Wear behavior of Al2O3/AC8A composites by low pressure infiltration process
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Metal matrix composites(MMC) can obtain mechanical characteristics of application purposes that a single material is difficult to obtain. Al2 O3/AC8A composites were fabricated by low pressure infiltration process. The purpose is establishing the optimal casting conditions for composite preparation under low pressure. It is known the inorganic binder help infiltration. Therefore Al2O3 fiber preform's optimum sinter temperature is 1160℃, added inorganic binder is mixed binder(SiO2 sol:Al2O3 sol=5:2). And three fibers have been compared (Al2O3 80%/SiO2 20%, Al2O3 80%/SiO2 10%and Al2O3 97%/SiO2 3%). Al2O3/AC8A composites was made by each melting temperatures(650℃, 700℃, 750℃) and wear test was performed about effect of temperatures, kind of fiber, matrix andcomposites, aging time. Wear test is Ball on disk wear test. The resistance increased with the low melting temperature and Al2O3 80%/SiO2 20% fiber.
Abstract
Metal matrix composites(MMC) can obtain mechanical characteristics of application purposes that a single material is difficult to obtain. Al2 O3/AC8A composites were fabricated by low pressure infiltration process. The purpose is establishing the optimal casting conditions for composite preparation under low pressure. It is known the inorganic binder help infiltration. Therefore Al2O3 fiber preform's optimum sinter temperature is 1160℃, added inorganic binder is mixed binder(SiO2 sol:Al2O3 sol=5:2). And three fibers have been compared (Al2O3 80%/SiO2 20%, Al2O3 80%/SiO2 10%and Al2O3 97%/SiO2 3%). Al2O3/AC8A composites was made by each melting temperatures(650℃, 700℃, 750℃) and wear test was performed about effect of temperatures, kind of fiber, matrix andcomposites, aging time. Wear test is Ball on disk wear test. The resistance increased with the low melting temperature and Al2O3 80%/SiO2 20% fiber.
참고문헌 (7)
- C. S. Liauo, "Deformation mechanisms for AC8A", Al2O3(sf)composites over wide ranges of temperature and strain rate, 1999, pp.271, 79~90
- H. K. Lee, "Wear propertiesof high temperature Al alloys", Journal of the Korean Inst. of Met. & Mater, 33, pp.242~251 (1995)
- Kelimu Tulugan, "Electrochemical Performance of Al-Si", C Nano-Composites Fabricated by Arc-Discharge Method, 2015, pp.17(3), 579~584[DOI]
- Anil Borah, "Microstructural Evolution and Hardening Behaviour of Cast and Heat-treated Ru-Al and Ru-Al-Ni alloys", Metals and Materials International, 14(1), pp.123~132 (2008), 대한금속·재료학회
- T. W. Clyne, "The squeeze infiltration process for fabrication of metalmatrix composites", MetalI. Trans, 18A, pp.1519~1530 (1987)
- 송태훈, "저압함침법에 의한 FeCrSi", AC8A 복합재료의 제조와 마모특성 평가, 2008, pp.22(5), 106~111[DOI]
- 이정익, "X-ray Scanning System 개발에 있어서 Line Detector 원리의 적용", 한국기계기술학회지, 16(3), pp.1559~1563 (2014), 한국기계기술학회