PURPOSE. The purpose of this in vitro study was to evaluate the effect of abrasive toothbrushing on the surface properties of monolithic computer-assisted design and computer-assisted manufacturing (CAD/CAM) materials stored in food-simulating liquids (FSLs). MATERIALS AND METHODS. Fourty-eight disk-shaped test specimens of each material (Paradigm MZ100/PMZ, Lava Ultimate/LU, Vita Enamic/VE, and Vita Mark II/VMII) with a diameter of 10.0 mm and a thickness of 3.0 ± 0.05 mm were prepared. Specimens were divided into 4 subgroups (n=12) and stored in air, distilled water, 0.02 M citric acid, or 75% ethanol/water solution for 7 days at 36.5 ℃. Then, the specimens were brushed in a multi-station brushing machine under a vertical load of 2.0 N for 3 hours. Surface gloss (GU), roughness (Ra), and hardness (Vickers [VHN]) were measured after storage and brushing simulation. The data sets were statistically analyzed with 2 and 3-way ANOVAs followed by the Tukey's post-hoc comparisons (α=.05). RESULTS. Statistically significant difference was found among the materials concerning the results of surface properties. VMII showed the highest VHN, while PMZ produced the lowest. Storage in FSLs significantly affected the VHN of PMZ and LU. VMII showed the lowest Ra and highest GU irrespective of FSLs and of abrasive toothbrushing. VE, LU, and PMZ produced significant decrease in GU and increase in Ra after toothbrushing. CONCLUSION. Surface properties of monolithic CAD/CAM restorative materials were differently affected by the storage media and abrasive toothbrushing.
Abstract
PURPOSE. The purpose of this in vitro study was to evaluate the effect of abrasive toothbrushing on the surface properties of monolithic computer-assisted design and computer-assisted manufacturing (CAD/CAM) materials stored in food-simulating liquids (FSLs). MATERIALS AND METHODS. Fourty-eight disk-shaped test specimens of each material (Paradigm MZ100/PMZ, Lava Ultimate/LU, Vita Enamic/VE, and Vita Mark II/VMII) with a diameter of 10.0 mm and a thickness of 3.0 ± 0.05 mm were prepared. Specimens were divided into 4 subgroups (n=12) and stored in air, distilled water, 0.02 M citric acid, or 75% ethanol/water solution for 7 days at 36.5 ℃. Then, the specimens were brushed in a multi-station brushing machine under a vertical load of 2.0 N for 3 hours. Surface gloss (GU), roughness (Ra), and hardness (Vickers [VHN]) were measured after storage and brushing simulation. The data sets were statistically analyzed with 2 and 3-way ANOVAs followed by the Tukey's post-hoc comparisons (α=.05). RESULTS. Statistically significant difference was found among the materials concerning the results of surface properties. VMII showed the highest VHN, while PMZ produced the lowest. Storage in FSLs significantly affected the VHN of PMZ and LU. VMII showed the lowest Ra and highest GU irrespective of FSLs and of abrasive toothbrushing. VE, LU, and PMZ produced significant decrease in GU and increase in Ra after toothbrushing. CONCLUSION. Surface properties of monolithic CAD/CAM restorative materials were differently affected by the storage media and abrasive toothbrushing.
참고문헌 (31)
- Ruse ND, "Resin-composite blocks for dental CAD", CAM applications, 2014, pp.93, 1232~1234
- Fasbinder DJ, "Materials for chairside CAD", CAM restorations, 2010, pp.31, 702~
- Beuer F, "Digital dentistry: an overview of recent developments for CAD", CAM generated restorations, 2008, pp.204, 505~511
- Della Bona A, "Characterization of a polymer-infiltrated ceramic-network material", Dent Mater, 30, pp.564~569 (2014)[DOI]
- Awada A, "Mechanical properties of resin-ceramic CAD", CAM restorative materials, 2015, pp.114, 587~593
- Tsitrou EA, "Brittleness index of machinable dental materials and its relation to the marginal chipping factor", J Dent, 35, pp.897~902 (2007)[DOI]
- Lauvahutanon S, "Mechanical properties of composite resin blocks for CAD", CAM, 2014, pp.33, 705~710
- 박준호, "Microtensile bond strength and micromorphologic analysis of surface-treated resin nanoceramics", The Journal of Advanced of Prosthodontics, 8(4), pp.275~284 (2016), 대한치과보철학회[DOI]
- Anil N, "Effect of toothbrushing on the material loss, roughness, and color of intrinsically and extrinsically stained porcelain used in metal-ceramic restorations: an in vitro study", Int J Prosthodont, 15, pp.483~487 (2002)
- Tanoue N, "Wear and surface roughness of current prosthetic composites after toothbrush", dentifrice abrasion, 2000, pp.84, 93~97
- Yap AU, "Influence of dietary simulating solvents on the hardness of provisional restorative materials", Dent Mater, 20, pp.370~376 (2004)[DOI]
- Yap AU, "Effect of food-simulating liquids on surface characteristics of composite and polyacid-modified composite restoratives", Oper Dent, 25, pp.170~176 (2000)
- Heintze SD, "Surface deterioration of dental materials after simulated toothbrushing in relation to brushing time and load", Dent Mater, 26, pp.306~319 (2010)[DOI]
- Garza LA, "Effect of toothbrushing on shade and surface roughness of extrinsically stained pressable ceramics", J Prosthet Dent, 115, pp.489~494 (2016)[DOI]
- Heintze SD, "Surface roughness and gloss of dental materials as a function of force and polishing time in vitro", Dent Mater, 22, pp.146~165 (2006)[DOI]
- Franzo D, "The effect of toothpaste concentration on enamel and dentine wear in vitro", J Dent, 38, pp.974~979 (2010)[DOI]
- Rosentritt M, "Effect of tooth brush abrasion and thermo-mechanical loading on direct and indirect veneer restorations", Clin Oral Investig, 19, pp.53~60 (2015)[DOI]
- Jasse FF, "Influence of filler charge on gloss of composite materials before and after in vitro toothbrushing", J Dent, 41, pp.41~44 (2013)[DOI]
- "ISO 11609, Dentistry-Dentifrices-Requirements, test methods and marking", International Organization for Standardization, ~ (2010)
- Ardu S, "Influence of mechanical and chemical degradation on surface gloss of resin composite materials", Am J Dent, 22, pp.264~268 (2009)
- da Silva EM, "Longitudinal evaluation of simulated toothbrushing on the roughness and optical stability of microfilled, microhybrid and nanofilled resin-based composites", J Dent, 41, pp.1081~1090 (2013)[DOI]
- Mormann WH, "Wear characteristics of current aesthetic dental restorative CAD", CAM materials: two-body wear, gloss retention, roughness and Martens hardness, 2013, pp.20, 113~125
- Flury S, "Effect of artificial toothbrushing and water storage on the surface roughness and micromechanical properties of tooth-colored CAD-CAM materials", J Prosthet Dent, 117, pp.767~774 (2017)[DOI]
- Ferracane JL, "Solvent degradation and reduced fracture toughness in aged composites", J Dent Res, 71, pp.13~19 (1992)[DOI]
- Pilliar RM, "The effect of environmental aging on the fracture toughness of dental composites", J Dent Res, 66, pp.722~726 (1987)[DOI]
- Sideridou ID, "Volumetric dimensional changes of dental light-cured dimethacrylate resins after sorption of water or ethanol", Dent Mater, 24, pp.1131~1136 (2008)[DOI]
- Yap AU, "Chemical degradation of composite restoratives", J Oral Rehabil, 28, pp.1015~1021 (2001)[DOI]
- Mehmet Mustafa Özarslan, "Effects of different surface finishing procedures on the change in surface roughness and color of a polymer infiltrated ceramic network material", The Journal of Advanced of Prosthodontics, 8(1), pp.16~20 (2016), 대한치과보철학회[DOI]
- Volpenhein DW, "A new method for in vitro evaluation of the interproximal penetration of manual toothbrushes", J Clin Dent, 5, pp.27~33 (1994)
- Koizumi H, "Surface roughness and gloss of current CAD", CAM resin composites before and after toothbrush abrasion, 2015, pp.34, 881~887
- Kamonkhantikul K, "Toothbrushing alters the surface roughness and gloss of composite resin CAD", CAM blocks, 2016, pp.35, 225~232