In vivo comparison between the effects of chemically modified hydrophilic and anodically oxidized titanium surfaces on initial bone healing
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Purpose: The aim of this study was to investigate the combined effects of physical and chemical surface factors on in vivo bone responses by comparing chemically modified hydrophilic sandblasted, large-grit, acid-etched (modSLA) and anodically oxidized hydrophobic implant surfaces. Methods: Five modSLA implants and five anodized implants were inserted into the tibiae of five New Zealand white rabbits (one implant for each tibia). The characteristics of each surface were determined using field emission scanning electron microscopy, energy dispersive spectroscopy, and confocal laser scanning microscopy before the installation. The experimental animals were sacrificed after 1 week of healing and histologic slides were prepared from the implant-tibial bone blocks removed from the animals. Histomorphometric analyses were performed on the light microscopic images, and bone-to-implant contact (BIC) and bone area (BA) ratios were measured. Nonparametric comparison tests were applied to find any significant differences (P<0.05) between the modSLA and anodized surfaces. Results: The roughness of the anodized surface was 1.22±0.17 μm in Sa, which was within the optimal range of 1.0-2.0 μm for a bone response. The modSLA surface was significantly rougher at 2.53±0.07 μm in Sa. However, the modSLA implant had significantly higher BIC than the anodized implant (P=0.02). Furthermore, BA ratios did not significantly differ between the two implants, although the anodized implant had a higher mean value of BA (P>0.05). Conclusions: Within the limitations of this study, the hydrophilicity of the modSLA surface may have a stronger effect on in vivo bone healing than optimal surface roughness and surface chemistry of the anodized surface.
Abstract
Purpose: The aim of this study was to investigate the combined effects of physical and chemical surface factors on in vivo bone responses by comparing chemically modified hydrophilic sandblasted, large-grit, acid-etched (modSLA) and anodically oxidized hydrophobic implant surfaces. Methods: Five modSLA implants and five anodized implants were inserted into the tibiae of five New Zealand white rabbits (one implant for each tibia). The characteristics of each surface were determined using field emission scanning electron microscopy, energy dispersive spectroscopy, and confocal laser scanning microscopy before the installation. The experimental animals were sacrificed after 1 week of healing and histologic slides were prepared from the implant-tibial bone blocks removed from the animals. Histomorphometric analyses were performed on the light microscopic images, and bone-to-implant contact (BIC) and bone area (BA) ratios were measured. Nonparametric comparison tests were applied to find any significant differences (P<0.05) between the modSLA and anodized surfaces. Results: The roughness of the anodized surface was 1.22±0.17 μm in Sa, which was within the optimal range of 1.0-2.0 μm for a bone response. The modSLA surface was significantly rougher at 2.53±0.07 μm in Sa. However, the modSLA implant had significantly higher BIC than the anodized implant (P=0.02). Furthermore, BA ratios did not significantly differ between the two implants, although the anodized implant had a higher mean value of BA (P>0.05). Conclusions: Within the limitations of this study, the hydrophilicity of the modSLA surface may have a stronger effect on in vivo bone healing than optimal surface roughness and surface chemistry of the anodized surface.
참고문헌 (38)
- Anselme K, "Qualitative and quantitative study of human osteoblast adhesion on materials with various surface roughnesses", J Biomed Mater Res, 49, pp.155~166 (2000)
- Lausmaa J, "Surface spectroscopic characterization of titanium implant materials", J Electron Spectros Relat Phenomena, 81, pp.343~361 (1996)
- Albrektsson T, "Direct bone anchorage of dental implants", J Prosthet Dent, 50, pp.255~261 (1983)
- Lim YJ, "Surface characterizations of variously treated titanium materials", Int J Oral Maxillofac Implants, 16, pp.333~342 (2001)
- Taborelli M, "Influence of surface treatments developed for oral implants on the physical and biological properties of titanium. (I) Surface characterization", Clin Oral Implants Res, 8, pp.208~216 (1997)
- Wennerberg A, "Effects of titanium surface topography on bone integration: a systematic review", Clin Oral Implants Res, 20(Suppl 4), pp.172~184 (2009)
- Cooper LF, "A role for surface topography in creating and maintaining bone at titanium endosseous implants", J Prosthet Dent, 84, pp.522~534 (2000)
- Pilliar RM, "Overview of surface variability of metallic endosseous dental implants: textured and porous surface-structured designs", Implant Dent, 7, pp.305~314 (1998)
- Kilpadi DV, "Surface energy characterization of unalloyed titanium implants", J Biomed Mater Res, 28, pp.1419~1425 (1994)
- Wang R, "Light-induced amphiphilic surfaces", Nature, 388, pp.431~432 (1997)
- Wennerberg A, "Suggested guidelines for the topographic evaluation of implant surfaces", Int J Oral Maxillofac Implants, 15, pp.331~344 (2000)
- Bico J, "Wetting of textured surfaces", Colloids Surf A Physicochem Eng Asp, 206, pp.41~46 (2002)
- Rupp F, "Wetting behavior of dental implants", Int J Oral Maxillofac Implants, 26, pp.1256~1266 (2011)
- Rupp F, "Enhancing surface free energy and hydrophilicity through chemical modification of microstructured titanium implant surfaces", J Biomed Mater Res A, 76, pp.323~334 (2006)
- Rupp F, "Roughness induced dynamic changes of wettability of acid etched titanium implant modifications", Biomaterials, 25, pp.1429~1438 (2004)
- Textor M, "Titanium in medicine: material science, surface science, engineering, biological responses, and medical applications", pp.171~230 (2001), Springer
- Buser D, "Enhanced bone apposition to a chemically modified SLA titanium surface", J Dent Res, 83, pp.529~533 (2004)
- Junker R, "Effects of implant surface coatings and composition on bone integration: a systematic review", Clin Oral Implants Res, 20(Suppl 4), pp.185~206 (2009)
- Schwarz F, "Effects of surface hydrophilicity and microtopography on early stages of soft and hard tissue integration at non-submerged titanium implants: an immunohistochemical study in dogs", J Periodontol, 78, pp.2171~2184 (2007)
- Choi JY, "Comparison between bioactive fluoride modified and bioinert anodically oxidized implant surfaces in early bone response using rabbit tibia model", Implant Dent, 21, pp.124~128 (2012)
- Wennerberg A, "On implant surfaces: a review of current knowledge and opinions", Int J Oral Maxillofac Implants, 25, pp.63~74 (2010)
- Iwai-Yoshida M, "Antioxidant and osteogenic properties of anodically oxidized titanium", J Mech Behav Biomed Mater, 13, pp.230~236 (2012)
- Le Guehennec L, "Osteoblastic cell behaviour on different titanium implant surfaces", Acta Biomater, 4, pp.535~543 (2008)
- Schuler RF, "Effect of implant surface and grafting on implants placed into simulated extraction sockets: a histologic study in dogs", Int J Oral Maxillofac Implants, 25, pp.893~900 (2010)
- Ferguson SJ, "Geis-Gerstorfer J, et al. Biomechanical evaluation of the interfacial strength of a chemically modified sandblasted and acid-etched titanium surface", J Biomed Mater Res A, 78, pp.291~297 (2006)
- Wall I, "Modified titanium surfaces promote accelerated osteogenic differentiation of mesenchymal stromal cells in vitro", Bone, 45, pp.17~26 (2009)
- Hong J, "A hydrophilic dental implant surface exhibits thrombogenic properties in vitro", Clin Implant Dent Relat Res, 15, pp.105~112 (2013)
- Yeo IS, "Biomechanical and histomorphometric study of dental implants with different surface characteristics", J Biomed Mater Res B Appl Biomater, 87, pp.303~311 (2008)
- Donath K, "A method for the study of undecalcified bones and teeth with attached soft tissues. The Säge-Schliff (sawing and grinding) technique", J Oral Pathol, 11, pp.318~326 (1982)
- Roberts WE, "Osseous adaptation to continuous loading of rigid endosseous implants", Am J Orthod, 86, pp.95~111 (1984)
- Steigenga J, "Effects of implant thread geometry on percentage of osseointegration and resistance to reverse torque in the tibia of rabbits", J Periodontol, 75, pp.1233~1241 (2004)
- Albrektsson T, "Oral implant surfaces: Part 2--review focusing on clinical knowledge of different surfaces", Int J Prosthodont, 17, pp.544~564 (2004)
- Schwarz F, "Bone regeneration in dehiscence-type defects at chemically modified (SLActive) and conventional SLA titanium implants: a pilot study in dogs", J Clin Periodontol, 34, pp.78~86 (2007)
- Gottlow J, "An experimental comparison of two different clinically used implant designs and surfaces", Clin Implant Dent Relat Res, 14(Suppl 1), pp.e204~e212 (2012)
- Abrahamsson I, "Early bone formation adjacent to rough and turned endosseous implant surfaces. An experimental study in the dog", Clin Oral Implants Res, 15, pp.381~392 (2004)
- Berglundh T, "De novo alveolar bone formation adjacent to endosseous implants", Clin Oral Implants Res, 14, pp.251~262 (2003)
- Schwarz F, "Histological and immunohistochemical analysis of initial and early osseous integration at chemically modified and conventional SLA titanium implants: preliminary results of a pilot study in dogs", Clin Oral Implants Res, 18, pp.481~488 (2007)
- Schmid J, "The significance of angiogenesis in guided bone regeneration. A case report of a rabbit experiment", Clin Oral Implants Res, 8, pp.244~248 (1997)