동적하중 하에서 근관치료용 임시충전재의 미세누출의 평가
Microleakage of endodontic temporary restorative materials under dynamic loading
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The purpose of this study was to compare the sealing abilities of four endodontic temporary restorative materials using a methylene blue dye penetration test under dynamic loading. Standardized access cavities were prepared in forty-four intact human permanent molar teeth, and the cavities were restored with Caviton, MD-Temp, IRM, or ZOE. After thermocycling, an intermittent load of 98 N at 1 Hz was applied for 1,000 cycles to the long axis of the functional cusp of each of the teeth, which were immersed in a 1% methylene blue solution. The teeth were split in half, and the linear depth of dye penetration was evaluated according to the criteria. The results were analyzed using one-way ANOVA (p = 0.05) and Duncan’s multiple range test. The results demonstrated that Caviton and MD-Temp showed significantly lower microleakage than IRM and ZOE. It was concluded that Caviton and MD-Temp exhibited better sealing ability than IRM and ZOE under dynamic loading.
Abstract
The purpose of this study was to compare the sealing abilities of four endodontic temporary restorative materials using a methylene blue dye penetration test under dynamic loading. Standardized access cavities were prepared in forty-four intact human permanent molar teeth, and the cavities were restored with Caviton, MD-Temp, IRM, or ZOE. After thermocycling, an intermittent load of 98 N at 1 Hz was applied for 1,000 cycles to the long axis of the functional cusp of each of the teeth, which were immersed in a 1% methylene blue solution. The teeth were split in half, and the linear depth of dye penetration was evaluated according to the criteria. The results were analyzed using one-way ANOVA (p = 0.05) and Duncan’s multiple range test. The results demonstrated that Caviton and MD-Temp showed significantly lower microleakage than IRM and ZOE. It was concluded that Caviton and MD-Temp exhibited better sealing ability than IRM and ZOE under dynamic loading.
참고문헌 (19)
- Noguera AP, "A comparative in vitro coronal microleakage study of new endodontic restorative materials", J Endod, 16, pp.523~527 (1990)
- Saunders WP, "Coronal leakage as a cause of failure in root canal therapy: a review", Endod Dent Traumatol, 10, pp.105~108 (1994)
- Delivanis PD, "Comparison and reliability of techniques for measuring leakage and marginal penetration", Oral Surg Oral Med Oral Pathol, 53, pp.410~416 (1982)
- Jacquot BM, "Evaluation of temporary restorations’microleakage by means of electrochemical impedance measurements", J Endod, 22, pp.586~589 (1996)
- Anderson RW, "Microleakage of temporary restorations in complex endodontic access preparation", J Endod, 15, pp.526~529 (1989)
- Krakow AA, "In vivo study of temporary filling materials used in endodontics in anterior teeth", Oral Surg Oral Med Oral Pathol, 43, pp.615~620 (1977)
- Mayer T, "Microleakage of temporary restorations after thermocycling and mechanical loading", J Endod, 23, pp.320~322 (1997)
- Liberman R, "Effect of repeated vertical loads on microleakage of IRM and calcium sulfate-based temporary fillings", J Endod, 27, pp.724~729 (2001)
- Cruz EV, "A laboratory study of coronal microleakage using four temporary restorative materials", Int Endod J, 35, pp.315~320 (2002)
- Jung SH, "Microleakage and fracture pat terns of teeth restored with different posts under dynamic loading", J Prosthet Dent, 98, pp.270~276 (2007)
- Webber RT, "Sealing quality of a temporary filling material", Oral Surg Oral Med Oral Pathol, 46, pp.123~130 (1978)
- Anderson RW, "Microleakage of three temporary endodontic restorations", J Endod, 14, pp.497~501 (1988)
- Graf H, "Bruxim", Dent Clin North Am, 13, pp.659~665 (1969)
- Anderson DJ, "Measurements of stress in mastication 1", J Dent Res, 135, pp.664~670 (1956)
- Anderson DJ, "Measurements of stress in mastication 2", J Dent Res, 135, pp.671~673 (1956)
- Vail MM, "Preference of temporary restorations and spacers: a survey of Diplomates of the American Board of Endodontists", J Endod, 32, pp.513~515 (2006)
- Widerman FH, "The physical and biologic properties of Cavit", J Am Dent Assoc, 82, pp.378~382 (1971)
- Lee YC, "Microleakage of endodontic temporary restorative materials", J Endod, 19, pp.516~520 (1993)
- Pai SF, "Microleakage between endodontic temporary restorative materials placed at different times", J Endod, 25, pp.453~456 (1999)