탄소섬유 Z-핀의 제작공정에 따른 인발특성
Pull-out Characteristics of Carbon Fiber Z-pin Depending on the Manufacturing Process
5
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, carbon fiber Z-pins were fabricated by applying the different manufacturing process, and pull out test was performed for the dumbbell type of test specimens. Carbon fiber Z pins with smooth surface(type I) and stepped surface(type II, type III) were fabricated by using autoclave. Carbon fiber Z-pins with stepped surface were manufacturing method, that is, mold forming and machining process. The experimantal results show that carbon fiber Z pins have superior pull-out characteristics to carbon steel Z-pins. Pull-out load and pull-out toughness of carbon fiber Z pins with stepped surface are larger than those of carbon fiber Z-pins with smooth surface. Pull-out load and pull out toughness of mold f ormed Z-pin are 31% and 218% larger than those of smooth surfaced Z-pins, respectively.
Abstract
In this study, carbon fiber Z-pins were fabricated by applying the different manufacturing process, and pull out test was performed for the dumbbell type of test specimens. Carbon fiber Z pins with smooth surface(type I) and stepped surface(type II, type III) were fabricated by using autoclave. Carbon fiber Z-pins with stepped surface were manufacturing method, that is, mold forming and machining process. The experimantal results show that carbon fiber Z pins have superior pull-out characteristics to carbon steel Z-pins. Pull-out load and pull-out toughness of carbon fiber Z pins with stepped surface are larger than those of carbon fiber Z-pins with smooth surface. Pull-out load and pull out toughness of mold f ormed Z-pin are 31% and 218% larger than those of smooth surfaced Z-pins, respectively.
참고문헌 (23)
- 신형곤, "CFRP 구멍가공 시 공구의 절삭성능에 관한 연구", 한국기계기술학회지, 20(6), pp.941~946 (2018), 한국기계기술학회[DOI]
- 황규완, "적층각도를 가진 모드 Ⅱ CFRP 시험편의 접착 피로특성에 의한 구조안정성 평가", 한국기계기술학회지, 18(4), pp.523~528 (2016), 한국기계기술학회[DOI]
- A.P. Mouritz, "Review of z-pinned composite laminates", Composites Part A: Applied Science and Manufacturing, 38(12), pp.2383~2397 (2007)
- 정종설, "Z-핀으로 보강된 탄소섬유 강화 복합재의 파단 특성 연구", 박사, 나노·IT융합프로그램, pp.2014
- Jangkyo Kim, "Fracture toughness of CFRP with modified epoxy resin matrices", Composites Science and Technology, 43(3), pp.283~297 (1992)
- Seung-Hwan Lee, "Effect of Interleaved Non-Woven Carbon Tissue on Interlaminar Fracture Toughness of Laminated Composites: Part I – Mode II", Journal of Composite Materials, 36(18), pp.2153~2168 (2002)
- Seung-Hwan Lee, "Effect of Interleaved Non-Woven Carbon Tissue on Interlaminar Fracture Toughness of Laminated Composites: Part II – Mode I", Journal of Composite Materials, 36(18), pp.2169~2181 (2002)
- 정종설, "Interlaminar fracture toughness of CFRP laminates with silk fibers interleave", Journal of Mechanical Science and Technology, 27(12), pp.3651~3656 (2013), 대한기계학회[DOI]
- Sunny S. Wicks, "Interlaminar and intralaminar reinforcement of composite laminates with aligned carbon nanotubes", Composites Science and Technology, 70(1), pp.20~28 (2010)
- Kimberley Dransfield, "Improving the delamination resistance of CFRP by stitching—a review", Composites Science and Technology, 50(3), pp.305~317 (1994)
- Shen Chou, "Effect of weave structure on mechanical fracture behavior of three-dimensional carbon fiber fabric reinforced epoxy resin composites", Composites Science and Technology, 45(1), pp.23~35 (1992)
- Y. Shinyama, "Nondestructive evaluation of braided carbon fiber composites with artificial defect using HTS-SQUID gradiometer", Physica C: Superconductivity and its Applications, 471(21–22), pp.1242~1245 (2011)
- Hong-Yuan Liu, "Experimental study on effect of loading rate on mode I delamination of z-pin reinforced laminates", Composites Science and Technology, 67(7–8), pp.1294~1301 (2007)
- Shao-Cong Dai, "Experimental study on z-pin bridging law by pullout test", Composites Science and Technology, 64(16), pp.2451~2457 (2004)
- Nam Ju Lee, "SIMULATION OF PULL-OUT TEST BY FINITE ELEMENT METHOD WITH THE TRACTION-SEPARATION LAW", 21th International Conference on composite materials, pp.1106~1124 (2017)
- G. Allegri, "A novel model of delamination bridging via Z-pins in composite laminates", International Journal of Solids and Structures, 51(19–20), pp.3314~3332 (2014)
- Beene M’membe, "DELAMINATION RESISTANCE OF COMPOSITES USING INCLINED Z-PINS", 20th International Conference on composite materials, pp.2116~2112 (2015)
- Ivana K. Partridge, "Delamination resistant laminates by Z-Fiber® pinning: Part I manufacture and fracture performance", Composites Part A: Applied Science and Manufacturing, 36(1), pp.55~64 (2005)
- K. Pingkarawat, "Comparative study of metal and composite z-pins for delamination fracture and fatigue strengthening of composites", Engineering Fracture Mechanics, 154, pp.180~190 (2016)
- Myung-Gyun Ko, "Fatigue characteristics of jagged pin-reinforced composite single-lap joints in hygrothermal environments", Composite Structures, 119, pp.59~66 (2015)
- M Tavakkolizadeh, "Galvanic corrosion of carbon and steel in aggressive environments", Journal of Composites for Construction, 5(3), pp.200~210 (2001)
- Chung-Ki Sim, "Pull- out Characteristics of Grooved Carbon Fiber Z-pins", The 10th Asian-Australasian Conference on composite materials, pp.2~17 (2016)
- "Z-Pinning Apparatus using Preheating Apparatus, KR Patent 10-1518139, 201", ~