Characterization of Core/Shell PMMA/CdS Nanoparticles Synthesized by Surfactant-free Emulsion Polymerization
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Herein, CdS-coated PMMA nanoparticles were prepared by in-situ surfactant-free emulsion copolymerization and subsequent CdS coating process. As-prepared CdS/PMMA hybrid particles had 201.7 nm in diameter. The amount of CdS nanocrystals in the hybrid particles was 10.37 wt% determined by TGA and elemental analysis. The size of CdS crystals was 3.55 nm preferentially grown in (111) plane. UV-vis spectrum of PMMA/CdS nanoparticles showed the significant blue-shift in optical illumination. The reason was found because the synthesized CdS nanocrystals on PMMA particles had a different band gap energy of 2.70 eV which was significantly higher than that of known-value of bulk CdS (2.41 eV) due to a quantum confinement effect.
Abstract
Herein, CdS-coated PMMA nanoparticles were prepared by in-situ surfactant-free emulsion copolymerization and subsequent CdS coating process. As-prepared CdS/PMMA hybrid particles had 201.7 nm in diameter. The amount of CdS nanocrystals in the hybrid particles was 10.37 wt% determined by TGA and elemental analysis. The size of CdS crystals was 3.55 nm preferentially grown in (111) plane. UV-vis spectrum of PMMA/CdS nanoparticles showed the significant blue-shift in optical illumination. The reason was found because the synthesized CdS nanocrystals on PMMA particles had a different band gap energy of 2.70 eV which was significantly higher than that of known-value of bulk CdS (2.41 eV) due to a quantum confinement effect.
참고문헌 (12)
- X. Cheng, , J. Colloid Interface Sci., 326, pp.121~ (2008)
- A. V. Firth, , Appl. Phys. Lett, 75, pp.3120~ (1999)
- P. K. Khanna, , Synth. React. Inorg., Met.-Org., Nano-Met. Chem, 38, pp.409~ (2008)
- Y. Jin, , J. Colloid Interface Sci, 301, pp.130~ (2006)
- J. Jasieniak, , J. Phys. Chem. C, 113, pp.19468~ (2009)
- T. Trindade, , Adv. Mater, 8, pp.161~ (1996)
- H. Yoon, , Colloid Polym. Sci, 288, pp.613~ (2010)
- Y. Zhang, , J. Appl. Polym. Sci, 92, pp.839~ (2004)
- P. Gupta, , Open Nanosci. J, 3, pp.15~ (2009)
- M. Maleki, , Semicond. Phys. Quantum Electron. Optoelectron, 10, pp.30~ (2007)
- C. Xu, , Mater. Lett, 57, pp.3070~ (2003)
- D. Wu, , Langmuir, 20, pp.5192~ (2004)