Effect of immersion into solutions at various pH on the color stability of composite resins with different shades
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Objectives: This study examined the color changes of a resin composite with different shades upon exposure to water with different pH. Materials and Methods: Nanohybrid resin composites (Filtek Z350XT, 3M ESPE) with four different shades (A2, A3, B1, and B2) were immersed in water with three different pH (pH 3, 6, and 9) for 14 day. The CIE L*a*b* color coordinates of the specimens were evaluated before and after immersion in the solutions. The color difference (ΔE*) and the translucency parameter (TP) were calculated using the color coordinates. Results: ΔE* ranged from 0.33 to 1.58, and the values were affected significantly by the pH. The specimens immersed in a pH 6 solution showed the highest ΔE* values (0.87 - 1.58). The specimens with a B1 shade showed the lowest ΔE* change compared to the other shades. TP ranged from 7.01 to 9.46 depending on the pH and resin shade. The TP difference between before and after immersion in the pH solutions was less than 1.0. Conclusions: The resulting change of color of the tested specimens did not appear to be clinically problematic because the color difference was < 1.6 in the acidic, neutral, and alkaline solutions regardless of the resin shade, i.e., the color change was imperceptible.
Abstract
Objectives: This study examined the color changes of a resin composite with different shades upon exposure to water with different pH. Materials and Methods: Nanohybrid resin composites (Filtek Z350XT, 3M ESPE) with four different shades (A2, A3, B1, and B2) were immersed in water with three different pH (pH 3, 6, and 9) for 14 day. The CIE L*a*b* color coordinates of the specimens were evaluated before and after immersion in the solutions. The color difference (ΔE*) and the translucency parameter (TP) were calculated using the color coordinates. Results: ΔE* ranged from 0.33 to 1.58, and the values were affected significantly by the pH. The specimens immersed in a pH 6 solution showed the highest ΔE* values (0.87 - 1.58). The specimens with a B1 shade showed the lowest ΔE* change compared to the other shades. TP ranged from 7.01 to 9.46 depending on the pH and resin shade. The TP difference between before and after immersion in the pH solutions was less than 1.0. Conclusions: The resulting change of color of the tested specimens did not appear to be clinically problematic because the color difference was < 1.6 in the acidic, neutral, and alkaline solutions regardless of the resin shade, i.e., the color change was imperceptible.
참고문헌 (18)
- Uchida H, "Color stability of dental composites as a function of shade", J Prosthet Dent, 79, pp.372~377 (1998)
- Correr GM, "In vitro long-term degradation of aesthetic restorative materials in food-simulating media", Acta Odontol Scand, 70, pp.101~108 (2012)
- Bagheri R, "Influence of food simulating solutions and surface finish on susceptibility to staining of aesthetic restorative materials", J Dent, 33, pp.389~398 (2005)
- Bollen CM, "Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: a review of the literature", Dent Mater, 13, pp.258~269 (1997)
- Göpferich A, "Mechanisms of polymer degradation and erosion", Biomaterials, 17, pp.103~114 (1996)
- Lingström P, "Comparison of three different methods for measurements of plaque-pH in humans after consumption of soft bread and potato chips", J Dent Res, 72, pp.865~870 (1993)
- Chadwick RG, "The effect of storage media upon the surface microhardness and abrasion resistance of three composites", Dent Mater, 6, pp.123~128 (1990)
- Prakki A, "Influence of pH environment on polymer based dental material properties", J Dent, 33, pp.91~98 (2005)
- Cilli R, "Properties of dental resins submitted to pH catalysed hydrolysis", J Dent, 40, pp.1144~1150 (2012)
- Guler AU, "Effects of different drinks on stainability of resin composite provisional restorative materials", J Prosthet Dent, 94, pp.118~124 (2005)
- Turssi CP, "Effect of storage media upon the surface micromorphology of resin-based restorative materials", J Oral Rehabil, 29, pp.864~871 (2002)
- Um CM, "Staining of resin-based veneering materials with coffee and tea", Quintessence Int, 22, pp.377~386 (1991)
- Ortengren U, "Influence of pH and storage time on the sorption and solubility behavior of three composite resin materials", J Dent, 29, pp.35~41 (2001)
- Poggio C, "Surface roughness of flowable resin composites eroded by acidic and alcoholic drinks", J Conserv Dent, 15, pp.137~140 (2012)
- Buchalla W, "Brushing abrasion of luting cements under neutral and acidic conditions", Oper Dent, 25, pp.482~487 (2000)
- Eisenburger M, "Acidic solubility of luting cements", J Dent, 31, pp.137~142 (2003)
- Abu-Bakr N, "Color stability of compomer after immersion in various media", J Esthet Dent, 12, pp.258~263 (2000)
- Vichi A, "Color and opacity variations in three different resin-based composite products after water aging", Dent Mater, 20, pp.530~534 (2004)