도재 소성 과정에서의 고온이 지르코니아 코어의 변연적합도에 미치는 영향", 치위생과학회지, 13(2), pp.135~141 (2013), 한국치위생과학회
- Komine F, "Influence of different adhesive resin cements on the fracture strength of aluminum oxide ceramic posterior crowns", J Prosthet Dent, 92, pp.359~364 (2004)
- Guess PC, "Shear bond strengths between different zirconia cores and veneering ceramics and their susceptibility to thermocycling", Dent Mater, 24, pp.1556~1567 (2008)
- Craig RG, "Mechanical properties in restorative dental materials", pp.551~592 (2002), Mosby
- Dundar M, "Bond strengths of veneering ceramics to reinforced ceramic core materials", Int J Prosthodont, 18, pp.71~72 (2005)
- Derand T, "Bond strength of composite luting cement to zirconia ceramic surfaces", Dent Mater, 21, pp.1158~1162 (2005)
- Ishibe M, "Shear bond strengths of pressed and layered veneering ceramics to highnoble alloy and zirconia cores", J Prosthet Dent, 106, pp.29~37 (2011)
- De Melo RM, "Shear bond strengths of a ceramic system to alternative metal alloys", J Prosthet Dent, 93, pp.64~69 (2005)
- 최부경, "Shear bond strength of veneering porcelain to zirconia and metal cores", The Journal of Advanced of Prosthodontics, 1(3), pp.129~135 (2009), 대한치과보철학회
- Denry I, "State of the art of zirconia for dental applications", Dent Mater, 24, pp.299~307 (2008)