A study on the fracture strength of collarless metal-ceramic fixed partial dentures
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. The objective of this study was to evaluate fracture strength of collarless metal-ceramic FPDs according to their metal coping designs. MATERIALS AND METHODS. Four different facial margin design groups were investigated. Group A was a coping with a thin facial metal collar, group B was a collarless coping with its facial metal to the shoulder, group C was a collarless coping with its facial metal 1 mm short of the shoulder, and group D was a collarless coping with its facial metal 2 mm short of the shoulder. Fifteen 3-unit collarless metal-ceramic FPDs were fabricated in each group. Finished FPDs were cemented to PBT (Polybutylene terephthalate) dies with resin cement. The fracture strength test was carried out using universal testing machine (Instron 4465, Instron Co., Norwood MA, USA) at a cross head speed of 0.5 mm/min. Aluminum foil folded to about 1 mm of thickness was inserted between the plunger tip and the incisal edge of the pontic. Vertical load was applied until catastrophic porcelain fracture occurred. RESULTS. The greater the bulk of unsupported facial shoulder porcelain was, the lower the fracture strength became. However, there were no significant differences between experimental groups (P > .05). CONCLUSION. All groups of collarless metal-ceramic FPDs had higher fracture strength than maximum incisive biting force. Modified collarless metal-ceramic FPD can be an alternative to all-ceramic FPDs in clinical situations.
Abstract
PURPOSE. The objective of this study was to evaluate fracture strength of collarless metal-ceramic FPDs according to their metal coping designs. MATERIALS AND METHODS. Four different facial margin design groups were investigated. Group A was a coping with a thin facial metal collar, group B was a collarless coping with its facial metal to the shoulder, group C was a collarless coping with its facial metal 1 mm short of the shoulder, and group D was a collarless coping with its facial metal 2 mm short of the shoulder. Fifteen 3-unit collarless metal-ceramic FPDs were fabricated in each group. Finished FPDs were cemented to PBT (Polybutylene terephthalate) dies with resin cement. The fracture strength test was carried out using universal testing machine (Instron 4465, Instron Co., Norwood MA, USA) at a cross head speed of 0.5 mm/min. Aluminum foil folded to about 1 mm of thickness was inserted between the plunger tip and the incisal edge of the pontic. Vertical load was applied until catastrophic porcelain fracture occurred. RESULTS. The greater the bulk of unsupported facial shoulder porcelain was, the lower the fracture strength became. However, there were no significant differences between experimental groups (P > .05). CONCLUSION. All groups of collarless metal-ceramic FPDs had higher fracture strength than maximum incisive biting force. Modified collarless metal-ceramic FPD can be an alternative to all-ceramic FPDs in clinical situations.
참고문헌 (37)
- Geller W, "Dark and shaded zones-one of the important aspects of the W.Geller creative color technic", Quintessenz Zahntech, 8, pp.467~473 (1982)
- Touati B, "Light transmission in bonded ceramic restorations", J Esthet Dent, 5, pp.11~18 (1993)
- Cornell DF, "Soft tissue-ceramic interface:true parameter for successful esthetics", J Esthet Dent, 7, pp.81~86 (1995)
- O’Boyle KH, "An investigation of new metal framework design for metal ceramic restorations", J Prosthet Dent, 78, pp.295~301 (1997)
- Choung CK, "Procedure for a simplified collarless metal-ceramic restoration using gold powder", J Prosthet Dent, 47, pp.449~453 (1982)
- Behrend DA, "Ceramometal restorations with supragingival margins", J Prosthet Dent, 47, pp.625~632 (1982)
- Lehner CR, "Variable reduced metal support for collarless metal ceramic crowns:a new model for strength evaluation", Int J Prosthodont, 8, pp.337~345 (1995)
- Ulusoy M, "Fracture resistance of five different metal framework designs for metal-ceramic restorations", Int J Prosthodont, 15, pp.571~574 (2002)
- Yun JW, "A study on fracture strength of collarless metal ceramic crown with different metal coping design", J Korean Acad Prosthodont, 37, pp.454~464 (1999)
- Shillingburg HT, "Fundamentals of Fixed Prosthodontics. 3rd ed", pp.142~148 (1997), Quintessence Publishing
- Waltimo A, "A novel bite force recorder and maximal isometric bite force values for healthy young adults", Scand J Dent Res, 101, pp.171~175 (1993)
- Kiliaridis S, "The relationship between maximal bite force,bite force endurance,and facial morphology during growth.A cross-sectional study", Acta Odontol Scand, 51, pp.323~331 (1993)
- Schneider DM, "Porcelain shoulder adaptation using direct refractory dies", J Prosthet Dent, 36, pp.583~587 (1976)
- Goodacre CJ, "The collarless metal-ceramic crown", J Prosthet Dent, 38, pp.615~622 (1977)
- Toogood GD, "Technique for establishing porcelain margins", J Prosthet Dent, 40, pp.464~466 (1978)
- Vryonis P, "A simplified approach to the complete porcelain margin", J Prosthet Dent, 42, pp.592~593 (1979)
- Prince J, "The all-porcelain labial margin for ceramometal restorations:a new concept", J Prosthet Dent, 50, pp.793~796 (1983)
- Edge MJ, "An alternate method for establishing porcelain margins", J Prosthet Dent, 57, pp.276~277 (1987)
- Pinnell DC, "Light-cured porcelain margins:a new technique", J Prosthet Dent, 58, pp.50~52 (1987)
- Belles DM, "Effect of metal design and technique on the marginal characteristics of the collarless metal ceramic restoration", J Prosthet Dent, 65, pp.611~619 (1991)
- Boyle JJ Jr, "Marginal accuracy of metal ceramic restorations with porcelain facial margins", J Prosthet Dent, 69, pp.19~27 (1993)
- Warpeha WS Jr, "Design and technique variables affecting fracture resistance of metal-ceramic restorations", J Prosthet Dent, 35, pp.291~298 (1976)
- Smith TB, "In vitro fracture behavior of ceramic and metal-ceramic restorations", J Prosthodont, 3, pp.138~144 (1994)
- Kheradmandan S, "Fracture strength of four different types of anterior 3-unit bridges after thermo-mechanical fatigue in the dual-axis chewing simulator", J Oral Rehabil, 28, pp.361~369 (2001)
- Kern M, "Fracture strength of all-porcelain,resin-bonded bridges after testing in an artificial oral environment", J Dent, 21, pp.117~121 (1993)
- Rosentritt M, "In vitro fracture force and marginal adaptation of ceramic crowns fixed on natural and artificial teeth", Int J Prosthodont, 13, pp.387~391 (2000)
- Scherrer SS, "The fracture resistance of all-ceramic crowns on supporting structures with different elastic moduli", Int J Prosthodont, 6, pp.462~467 (1993)
- Yoshinari M, "Fracture strength of all-ceramic crowns", Int J Prosthodont, 7, pp.329~338 (1994)
- Anusavice KJ, "Tensile stress in glass-ceramic crowns:effect of flaws and cement voids", Int J Prosthodont, 5, pp.351~358 (1992)
- Stangel I, "Shear strength of the composite bond to etched porcelain", J Dent Res, 66, pp.1460~1465 (1987)
- Tuntiprawon M, "The effect of cement thickness on the fracture strength of all-ceramic crowns", Aust Dent J, 40, pp.17~21 (1995)
- Miller A, "Comparison of the fracture strengths of ceramometal crowns versus several all-ceramic crowns", J Prosthet Dent, 68, pp.38~41 (1992)
- Nakamura T, "Fracture resistance of pressable glass-ceramic fixed partial dentures", J Oral Rehabil, 29, pp.951~955 (2002)
- Rinke S, "Marginal accuracy and fracture strength of conventional and copy-milled all-ceramic crowns", Int J Prosthodont, 8, pp.303~310 (1995)
- Dickinson AJ, "A comparative study of the strength of aluminous porcelain and all-ceramic crowns", J Prosthet Dent, 61, pp.297~304 (1989)
- Hwang JW, "Fracture strength of copy-milled and conventional In-Ceram crowns", J Oral Rehabil, 28, pp.678~683 (2001)
- Wilson PR, "Deformation of crowns during cementation", J Prosthet Dent, 64, pp.601~609 (1990)