Biomechanical evaluation of dental implants with different surfaces: Removal torque and resonance frequency analysis in rabbits
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
STATEMENT OF PROBLEM. Macroscopic and especially microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. Dental implants with modified surfaces have shown stronger osseointegration than implants which are only turned (machined). Advanced surface modification techniques such as anodic oxidation and Ca-P application have been developed to achieve faster and stronger bonding between the host bone and the implant. PURPOSE. The purpose of this study was to investigate the effect of surface treatment of titanium dental implant on implant stability after insertion using the rabbit tibia model. MATERIAL AND METHODS. Three test groups were prepared: sandblasted, large-grit and acid-etched (SLA) implants, anodic oxidized implants, and anodized implants with Ca-P immersion. The turned implants served as control. Twenty rabbits received 80 implants in the tibia. Resonance frequencies were measured at the time of implant insertion, 2 weeks and 4 weeks of healing. Removal torque values (RTV) were measured 2 and 4 weeks after insertion. RESULTS. The implant stability quotient (ISQ) values of implants for resonance frequency analysis (RFA) increased significantly (P < .05) during 2 weeks of healing period although there were no significant differences among the test and control groups (P > .05). The test and control implants also showed significantly higher ISQ values during 4 weeks of healing period (P < .05). No significant differences, however, were found among all the groups. All the groups showed no significant differences in ISQ values between 2 and 4 weeks after implant insertion (P >.05). The SLA, anodized and Ca-P immersed implants showed higher RTVs at 2 and 4 weeks of healing than the machined one (P < .05). However, there was no significant difference among the experimental groups. CONCLUSION. The surface-modified implants appear to provide superior implant stability to the turned one. Under the limitation of this study, however, we suggest that neither anodic oxidation nor Ca-P immersion techniques have any advantage over the conventional SLA technique with respect to implant stability.
Abstract
STATEMENT OF PROBLEM. Macroscopic and especially microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. Dental implants with modified surfaces have shown stronger osseointegration than implants which are only turned (machined). Advanced surface modification techniques such as anodic oxidation and Ca-P application have been developed to achieve faster and stronger bonding between the host bone and the implant. PURPOSE. The purpose of this study was to investigate the effect of surface treatment of titanium dental implant on implant stability after insertion using the rabbit tibia model. MATERIAL AND METHODS. Three test groups were prepared: sandblasted, large-grit and acid-etched (SLA) implants, anodic oxidized implants, and anodized implants with Ca-P immersion. The turned implants served as control. Twenty rabbits received 80 implants in the tibia. Resonance frequencies were measured at the time of implant insertion, 2 weeks and 4 weeks of healing. Removal torque values (RTV) were measured 2 and 4 weeks after insertion. RESULTS. The implant stability quotient (ISQ) values of implants for resonance frequency analysis (RFA) increased significantly (P < .05) during 2 weeks of healing period although there were no significant differences among the test and control groups (P > .05). The test and control implants also showed significantly higher ISQ values during 4 weeks of healing period (P < .05). No significant differences, however, were found among all the groups. All the groups showed no significant differences in ISQ values between 2 and 4 weeks after implant insertion (P >.05). The SLA, anodized and Ca-P immersed implants showed higher RTVs at 2 and 4 weeks of healing than the machined one (P < .05). However, there was no significant difference among the experimental groups. CONCLUSION. The surface-modified implants appear to provide superior implant stability to the turned one. Under the limitation of this study, however, we suggest that neither anodic oxidation nor Ca-P immersion techniques have any advantage over the conventional SLA technique with respect to implant stability.
참고문헌 (20)
- Weinlaender M, "Histomorphometry of bone apposition around three types of endosseous dental implants", Int J Oral Maxillofac Implants, 7, pp.491~496 (1992)
- Sul YT, "Characteristics of the surface oxides on turned and electrochemically oxidized pure titanium implants up to dielectric breakdown: the oxide thickness, micropore configurations, surface roughness, crystal structure and chemical composition", Biomaterials, 23, pp.491~501 (2002)
- Ellingsen JE, "Surface configurations of dental implants", Periodontology, 17, pp.36~46 (2000)
- Changkook You, "Characterization and in vivo evaluation of calcium phosphatecoated cp-titanium by dip-spin method", Current Applied Physics, 5(5), pp.501~506 (2005), 한국물리학회
- Meredith N, "Assessment of implant stability as a prognostic determinant", Int J Prosthodont, 11, pp.491~501 (1998)
- Meredith N, "Quantitative determination of the stability of the implant-tissue interface using resonance frequency analysis", Clin Oral Implants Res, 7, pp.261~267 (1996)
- Meredith N, "On the clinical measurement of implant stability, osseointegration", 박사, Department of Handicap Research, pp.1997
- Huang HM, "Early detection of implant healing process using resonance frequency analysis", Clin Oral Implants Res, 14, pp.467~443 (2003)
- Kim YH, "A histomorphometric analysis of the effects of various surface treatment methods on osseointegration", Int J Oral Maxillofac Implants, 18, pp.349~356 (2003)
- Changkook You, "Characterization and in vivo evaluation of calcium phosphatecoated cp-titanium by dip-spin method", Current Applied Physics, 5(5), pp.501~506 (2005), 한국물리학회
- Yeo IS, "Biomechanical and Histomorphometric Study of Dental Implants with different surface characteristics", J Biomed Mater Res Part B: Appl Biomater, 87B, pp.303~311 (2008)
- Meredith N, "The application of resonance frequency measurement to study the stability of titanium implants during healing in the rabbit tibia", Clin Oral Implants Res, 8, pp.234~243 (1997)
- Zhu X, "Surface characteristics and structure of anodic oxide films containing Ca and P on a titanium implant material", J Biomed Mater Res, 60, pp.333~338 (2002)
- Ivanoff CJ, "Influence of mono and bicortical anchorage on the titanium implants. A study in rabbit tibia", Int J Oral Maxillofac Surg, 25, pp.229~235 (1996)
- Sennerby L, "A histomorphometric and biomechanical comparison of titanium implants inserted in rabbit cortical and cancellous bone", Int J Oral Maxillofac Implants, 7, pp.62~71 (1992)
- Oh SH, "Cytotoxicity of calcium metaphosphate coated on cp-titanium", Key Eng Mater, pp.218~220 (2002)
- Choi JW, "Bone responses of anodized titanium implants under different current voltages", J Oral Rehabil, 33, pp.889~897 (2006)
- Larsson C, "Bone response to surface-modified titanium implants: Studies on the early tissue response to machined and electropolished implants with different oxide thicknesses", Biomaterials, 17, pp.605~616 (1996)
- M.M. Shalabi, "Implant Surface roughness and bone healing : a systematic review", J Dent Res, 85, pp.496~500 (2006)
- Wennerberg A, "Characterizing three-dimensional topography of engineering and biomaterial surfaces by confocal laser scanning and stylus techniques", Med Eng Phys, 18, pp.548~556 (1996)