Wear behavior of Ni and Ni-Cr enhanced AC8A composites by low pressure infiltration process
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Ni and Ni-Cr reinforced Al alloy (AC8A) composites were fabricated by low pressure infiltration process. Porous Ni was applied as preform. Ni reinforced AC8A composites were fabricated under 0.3 MPa at 650, 700 and 750 degrees centigrade, respectively, while Ni-Cr reinforced AC8A composites were fabricated under low pressure limited to the maximum of 0.5 Mpa at 750, 800 and 850 degrees centigrade, respectively. Microstructure and phase composition of the composites were evaluated by optical microscope, X-Ray diffraction (XRD), electro-probe micro analyzer (EMPA). Intermetallic compounds Al3Ni and CrSi were observed in the composites. The results indicate that the grain size has been increasing with the increase of the infiltration temperatures. However, the wear resistance of Ni/AC8A and Ni-Cr AC8A peaked at 650 degree centigrade and 800 degrees centigrade, respectively. In addition, based on the wear characteristics and wear surfaces, Ni-Cr/AC8A composites have a better wear resistance than Ni/AC8A composites and AC8A.
Abstract
Ni and Ni-Cr reinforced Al alloy (AC8A) composites were fabricated by low pressure infiltration process. Porous Ni was applied as preform. Ni reinforced AC8A composites were fabricated under 0.3 MPa at 650, 700 and 750 degrees centigrade, respectively, while Ni-Cr reinforced AC8A composites were fabricated under low pressure limited to the maximum of 0.5 Mpa at 750, 800 and 850 degrees centigrade, respectively. Microstructure and phase composition of the composites were evaluated by optical microscope, X-Ray diffraction (XRD), electro-probe micro analyzer (EMPA). Intermetallic compounds Al3Ni and CrSi were observed in the composites. The results indicate that the grain size has been increasing with the increase of the infiltration temperatures. However, the wear resistance of Ni/AC8A and Ni-Cr AC8A peaked at 650 degree centigrade and 800 degrees centigrade, respectively. In addition, based on the wear characteristics and wear surfaces, Ni-Cr/AC8A composites have a better wear resistance than Ni/AC8A composites and AC8A.
참고문헌 (10)
- C.S. Liauo, "Deformation mechanisms for AC8A", Al2O3(sf) composites over wide ranges of temperature and strain rate, 1999, pp.271, 79~90
- H.K. Lee, "Wear propertiesof high temperature Al alloys", Journal of the Korean Inst. of Met. & Mater, 33, pp.242~251 (1995)
- J.C. Lee, "Interfacial reactions in squeeze cast (saffil+C)", SAE329 Al composite, 1997, pp.28, 1250~1259
- Anil Borah, "Microstructural Evolution and Hardening Behaviour of Cast and Heat-treated Ru-Al and Ru-Al-Ni alloys", Metals and Materials International, 14(1), pp.123~132 (2008), 대한금속·재료학회
- T.W. Clyne, "The squeeze infiltration process for fabrication of metal-matrix composites", MetalI. Trans, 18A, pp.1519~1530 (1987)
- 송태훈, "저압함침법에 의한 FeCrSi", AC8A 복합재료의 제조와 마모특성 평가, 2008, pp.22(5), 106~111[DOI]
- H.B. Wang, "Hydrolysis behaviour of magnides and aluminides and its application to the synthesis of nanoparticles", Intermetallics, 16(3), pp.479~484 (2008)
- 조재혁, "Cathode 입구 상대습도에 따른 고분자 전해질 연료전지 성능분석", 한국기계기술학회지, 16(3), pp.1509~1514 (2014), 한국기계기술학회
- J.B. Fogagnolo, "Processing of Al matrix composites reinforced with Al-Ni compounds and Al2O3 by reactive milling and reactive sintering", Journal of Alloys and Compounds, 471(1-2), pp.448~452 (2009)
- Kelimu Tulugan, "Electrochemical Performance of Al-Si", C Nano-Composites Fabricated by Arc-Discharge Method, 2015, pp.17(3), 579~584[DOI]