Effects of post surface conditioning before silanization on bond strength between fiber post and resin cement
2
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
PURPOSE. Post surface conditioning is necessary to expose the glass fibers to enable bonding between fiber post and resin cement. The purpose of the present study was to evaluate the effect of different surface conditioning on tensile bond strength (TBS) of a glass fiber reinforced post to resin cement. MATERIALS AND METHODS. In this in vitro study, 40 extracted single canal central incisors were endodontically treated and post spaces were prepared. The teeth were divided into four groups according to the methods of post surface treatment (n=10): 1) Silanization after etching with 20% H2O2, 2) Silanization after airborne-particle abrasion, 3) Silanization, and 4) No conditioning (Control). Adhesive resin cement (Panavia F 2.0) was used for cementation of the fiber posts to the root canal dentin. Three slices of 3 mm thick were obtained from each root. A universal testing machine was used with a cross-head speed of 1 mm/minute for performing the push-out tests. Two-way ANOVA and Tukey post hoc tests were used for analyzing data (α=0.05). RESULTS. It is revealed that different surface treatments and root dentin regions had significant effects on TBS, but the interaction between surface treatments and root canal regions had no significant effect on TBS. There was significant difference among H2O2 + Silane Group and other three groups. CONCLUSION. There were significant differences among the mean TBS values of different surface treatments. Application of hydrogen peroxide before silanization increased the bond strength between resin cements and fiber posts. The mean TBS mean values was significantly greater in the coronal region of root canal than the middle and apical thirds.
Abstract
PURPOSE. Post surface conditioning is necessary to expose the glass fibers to enable bonding between fiber post and resin cement. The purpose of the present study was to evaluate the effect of different surface conditioning on tensile bond strength (TBS) of a glass fiber reinforced post to resin cement. MATERIALS AND METHODS. In this in vitro study, 40 extracted single canal central incisors were endodontically treated and post spaces were prepared. The teeth were divided into four groups according to the methods of post surface treatment (n=10): 1) Silanization after etching with 20% H2O2, 2) Silanization after airborne-particle abrasion, 3) Silanization, and 4) No conditioning (Control). Adhesive resin cement (Panavia F 2.0) was used for cementation of the fiber posts to the root canal dentin. Three slices of 3 mm thick were obtained from each root. A universal testing machine was used with a cross-head speed of 1 mm/minute for performing the push-out tests. Two-way ANOVA and Tukey post hoc tests were used for analyzing data (α=0.05). RESULTS. It is revealed that different surface treatments and root dentin regions had significant effects on TBS, but the interaction between surface treatments and root canal regions had no significant effect on TBS. There was significant difference among H2O2 + Silane Group and other three groups. CONCLUSION. There were significant differences among the mean TBS values of different surface treatments. Application of hydrogen peroxide before silanization increased the bond strength between resin cements and fiber posts. The mean TBS mean values was significantly greater in the coronal region of root canal than the middle and apical thirds.
참고문헌 (50)
- Ramin Mosharraf, "Comparative evaluation of effects of different surface treatment methods on bond strength between fiber post and composite core", The Journal of Advanced of Prosthodontics, 4(2), pp.103~108 (2012), 대한치과보철학회
- Ayad MF, "Influence of irrigant, dowel type, and root-reinforcing material on fracture resistance of thin-walled endodontically treated teeth", J Prosthodont, 20, pp.180~189 (2011)
- Albashaireh ZS, "Effects of endodontic post surface treatment, dentin conditioning, and artificial aging on the retention of glass fiber-reinforced composite resin posts", J Prosthet Dent, 103, pp.31~39 (2010)
- Bitter K, "Post-endodontic restorations with adhesively luted fiber-reinforced composite post systems: a review", Am J Dent, 20, pp.353~360 (2007)
- Bateman G, "Fibre-based post systems: a review", Br Dent J, 195, pp.43~48 (2003)
- Monticelli F, "Surface treatments for improving bond strength to prefabricated fiber posts : a literature review", Oper Dent, 33, pp.346~355 (2008)
- Malferrari S, "Clinical evaluation of teeth restored with quartz fiber-reinforced epoxy resin posts", Int J Prosthodont, 16, pp.39~44 (2003)
- Monticelli F, "Clinical behavior of translucent-fiber posts: a 2-year prospective study", Int J Prosthodont, 16, pp.593~596 (2003)
- Aksornmuang J, "Microtensile bond strength of a dual-cure resin core material to glass and quartz fibre posts", J Dent, 32, pp.443~450 (2004)
- D’Arcangelo C, "Effect of surface treatments on tensile bond strength and on morphology of quartz-fiber posts", J Endod, 33, pp.264~267 (2007)
- Huber L, "Push-out bond strengths of endodontic posts bonded with different resin-based luting cements", Am J Dent, 20, pp.16772~ (2007)
- Rathke A, "Effectiveness of bonding fiber posts to root canals and composite core buildups", Eur J Oral Sci, 117, pp.604~610 (2009)
- Akgungor G, "Influence of dentin bonding agents and polymerization modes on the bond strength between translucent fiber posts and three dentin regions within a post space", J Prosthet Dent, 95, pp.368~378 (2006)
- Akgungor G, "Influence of different surface treatments on the short-term bond strength and durability between a zirconia post and a composite resin core material", J Prosthet Dent, 99, pp.388~399 (2008)
- Ferrari M, "Post placement affects survival of endodontically treated premolars", J Dent Res, 86, pp.729~734 (2007)
- Zicari F, "Van Meerbeek B. Factors affecting the cement-post interface", Dent Mater, 28, pp.287~297 (2012)
- Perdigao J, "The effect of silane on the bond strengths of fiber posts", Dent Mater, 22, pp.752~758 (2006)
- Valandro LF, "Microtensile bond strength between a quartz fiber post and a resin cement: effect of post surface conditioning", J Adhes Dent, 8, pp.10511~ (2006)
- Mosharraf R, "Push-out bond strength of a fiber post system with two resin cements", Dent Res J, 8(1), pp.88~93 (2011)
- Mazzitelli C, "Surface roughness analysis of fiber post conditioning processes", J Dent Res, 87, pp.186~190 (2008)
- Monticelli F, "Cement system and surface treatment selection for fiber post luting", Med Oral Patol Oral Cir Bucal, 13, pp.214~221 (2008)
- Jongsma LA, "Influence of surface pretreatment of fiber posts on cement delamination", Dent Mater, 26, pp.901~907 (2010)
- Bell AM, "Bonding of fibre-reinforced composite post to root canal dentin", J Dent, 33, pp.533~539 (2005)
- Sahafi A, "Effect of surface treatment of prefabricated posts on bonding of resin cement", Oper Dent, 29, pp.60~68 (2004)
- Goracci C, "The adhesion between prefabricated FRC posts and composite resin cores: microtensile bond strength with and without post-silanization", Dent Mater, 21, pp.437~444 (2005)
- Mazzitelli C, "Effects of post surface treatments on the bond strength of self-adhesive cements", Am J Dent, 25, pp.159~164 (2012)
- Sahafi A, "Bond strength of resin cement to dentin and to surface-treated posts of titanium alloy, glass fiber, and zirconia", J Adhes Dent, 5, pp.153~162 (2003)
- Magni E, "Adhesion between fiber posts and resin luting agents: a microtensile bond strength test and an SEM investigation following different treatments of the post surface", J Adhes Dent, 9, pp.195~202 (2007)
- Manicardi CA, "Influence of filling materials on the bonding interface of thin-walled roots reinforced with resin and quartz fiber posts", J Endod, 37, pp.531~537 (2011)
- Sumitha M, "Evaluation of postsurface conditioning to improve interfacial adhesion in postcore restorations", J Conserv Dent, 14, pp.28~31 (2011)
- Kulunk S, "Effects of different surface pre-treatments on the bond strength of adhesive resin cement to quartz fiber post", Acta Odontol Scand, 70, pp.54754~ (2012)
- de Sousa Menezes M, "Fiber post etching with hydrogen peroxide: effect of concentration and application time", J Endod, 37, pp.398~402 (2011)
- Monticelli F, "Post-surface conditioning improves interfacial adhesion in post", core restorations, 2006, pp.22, 602~609
- Xible AA, "Effect of silica coating and silanization on flexural and composite-resin bond strengths of zirconia posts: An in vitro study", J Prosthet Dent, 95, pp.224~229 (2006)
- Zhang Y, "H2O2 treatment improves the bond strength between glass fiber posts and resin cement", Beijing Da Xue Xue Bao, 43, pp.85~88 (2011)
- Monticelli F, "A simple etching technique for improving the retention of fiber posts to resin composites", J Endod, 32, pp.44~47 (2006)
- Khamverdi Z, "Effect of storage time on microtensile bond strength between quartz fiber post and composite core after different post surface treatments", J Conserv Dent, 14, pp.361~365 (2011)
- Monticelli F, "Improving the quality of the quartz fiber postcore bond using sodium ethoxide etching and combined silane", adhesive coupling, 2006, pp.32, 447~451
- Monticelli F, "Effect of temperature on the silane coupling agents when bonding core resin to quartz fiber posts", Dent Mater, 22, pp.1024~1028 (2006)
- Vano M, "The adhesion between fibre posts and composite resin cores: the evaluation of microtensile bond strength following various surface chemical treatments to posts", Int Endod J, 39, pp.31~39 (2006)
- Monticelli F, "Effect of adhesive systems and surface treatment of methacrylate resin-based fiber posts on post-resin-dentin bonds", Am J Dent, 20, pp.231~234 (2007)
- Wrbas KT, "Influence of adhesive systems on bond strength between fiber posts and composite resin cores in a Effects pull-out test design", Dent Mater J, 26, pp.401~408 (2007)
- Yenisey M, "Effects of chemical surface treatments of quartz and glass fiber posts on the retention of a composite resin", J Prosthet Dent, 99, pp.38~45 (2008)
- Wrbas KT, "Effect of adhesive resin cements and post surface silanization on the bond strengths of adhesively inserted fiber posts", J Endod, 33, pp.840~843 (2007)
- Bitter K, "Bond strengths of resin cements to fiber-reinforced composite posts", Am J Dent, 19, pp.138~142 (2006)
- Park SJ, "Effect of Silane Coupling Agent on Interphase and Performance of Glass Fibers", Unsaturated Polyester Composites, 2001, pp.242, 174~179
- Bitter K, "Effect of silanization on bond strengths of fiber posts to various resin cements", Quintessence Int, 38, pp.121~128 (2007)
- Radovic I, "Accelerated aging of adhesive-mediated fiber post-resin composite bonds: A modeling approach", J Dent, 35, pp.683~689 (2007)
- Soares CJ, "Influence of airborne-particle abrasion on mechanical properties and bond strength of carbon", epoxy and glass, J Prosthet Dent, pp.2008, 99[DOI]
- Topcu FT, "Push-out bond strengths of two fiber post types bonded with different dentin bonding agents", J Biomed Mater Res B Appl Biomater, 93, pp.359~366 (2010)