복합 레진으로 수복된 세 가지 첨와형태 와동의 파절 저항성에 관한 연구
Fracture resistance of the three types of undermined cavity filled with composite resin
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
It was reported that esthetic composite resin restoration reinforces the strength of remaining tooth structure with preserving the natural tooth structure. However, it is unknown how much the strength would be recovered. The purpose of this study was to compare the fracture resistance of three types of undermined cavity filled with composite resin with that of non-cavitated natural tooth. Forty sound upper molars were allocated randomly into four groups of 10 teeth. After flattening occlusal enamel, undermined cavities were prepared in thirty teeth to make three types of specimens with various thickness of occlusal structure (Group 1 3). All the cavity have the 5 ㎜ width mesiodistally and 7 ㎜ depth bucco-lingually. Another natural 10 teeth (Group 4) were used as a control group. Teeth in group 1 have remaining occlusal structure about 1 ㎜ thickness, which was composed of mainly enamel and small amount of dentin. In Group 2, remained thickness was about 1.5 ㎜, including 0.5 ㎜ thickness dentin. In Group 3, thickness was about 2.0 ㎜, including 1 ㎜ thickness dentin. Every effort was made to keep the remaining dentin thickness about 0.5 ㎜ from the pulp space in cavitated groups. All the thickness was evaluated with radiographic Length Analyzer program. After acid etching with 37% phosphoric acid, one-bottle adhesive (Single BondTM, 3M/ESPE, USA) was applied following the manufacturer’s recommendation and cavities were incrementally filled with hybrid composite resin (Filtek Z-250TM, 3M/ESPE, USA). Teeth were stored in distilled water for one day at room temperature, after then, they were finished and polished with Sof-Lex system. All specimens were embedded in acrylic resin and static load was applied to the specimens with a 3㎜ diameter stainless steel rod in an Universal testing machine and cross-head speed was 1 ㎜/min. Maximum load in case of fracture was recorded for each specimen. The data were statistically analyzed using one-way analysis of variance (ANOVA) and a Tukey test at the 95% confidence level. The results were as follows: 1. Fracture resistance of the undermined cavity filled with composite resin was about 75% of the natural tooth. 2. No significant difference in fracture loads of composite resin restoration was found among the three types of cavitated groups. Within the limits of this study, it can be concluded the fracture resistance of the undermined cavity filled with composite resin was lower than that of natural teeth, however remaining tooth structure may be supported and saved by the reinforcement with adhesive restoration, even if that portion consists of mainly enamel and a little dentin structure.
Abstract
It was reported that esthetic composite resin restoration reinforces the strength of remaining tooth structure with preserving the natural tooth structure. However, it is unknown how much the strength would be recovered. The purpose of this study was to compare the fracture resistance of three types of undermined cavity filled with composite resin with that of non-cavitated natural tooth. Forty sound upper molars were allocated randomly into four groups of 10 teeth. After flattening occlusal enamel, undermined cavities were prepared in thirty teeth to make three types of specimens with various thickness of occlusal structure (Group 1 3). All the cavity have the 5 ㎜ width mesiodistally and 7 ㎜ depth bucco-lingually. Another natural 10 teeth (Group 4) were used as a control group. Teeth in group 1 have remaining occlusal structure about 1 ㎜ thickness, which was composed of mainly enamel and small amount of dentin. In Group 2, remained thickness was about 1.5 ㎜, including 0.5 ㎜ thickness dentin. In Group 3, thickness was about 2.0 ㎜, including 1 ㎜ thickness dentin. Every effort was made to keep the remaining dentin thickness about 0.5 ㎜ from the pulp space in cavitated groups. All the thickness was evaluated with radiographic Length Analyzer program. After acid etching with 37% phosphoric acid, one-bottle adhesive (Single BondTM, 3M/ESPE, USA) was applied following the manufacturer’s recommendation and cavities were incrementally filled with hybrid composite resin (Filtek Z-250TM, 3M/ESPE, USA). Teeth were stored in distilled water for one day at room temperature, after then, they were finished and polished with Sof-Lex system. All specimens were embedded in acrylic resin and static load was applied to the specimens with a 3㎜ diameter stainless steel rod in an Universal testing machine and cross-head speed was 1 ㎜/min. Maximum load in case of fracture was recorded for each specimen. The data were statistically analyzed using one-way analysis of variance (ANOVA) and a Tukey test at the 95% confidence level. The results were as follows: 1. Fracture resistance of the undermined cavity filled with composite resin was about 75% of the natural tooth. 2. No significant difference in fracture loads of composite resin restoration was found among the three types of cavitated groups. Within the limits of this study, it can be concluded the fracture resistance of the undermined cavity filled with composite resin was lower than that of natural teeth, however remaining tooth structure may be supported and saved by the reinforcement with adhesive restoration, even if that portion consists of mainly enamel and a little dentin structure.
참고문헌 (23)
- Mount GJ, "Preservation and restoration of tooth structure", pp.126~153 (1998), Mosby
- Lacy AM, "The class III posterior composite restoration", Dentistry Today, pp.80~85 (2002)
- Setien V, "Conservative restoration of proximal-cervical lesions", Oper Dent, 28(3), pp.321~323 (2003)
- Abu-Hanna AA, "Resin composite reinforcement of undermined enamel", Oper Dent, 29(2), pp.234~237 (2004)
- Wilson AD, "Glass-ionomer cement", Quintessence Int, 30(3), pp.197~200 (1988)
- Mount GJ, "An Atlas of Glass-ionomer cements, second ed", pp.118~122 (1994), Martin Dunitz
- Denehy GE, "Internal enamel reinforcement through micromechanical bonding", J Prosthet Dent, 36(2), pp.171~175 (1976)
- Eakle WS, "Effect of bonded gold inlays on fracture resistance of teeth", Quintessence Int, 23, pp.421~425 (1992)
- Jagadish S, "Fracture resistance of teeth with class II silver amalgam, posterior composite and glass cermet restorations", Oper Dent, 15(2), pp.42~47 (1990)
- Borges AFS, "Compressive strength recovered by composite onlays in primary teeth Substrate treatment and luting agent effects", J Dent, 34, pp.478~484 (2006)
- Roggenkamp CL, "The facial slot preparation: a non-occlusal option for Class 2 carious lesions", Oper Dent, 7(3), pp.102~106 (1982)
- Croll TP, "Lateral-access class II restoration using resin-modified glass-ionomer or silver-cermet cement", Quintessence Int, 26, pp.121~126 (1995)
- Gorucu J, "Fracture resistance of teeth with class II bonded amalgam and new tooth-colored restorations", Oper Dent, 28(5), pp.501~507 (2003)
- Johnston WM, "A mathematical model for post-irradiation hardening of photoactivated composite resins", Dent Mater, 1(5), pp.191~194 (1985)
- Eick JD, "Dentin adhesives-do they protect the dentin from acid etching?", Quintessence Int, 17(9), pp.533~544 (1986)
- Wieczkowski G, "Effects of incremental versus bulk fill technique on resistance to cuspal fracture of teeth restored with posterior composites", J Prosthet Dent, 60(3), pp.283~287 (1988)
- Martins LRM, "Influence of the glass ionomer cement and composite resin on enamel supported and its effect in the cuspal stiffness and flexure", J Dent Res, 76(3232) (1997)
- Eidelman E, "Composite resin support of undermined enamel in amalgam restorations", Pediatr Dent, 21, pp.118~120 (1999)
- Yaman SD, "Fracture resistance of class II approximal slot restorations", J Prosthet Dent, 84, pp.297~302 (2000)
- Gracis SE, "Shock-absorbing behavior of five restorative materials used on implants", Int J Prosthodont, 4, pp.282~291 (1991)
- Strand GV, "Marginal ridge strength of tunnel-prepared teeth restored with various adhesive filling materials", Cement and Concrete Research, 29, pp.645~650 (1999)
- St-Georges AJ, "Fracture resistance of prepared teeth restored with bonded inlay restorations", J Prosthet Dent, 89, pp.551~557 (2003)
- Latino C, "Support of undermined occlusal enamel provided by restorative materials", Quintessence Int, 32, pp.287~291 (2001)