Investigation of bonding properties of denture bases to silicone-based soft denture liner immersed in isobutyl methacrylate and 2-hydroxyethyl methacrylate
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. The purpose of this study was to investigate the bonding properties of denture bases to silicone-based soft denture liners immersed in isobutyl methacrylate (iBMA) and 2-hydroxyethyl methacrylate (HEMA) for various lengths of time. MATERIALS AND METHODS. Polymethyl methacrylate (PMMA) test specimens were fabricated (75 mm in length, 12 mm in diameter at the thickest section, and 7 mm at the thinnest section) and then randomly assigned to five groups (n=15); untreated (Group 1), resilient liner immersed in iBMA for 1 minute (Group 2), resilient liner immersed in iBMA for 3 minutes (Group 3), resilient liner immersed in HEMA for 1 minute (Group 4), and resilient liner immersed in HEMA for 3 minutes (Group 5). The resilient liner specimens were processed between 2 PMMA blocks. Bonding strength of the liners to PMMA was compared by tensile test with a universal testing machine at a crosshead speed of 5 mm/min. Data were evaluated by 1-way ANOVA and post hoc Tukey-Kramer multiple comparisons tests (α=0.05). RESULTS. The highest mean value of force was observed in Group 3 specimens. The differences between groups were statistically significant (P<.05), except between Group 1 and Group 4 (P=.063). CONCLUSION. Immersion of silicone-based soft denture liners in iBMA for 3 minutes doubled the tensile bond strength between the silicone soft liner and PMMA denture base materials compared to the control group.
Abstract
PURPOSE. The purpose of this study was to investigate the bonding properties of denture bases to silicone-based soft denture liners immersed in isobutyl methacrylate (iBMA) and 2-hydroxyethyl methacrylate (HEMA) for various lengths of time. MATERIALS AND METHODS. Polymethyl methacrylate (PMMA) test specimens were fabricated (75 mm in length, 12 mm in diameter at the thickest section, and 7 mm at the thinnest section) and then randomly assigned to five groups (n=15); untreated (Group 1), resilient liner immersed in iBMA for 1 minute (Group 2), resilient liner immersed in iBMA for 3 minutes (Group 3), resilient liner immersed in HEMA for 1 minute (Group 4), and resilient liner immersed in HEMA for 3 minutes (Group 5). The resilient liner specimens were processed between 2 PMMA blocks. Bonding strength of the liners to PMMA was compared by tensile test with a universal testing machine at a crosshead speed of 5 mm/min. Data were evaluated by 1-way ANOVA and post hoc Tukey-Kramer multiple comparisons tests (α=0.05). RESULTS. The highest mean value of force was observed in Group 3 specimens. The differences between groups were statistically significant (P<.05), except between Group 1 and Group 4 (P=.063). CONCLUSION. Immersion of silicone-based soft denture liners in iBMA for 3 minutes doubled the tensile bond strength between the silicone soft liner and PMMA denture base materials compared to the control group.
참고문헌 (28)
- McCabe JF., "Adhesive bond strength and compliance for denture soft lining materials", Biomaterials, 23, pp.1347~1352 (2002)
- Machado AL., "Effect of microwave disinfection on the hardness and adhesion of two resilient liners", J Prosthet Dent, 94, pp.183~189 (2005)
- León BL., "Water sorption, solubility, and tensile bond strength of resilient denture lining materials polymerized by different methods after thermal cycling", J Prosthet Dent, 93, pp.282~287 (2005)
- Usumez A., "Bond strength of a silicone lining material to alumina-abraded and lased denture resin", J Biomed Mater Res B Appl Biomater, 71, pp.196~200 (2004)
- Botega DM., "Effects of thermocycling on the tensile bond strength of three permanent soft denture liners", J Prosthodont, 17, pp.550~554 (2008)
- Braden M., "Water absorption and water solubility of soft lining materials for acrylic dentures", J Dent Res, 62, pp.764~768 (1983)
- Kulak-Ozkan Y., "Effect of thermocycling on tensile bond strength of six silicone-based, resilient denture liners", J Prosthet Dent, 89, pp.303~310 (2003)
- Murat H., "Dynamic viscoelastic properties and the age changes of long-term soft denture liners", Biomaterials, 21, pp.1421~1427 (2000)
- Akin H., "Effect of different surface treatments on tensile bond strength of silicone-based soft denture liner", Lasers Med Sci, 26, pp.783~788 (2011)
- Akin H., "Effect of sandblasting with different size of aluminum oxide particles on tensile bond strength of resilient liner to denture base", Cumhuriyet Dent J, 14, pp.5~11 (2011)
- Amin WM., "The nature of the interface between polymethyl methacrylate denture base materials and soft lining materials", J Dent, 9, pp.336~346 (1981)
- Bolayır G., "Effects of different high alkyl methacrylate monomers on tensile bond strength between resilient liner and acrylic resin", Mater Res Innov, 13, pp.431~435 (2009)
- Craig RG., "Properties of resilient denture liners", J Am Dent Assoc, 63, pp.382~390 (1961)
- Jacobsen NL., "Lased and sandblasted denture base surface preparations affecting resilient liner bonding", J Prosthet Dent, 78, pp.153~158 (1997)
- Storer R., "Resilient denture base materials. Part 1, introduction and laboratory evaluation", Br Dent J, 113, pp.195~203 (1962)
- Tugut F., "Strength of the bond between a silicone lining material and denture resin after Er : YAG laser treatments with different pulse durations and levels of energy", Lasers Med Sci, 27, pp.281~285 (2012)
- Mutluay MM., "Evaluation of bond strength of soft relining materials to denture base polymers", Dent Mater, 23, pp.1373~1381 (2007)
- Johnson JA., "The mechanical properties of PMMA and its copolymers with ethyl methacrylate and butyl methacrylate", J Mater Sci, 29, pp.870~876 (1994)
- Hatamleh MM., "Effect of net fiber reinforcement surface treatment on soft denture liner retention and longevity", J Prosthodont, 19, pp.258~262 (2010)
- Çökeliler D., "Modification of glass fibers to improve reinforcement : a plasma polymerization technique", Dent Mater, 23, pp.335~342 (2007)
- Keyf F., "The effects of HEMA-monomer and air atmosphere treatment of glass fibre on the transverse strength of a provisional fixed partial denture resin", J Oral Rehabil, 30, pp.1142~1148 (2003)
- Doğan OM., "Effects of some methacrylate monomers used as liquid component on tensile and flexural strengths of poly(methylmethacrylate)denture base resin", Mater Res Innov, 10, pp.424~427 (2006)
- Leles CR., "Bonding strength between a hard chairside reline resin and a denture base material as influenced by surface treatment", J Oral Rehabil, 28, pp.1153~1157 (2001)
- Vargün E., "Synthesis and Characterization of 2-Hydroxyethyl Methacrylate(HEMA)and Methyl Methacrylate(MMA)Copolymer Used as Biomaterial", J Macromol Sci A, 47, pp.235~240 (2010)
- al-Athel MS., "Effect of test method on the bond strength of a silicone resilient denture lining material", J Prosthet Dent, 76, pp.535~540 (1996)
- Aydin AK., "Bond strength and failure analysis of lining materials to denture resin", Dent Mater, 15, pp.211~218 (1999)
- Waters MG., "Mechanical properties of an experimental denture soft lining material", J Dent, 27, pp.197~202 (1999)
- Kutay O., "Comparison of tensile and peel bond strengths of resilient liners", J Prosthet Dent, 71, pp.525~531 (1994)