Purpose. This in vitro study aimed to evaluate the surface characteristics of a full veneer crown fabricated chairside (CS) from a (Y, Nb)-TZP zirconia block in response to conventional zirconia grinding and polishing. Materials and Methods. Zirconia crowns (n = 40) were first prepared and divided into two groups of materials: Labside (LS) and CS, after which each specimen went through a five-step grinding and polishing procedure. Following each surface treatment, surface characteristics were analyzed using confocal laser microscopy (CLSM), average surface roughness (Ra) values were processed from the profile data through Gaussian filtering, and X-ray diffraction pattern analysis was performed to evaluate the monoclinic (M) phase content. Then, a representative specimen was selected for field-emission scanning electron microscopy (FE-SEM), followed by a final analysis of the roughness and X-ray diffraction of the specimens using the independent t-test and repeated measures analysis of variance (RM-ANOVA). Results. In every group, polishing significantly reduced the Ra values (P < .001). There was no significant difference in Ra between the polished state CS and LS. Furthermore, CLSM and FE-SEM investigations revealed that even though grain exposure was visible in CS specimens throughout the as-delivered and ground states, the exposure was reduced after polishing. Moreover, while no phase transformation was visible in the LS, phase transformation was visible in CS after every surface treatment, with the M phase content of the CS group showing a significant reduction after polishing (P < .001). Conclusion. Within the limits of this study, clinically acceptable level of surface finishing of (Y, Nb)-TZP can be achieved after conventional zirconia polishing sequence.
Abstract
Purpose. This in vitro study aimed to evaluate the surface characteristics of a full veneer crown fabricated chairside (CS) from a (Y, Nb)-TZP zirconia block in response to conventional zirconia grinding and polishing. Materials and Methods. Zirconia crowns (n = 40) were first prepared and divided into two groups of materials: Labside (LS) and CS, after which each specimen went through a five-step grinding and polishing procedure. Following each surface treatment, surface characteristics were analyzed using confocal laser microscopy (CLSM), average surface roughness (Ra) values were processed from the profile data through Gaussian filtering, and X-ray diffraction pattern analysis was performed to evaluate the monoclinic (M) phase content. Then, a representative specimen was selected for field-emission scanning electron microscopy (FE-SEM), followed by a final analysis of the roughness and X-ray diffraction of the specimens using the independent t-test and repeated measures analysis of variance (RM-ANOVA). Results. In every group, polishing significantly reduced the Ra values (P < .001). There was no significant difference in Ra between the polished state CS and LS. Furthermore, CLSM and FE-SEM investigations revealed that even though grain exposure was visible in CS specimens throughout the as-delivered and ground states, the exposure was reduced after polishing. Moreover, while no phase transformation was visible in the LS, phase transformation was visible in CS after every surface treatment, with the M phase content of the CS group showing a significant reduction after polishing (P < .001). Conclusion. Within the limits of this study, clinically acceptable level of surface finishing of (Y, Nb)-TZP can be achieved after conventional zirconia polishing sequence.
참고문헌 (47)
- Sannino G, "Cerec CAD-CAM chairside system", Oral Implantol(Rome), 7, pp.57~70 (2015)
- Collares K, "A practice-based research network on the survival of ceramic inlay", onlay restorations, 2016, pp.32, 687~694
- Pieger S, "Clinical outcomes of lithium disilicate single crowns and partial fixed dental prostheses : a systematic review", J Prosthet Dent, 112, pp.22~30 (2014)
- Zarone F, "Current status on lithium disilicate and zirconia : a narrative review", BMC Oral Health, 19, pp.134~ (2019)
- Lim CH, "Evaluation of fracture strength for single crowns made of the different types of lithium disilicate glass-ceramics", Odontology, 108, pp.231~239 (2020)
- Kern M, "Ten-year outcome of three-unit fixed dental prostheses made from monolithic lithium disilicate ceramic", J Am Dent Assoc, 143, pp.234~240 (2012)
- Alao AR, "roughness and phase transformation in CAD-CAM milling and subsequent surface treatments of lithium metasilicate", disilicate glass-ceramics, 2017, pp.74, 251~260
- Valenti M, "Retrospective survival analysis of 261 lithium disilicate crowns in a private general practice", Quintessence Int, 40, pp.573~579 (2009)
- Kaizer MR, "Speed sintering translucent zirconia for chairside one-visit dental restorations: Optical, mechanical, and wear characteristics", Ceram Int, 43, pp.10999~11005 (2017)
- Denry I, "State of the art of zirconia for dental applications", Dent Mater, 24, pp.299~307 (2008)
- Ahmed WM, "The influence of altering sintering protocols on the optical and mechanical properties of zirconia : A review", J Esthet Restor Dent, 31, pp.423~430 (2019)
- Khaledi AAR, "The effect of sintering time on the marginal fit of zirconia copings", J Prosthodont, 28, pp.e285~e289 (2019)
- Cokic SM, "Mechanical properties, aging stability and translucency of speed-sintered zirconia for chairside restorations", Dent Mater, 36, pp.959~972 (2020)
- Luthardt RG, "CAD-CAM-machining effects on Y-TZP zirconia", Dent Mater, 20, pp.655~662 (2004)
- Jeong KW, "Clinical feasibility of fully sintered (Y, Nb)-TZP for CADCAM single-unit restoration: a pilot study", Materials(Basel), 14, pp.2762~ (2021)
- Cho JH, "Trueness of the inner surface of monolithic crowns fabricated by milling of a fully sintered(Y, Nb)-TZP block in chairside CADCAM system for single-visit dentistry", Materials(Basel), 12, pp.3253~ (2019)
- Aljomard YRM, "Enamel wear against monolithic zirconia restorations : A meta-analysis and systematic review of in vitro studies", J Esthet Restor Dent, 34, pp.473~489 (2022)
- Burgess JO, "Enamel wear opposing polished and aged zirconia", Oper Dent, 39, pp.189~194 (2014)
- Janyavula S, "The wear of polished and glazed zirconia against enamel", J Prosthet Dent, 109, pp.22~29 (2013)
- Mathew MG, "Evaluation of adhesion of Streptococcus mutans, plaque accumulation on zirconia and stainless steel crowns, and surrounding gingival inflammation in primary molars: randomized controlled trial", Clin Oral Investig, 24, pp.3275~3280 (2020)
- Khayat W, "Effect of grinding and polishing on roughness and strength of zirconia", J Prosthet Dent, 119, pp.626~631 (2018)
- Park C, "Effect of various polishing systems on the surface roughness and phase transformation of zirconia and the durability of the polishing systems", J Prosthet Dent, 117, pp.430~437 (2017)
- Ipek Caglar, "The effect of various polishing systems on surface roughness and phase transformation of monolithic zirconia", The Journal of Advanced of Prosthodontics, 10(2), pp.132~137 (2018), 대한치과보철학회[DOI]
- Huh YH, "Evaluation of various polishing systems and the phase transformation of monolithic zirconia", J Prosthet Dent, 116, pp.440~449 (2016)
- Preis V, "The effectiveness of polishing kits : influence on surface roughness of zirconia", Int J Prosthodont, 28, pp.149~151 (2015)
- De Souza RH, "Flexural strength and crystalline stability of a monolithic translucent zirconia subjected to grinding, polishing and thermal challenges", Ceram Int, 46, pp.26168~26175 (2020)
- Sieper K, "Fracture strength of lithium disilicate crowns compared to polymer-infiltrated ceramic-network and zirconia reinforced lithium silicate crowns", J Mech Behav Biomed Mater, 74, pp.342~348 (2017)
- Carrabba M, "Effect of finishing and polishing on the surface roughness and gloss of feldspathic ceramic for chairside CAD-CAM systems", Oper Dent, 42, pp.175~184 (2017)
- Kosmač T, "The effects of dental grinding and sandblasting on ageing and fatigue behavior of dental zirconia(Y-TZP)ceramics", J Eur Ceram Soc, 28, pp.1085~1090 (2008)
- Toraya H, "Calibration curve for quantitative analysis of the monoclinic-tetragonal ZrO2 system by X-ray diffraction", J Am Ceram Soc, 67, pp.C-119-C-121~ (1984)
- Lee DY, "Phase stability of (Y, Nb)-TZP", Al2O3 composites under low temperature hydrothermal conditions, 1999, pp.39, 221~226
- Kim DJ, "Fracture toughness, ionic conductivity, and low-temperature phase stability of tetragonal zirconia codoped with yttria and niobium oxide", J Am Ceram Soc, 81, pp.2309~2314 (1998)
- Kowalski K, "Diffusion of niobium in yttria-stabilized zirconia and in titania-doped yttria-stabilized zirconia polycrystalline materials", J Eur Ceram Soc, 26, pp.3139~3143 (2006)
- Kim DJ, "Phase transformations of Y2O3 and Nb2O5 doped tetragonal zirconia during low temperature aging in air", Solid State Ion, 80, pp.67~73 (1995)
- Yin L, "A review of engineered zirconia surfaces in biomedical applications", Procedia CIRP, 65, pp.284~290 (2017)
- 신현섭, "Comparison of surface topography and roughness in different yttrium oxide compositions of dental zirconia after grinding and polishing", The Journal of Advanced of Prosthodontics, 13(4), pp.258~267 (2021), 대한치과보철학회[DOI]
- Al-Haj Husain N, "Effect of polishing instruments and polishing regimens on surface topography and phase transformation of monolithic zirconia : An evaluation with XPS and XRD analysis", J Mech Behav Biomed Mater, 64, pp.104~112 (2016)
- Zucuni CP, "Fatigue strength of yttria-stabilized zirconia polycrystals: Effects of grinding, polishing, glazing, and heat treatment", J Mech Behav Biomed Mater, 75, pp.512~520 (2017)
- Ramos GF, "Effect of grinding and heat treatment on the mechanical behavior of zirconia ceramic", Braz Oral Res, 30, pp.e12~ (2016)
- Pereira GK, "Effect of grinding with diamond-disc and-bur on the mechanical behavior of a Y-TZP ceramic", J Mech Behav Biomed Mater, 37, pp.133~140 (2014)
- Pereira GKR, "The effect of grinding on the mechanical behavior of Y-TZP ceramics : A systematic review and meta-analyses", J Mech Behav Biomed Mater, 63, pp.417~442 (2016)
- Go H, "Effect of various polishing burs on surface roughness and bacterial adhesion in pediatric zirconia crowns", Dent Mater J, 38, pp.311~316 (2019)
- Walia T, "Comparative evaluation of surface roughness of posterior primary zirconia crowns", Eur Arch Paediatr Dent, 20, pp.33~40 (2019)
- Kozmacs C, "Polishing of monolithic zirconia crowns-results of different dental practitioner groups", Dent J(Basel), 5, pp.30~ (2017)
- Mohammadi-Bassir M, "Effect of coarse grinding, overglazing, and 2 polishing systems on the flexural strength, surface roughness, and phase transformation of yttrium-stabilized tetragonal zirconia", J Prosthet Dent, 118, pp.658~665 (2017)
- Martins FV, "Evaluation of zirconia surface roughness after aluminum oxide airborne-particle abrasion and the erbium-YAG, neodymium-doped YAG, or CO2 lasers: A systematic review and meta-analysis", J Prosthet Dent, 121, pp.895~903 (2019)
- Zahoui A, "Cementation protocol for bonding zirconia crowns to titanium base CAD-CAM abutments", Int J Prosthodont, 33, pp.527~535 (2020)