Evaluation of effect of galvanic corrosion between nickel-chromium metal and titanium on ion release and cell toxicity
1
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
PURPOSE. The purpose of this study was to evaluate cell toxicity due to ion release caused by galvanic corrosion as a result of contact between base metal and titanium. MATERIALS AND METHODS. It was hypothesized that Nickel (Ni)-Chromium (Cr) alloys with different compositions possess different corrosion resistances when contacted with titanium abutment, and therefore in this study, specimens (10×10×1.5 mm) were fabricated using commercial pure titanium and 3 different types of Ni-Cr alloys (T3, Tilite, Bella bond plus) commonly used for metal ceramic restorations. The specimens were divided into 6 groups according to the composition of Ni-Cr alloy and contact with titanium. The experimental groups were in direct contact with titanium and the control groups were not. After the samples were immersed in the culture medium - Dulbecco’s modified Eagle’s medium[DMEM] for 48 hours, the released metal ions were detected using inductively coupled plasma mass spectrometer (ICP-MS) and analyzed by the Kruskal-Wallis and Mann-Whitney test (P<.05). Mouse L-929 fibroblast cells were used for cell toxicity evaluation. The cell toxicity of specimens was measured by the 3-{4,5-dimethylthiazol-2yl}-2,5-diphenyltetrazolium bromide (MTT) test. Results of MTT assay were statistically analyzed by the two-way ANOVA test (P<.05). Post-hoc multiple comparisons were conducted using Tukey’s tests. RESULTS. The amount of metal ions released by galvanic corrosion due to contact between the base metal alloy and titanium was increased in all of the specimens. In the cytotoxicity test, the two-way ANOVA showed a significant effect of the alloy type and galvanic corrosion for cytotoxicity (P<.001). The relative cell growth rate (RGR) was decreased further on the groups in contact with titanium (P<.05). CONCLUSION. The release of metal ions was increased by galvanic corrosion due to contact between base metal and titanium, and it can cause adverse effects on the tissue around the implant by inducing cytotoxicity.
Abstract
PURPOSE. The purpose of this study was to evaluate cell toxicity due to ion release caused by galvanic corrosion as a result of contact between base metal and titanium. MATERIALS AND METHODS. It was hypothesized that Nickel (Ni)-Chromium (Cr) alloys with different compositions possess different corrosion resistances when contacted with titanium abutment, and therefore in this study, specimens (10×10×1.5 mm) were fabricated using commercial pure titanium and 3 different types of Ni-Cr alloys (T3, Tilite, Bella bond plus) commonly used for metal ceramic restorations. The specimens were divided into 6 groups according to the composition of Ni-Cr alloy and contact with titanium. The experimental groups were in direct contact with titanium and the control groups were not. After the samples were immersed in the culture medium - Dulbecco’s modified Eagle’s medium[DMEM] for 48 hours, the released metal ions were detected using inductively coupled plasma mass spectrometer (ICP-MS) and analyzed by the Kruskal-Wallis and Mann-Whitney test (P<.05). Mouse L-929 fibroblast cells were used for cell toxicity evaluation. The cell toxicity of specimens was measured by the 3-{4,5-dimethylthiazol-2yl}-2,5-diphenyltetrazolium bromide (MTT) test. Results of MTT assay were statistically analyzed by the two-way ANOVA test (P<.05). Post-hoc multiple comparisons were conducted using Tukey’s tests. RESULTS. The amount of metal ions released by galvanic corrosion due to contact between the base metal alloy and titanium was increased in all of the specimens. In the cytotoxicity test, the two-way ANOVA showed a significant effect of the alloy type and galvanic corrosion for cytotoxicity (P<.001). The relative cell growth rate (RGR) was decreased further on the groups in contact with titanium (P<.05). CONCLUSION. The release of metal ions was increased by galvanic corrosion due to contact between base metal and titanium, and it can cause adverse effects on the tissue around the implant by inducing cytotoxicity.
참고문헌 (27)
- Wataha JC, "Alloys for prosthodontic restorations", J Prosthet Dent, 87, pp.351~363 (2002)
- Wataha JC, "Casting alloys", Dent Clin North Am, 48, pp.499~512 (2004)
- Corso PP Jr, "Corrosion evaluation of gold-based dental alloys", J Dent Res, 64, pp.854~859 (1985)
- Tuna SH, "The influence of the pure metal components of four different casting alloys on the electrochemical properties of the alloys", Dent Mater, 25, pp.1096~1103 (2009)
- Lappalainen R, "Release of elements from some gold alloys and amalgams in corrosion", Scand J Dent Res, 95, pp.364~368 (1987)
- Wataha JC, "Biocompatibility of dental casting alloys: a review", J Prosthet Dent, 83, pp.223~234 (2000)
- Schmalz G, "Biological interactions of dental cast alloys with oral tissues", Dent Mater, 18, pp.396~406 (2002)
- Geurtsen W, "Biocompatibility of dental casting alloys", Crit Rev Oral Biol Med, 13, pp.71~84 (2002)
- Moffa JP, "Biocompatibility of nickel based dental alloys", CDA J, 12, pp.45~51 (1984)
- Roach M, "Base metal alloys used for dental restorations and implants", Dent Clin North Am, 51, pp.603~627 (2007)
- Bumgardner JD, "Corrosion and cell culture evaluations of nickel-chromium dental casting alloys", J Appl Biomater, 5, pp.203~213 (1994)
- Wataha JC, "Effect of cell line on in vitro metal ion cytotoxicity", Dent Mater, 10, pp.156~161 (1994)
- Al-Hiyasat AS, "An investigation of the cytotoxic effects of dental casting alloys", Int J Prosthodont, 16, pp.8~12 (2003)
- Wang X, "Comparison of MTT assay, flow cytometry, and RT-PCR in the evaluation of cytotoxicity of five prosthodontic materials", J Biomed Mater Res B Appl Biomater, 95, pp.357~364 (2010)
- Lucas LC, "Biodegradation of restorative metallic systems", Adv Dent Res, 6, pp.32~37 (1992)
- "American Dental Association status report on the occurrence of galvanic corrosion in the mouth and its potential effects. Council on Dental Materials, Instruments, and Equipment", J Am Dent Assoc, 115, pp.783~787 (1987)
- Geis-Gerstorfer J, "In vitro substance loss due to galvanic corrosion in Ti implant", Ni-Cr supraconstruction systems, 1989, pp.4, 119~123
- Schmalz G, "Influence of metals on IL-6 release in vitro", Biomaterials, 19, pp.1689~1694 (1998)
- Venugopalan R, "Evaluation of restorative and implant alloys galvanically coupled to titanium", Dent Mater, 14, pp.165~172 (1998)
- Wylie CM, "Corrosion of nickel-based dental casting alloys", Dent Mater, 23, pp.714~723 (2007)
- Bumgardner JD, "Surface analysis of nickel-chromium dental alloys", Dent Mater, 9, pp.252~259 (1993)
- Baran GR, "The metallurgy of Ni-Cr alloys for fixed prosthodontics", J Prosthet Dent, 50, pp.639~650 (1983)
- Pana J, "Electrochemical studies of the influence of beryllium on the corrosion resistance of Ni-25Cr-10Mo cast alloys for dental applications", J Electrochem Soc, 142, pp.1454~1458 (1995)
- Brune D, "Metal release from dental biomaterials", Biomaterials, 7, pp.163~175 (1986)
- Wataha JC, "Uptake of metal cations by fibroblasts in vitro", J Biomed Mater Res, 27, pp.227~232 (1993)
- Tai Y, "Leaching of nickel, chromium, and beryllium ions from base metal alloy in an artificial oral environment", J Prosthet Dent, 68, pp.692~697 (1992)
- Hanawa T, "Cytotoxicities of oxides, phosphates and sulphides of metals", Biomaterials, 13, pp.20~24 (1992)