지르코니아 코어의 표면처리가 비니어링 세라믹과의 전단결합강도에 미치는 영향
Effect of surface treatmet on the shear bond strength of a zirconia core to veneering ceramic
2
조회
0
다운로드
7
인용
0
참고문헌
키워드
초록
Purpose: The purpose of this research was to evaluate the shear bond strength between zirconia core and veneer ceramic after surface treatment. Material and methods: Zirconia cores (N = 40, n = 10, 10 mm×10 mm×3 mm) were fabricated according to the manufacturers’ instructions and ultrasonically cleaned. The veneering ceramics (thickness 3 mm) were built and fired onto the zirconia core materials. Four groups of specimens with different surface treatment were prepared. Group I: without any pre-treatment, Group Ⅱ: treated with sandblasting, Group Ⅲ: treated with liner, Group Ⅳ: treated with sandblasting and liner. The shear bond strength was tested in a universal testing machine. Data were compared with an ANOVA and Scheffe′post hoc test (P = .05). Results: The shear bond strength of group Ⅵ was significantly higher than the other groups. Conclusion: Both mechanically and chemically treated simultaneously on zirconia core surface influenced the shear bond strength between the core and veneering ceramic in allceramic systems.
Abstract
Purpose: The purpose of this research was to evaluate the shear bond strength between zirconia core and veneer ceramic after surface treatment. Material and methods: Zirconia cores (N = 40, n = 10, 10 mm×10 mm×3 mm) were fabricated according to the manufacturers’ instructions and ultrasonically cleaned. The veneering ceramics (thickness 3 mm) were built and fired onto the zirconia core materials. Four groups of specimens with different surface treatment were prepared. Group I: without any pre-treatment, Group Ⅱ: treated with sandblasting, Group Ⅲ: treated with liner, Group Ⅳ: treated with sandblasting and liner. The shear bond strength was tested in a universal testing machine. Data were compared with an ANOVA and Scheffe′post hoc test (P = .05). Results: The shear bond strength of group Ⅵ was significantly higher than the other groups. Conclusion: Both mechanically and chemically treated simultaneously on zirconia core surface influenced the shear bond strength between the core and veneering ceramic in allceramic systems.
참고문헌 (15)
- Du ¨ndar M, "Comparison of two bond strength testing methodologies for bilayered all-ceramics", Dent Mater, 23, pp.630~636 (2007)
- Al-Dohan HM, "Shear strength of core-veneer interface in bi-layered ceramics", J Prosthet Dent, 91, pp.349~355 (2004)
- Daftary F, "Effect of four pretreatment techniques on porcelain-to-metal bond strength", J Prosthet Dent, 58, pp.535~540 (1986)
- Kelly JR, "Clinically relevant approach to failure testing of all-ceramic restorations", J Prosthet Dent, 81, pp.652~661 (1999)
- Braga RR, "Influence of time and adhesive system on the extrusion shear strength between feldspathic porcelain and bovine dentin", Dent Mater, 16, pp.303~310 (2000)
- Derand T, "Bond strength of composite luting cement to zirconia ceramic surfaces", Dent Mater, 21, pp.1158~1162 (2005)
- Du¨ndar M, "Bond strengths of veneering ceramics to reinforced ceramic core materials", Int J Prosthodont, 18, pp.71~72 (2005)
- Aboushelib MN, "Microtensile bond strength of different components of core veneered allceramic restorations. Part II: Zirconia veneering ceramics", Dent Mater, 22, pp.857~863 (2006)
- Aboushelib MN, "Microtensile bond strength of different components of core veneered all-ceramic restorations", Dent Mater, 21, pp.984~991 (2005)
- Borges GA, "Effect of etching and airborne particle abrasion on the microstructure of different dental ceramics", J Prosthet Dent, 89, pp.479~488 (2003)
- White SN, "Flexural strength of a layered zirconia and porcelain dental all-ceramic system", J Prosthet Dent, 94, pp.125~131 (2005)
- Sundh A, "Fracture resistance of yttrium oxide partially-stabilized zirconia all-ceramic bridges after veneering and mechanical fatigue testing", Dent Mater, 21, pp.476~482 (2005)
- Guazzato M, "Strength, fracture toughness and microstructure of a selection of allceramic materials. Part II. Zirconia-based dental ceramics", Dent Mater, 20, pp.449~456 (2004)
- Sundh A, "A comparison of fracture strength of yttrium-oxide- partially-stabilized zirconia ceramic crowns with varying core thickness, shapes and veneer ceramics", J Oral Rehabil, 31, pp.682~688 (2004)
- Anusavice KJ, "Comparative evaluation of ceramic-metal bond tests using finite element stress analysis", J Dent Res, 59, pp.608~613 (1980)